Influence of SiC content on the oxidation of carbon fibre reinforced ZrB2/SiC composites at 1500 and 1650 °C in air

The microstructure and the oxidation resistance in air of continuous carbon fibre reinforced ZrB₂–SiC ceramic composites were investigated. SiC content was varied between 5–20?vol.%, while maintaining fibre content at ～40?vol.%. Short term oxidation tests in air were carried out at 1500 and 1650?°C in a bottom-up loading furnace. The thickness, composition and microstructure of the resulting oxide scale were analysed by SEM-EDS and X-Ray diffraction. The results show that contents above 15?vol.% SiC ensure the formation of a homogeneous protective borosilicate glass that covers the entire sample and minimizes fibre burnout. The scale thickness is ～90?μm for the sample containing 5?vol.% SiC and decreases with increasing SiC content.     

Preparation of ZrC/SiC porous self-supporting monoliths via sol-gel process using polyethylene glycol as phase separation inducer

We present a straightforward method via sol-gel process using polyethylene glycol (PEG) as phase separation inducer to prepare zirconium carbide/silicon carbide (ZrC/SiC) porous monoliths. Organic/inorganic hybrid gels are prepared using zirconium oxychloride, furfuryl alcohol, and tetraethyl orthosilicate as major starting materials. In the presence of PEG, crack-free hybrid monoliths are obtained by drying the wet gels under ambient pressure, whereas in the absence of PEG, the wet gels break into pieces as expected. PEG plays a key role in maintaining the macroscopic shape of the monoliths. After ceramization at 1300–1500?°C, ZrC/SiC porous monoliths are obtained. SEM and mercury intrusion porosimetry data show that PEG also has strong influence on the microstructures of the monoliths. The compressive strengths of the ceramic monoliths are in the range of 0.3 to 0.7?MPa. And their compressive behavior starts to differ due to the changes in their microstructures, especially the pore structure.     

Covariance matrix adaptation evolution strategy based design of fixed structure robust H∞ loop shaping controller

This paper proposes the application of Covariance Matrix Adaptation Evolution Strategy (CMA-ES) in fixed structure H_∞ loop shaping controller design. Integral Time Absolute Error (ITAE) performance requirement is incorporated as a constraint with an objective of maximization of stability margin in the fixed structure H_∞ loop shaping controller design problem. Pneumatic servo system, separating tower process and F18 fighter aircraft system are considered as test systems. The CMA-ES designed fixed structure H_∞ loop-shaping controller is compared with the traditional H_∞ loop shaping controller, non-smooth optimization and Heuristic Kalman Algorithm (HKA) based fixed structure H_∞ loop shaping controllers in terms of stability margin. 20% perturbation in the nominal plant is used to validate the robustness of the CMA-ES designed H_∞ loop shaping controller. The effect of Finite Word Length (FWL) is considered to show the implementation difficulties of controller in digital processors. Simulation results demonstrated that CMA-ES based fixed structure H_∞ loop shaping controller is suitable for real time implementation with good robust stability and performance.     

Mechanophysical Cues in Extracellular Matrix Regulation of Cell Behavior

The extracellular matrix (ECM) is a macromolecular network that can provide biochemical and structural support for cell adhesion and formation. It regulates cell behavior by influencing biochemical and physical cues. It is a dynamic structure whose components are modified, degraded, or deposited during connective tissue development, giving tissues strength and structural integrity. The physical properties of the natural ECM environment control the design of naturally or synthetically derived biomaterials to guide cell function in tissue engineering. Tissue engineering is an important field that explores physical cues of the ECM to produce new viable tissue for medical applications, such as in organ transplant and organ recovery. Understanding how the ECM exerts physical effects on cell behavior, when cells are seeded in synthetic ECM scaffolds, is of utmost importance. Herein we review recent findings in this area that report on cell behaviors in a variety of ECMs with different physical properties, i.e., topology, geometry, dimensionality, stiffness, and tension.     

Novel thermal-sensitive properties of NBT-BZT composite ceramics for high-temperature NTC thermistors

We found for the first time that (1 − x) Na_0.5Bi_0.5TiO₃-xBiZn_0.5Ti_0.5O₃ (NBT–BZT) composite ceramics showed negative temperature coefficient (NTC) at a high temperature. The NBT–BZT nanopowders were successfully prepared by Pechini method. Their ceramics were sintered at 1100°C. The NBT–BZT ceramic exhibited a good linear relationship between logarithm of electrical resistivity (Inρ) and reciprocal of absolute temperature (1000/T) at 250°C–1050°C. The obtained ρ₆₀₀, ρ₉₀₀, and B_600/900 constants of the NBT–ZBT NTC thermistors are approximately 5.92 × 10⁶ to 3.01 × 10⁴ Ω cm, 7.03 × 10³ to 7.60 × 10² Ω cm and 2.3 × 10⁴-1.3 × 10⁴ K, respectively. The electrical characteristics can be tuned to the desired value by changing the Na_0.5Bi_0.5TiO₃ content in the compound. The electrical conductivity in these compounds is due to the electron jumps between Ti³⁺ and Ti⁴⁺ and oxygen-ion conductivity. Results demonstrate a tremendous potential of the studied system for perovskite materials with NTC performance.     

Effects of SiC content on the densification,microstructure, and mechanical properties of HfB2–SiC composites

To investigate the effects of SiC on microstructure, hardness, and fracture toughness, 0, 10, 20, and 30 vol% SiC were added to HfB₂ and sintered by SPS. Upon adding SiC to 30 vol%, relative density increased about 4%; but HfB₂ grain growth had a minimum at 20 vol% SiC. This may be due to grain boundary silicate glass, responsible for surface oxide wash out, enriched in SiO₂ with higher fraction of SiC. By SiO₂ enrichment, the glass viscosity increased and higher HfO₂ remained unsolved which subsequently lead to higher grain growth. Hardness has increased from about 13 to 15 GPa by SiC introduction with no sensible variation with SiC increase. Residual stress measurements by Rietveld method indicated high levels of tensile residual stresses in the HfB₂ Matrix. Despite the peak residual stress value at 20 vol% SiC, fracture toughness of this sample was the highest (6.43 MPa m^0.5) which implied that fracture toughness is mainly a grain size function. Tracking crack trajectory showed a mainly trans-granular fracture, but grain boundaries imposed a partial deflection on the crack pathway. SiC had a higher percentage in fracture surface images than the cross-section which implied a weak crack deflection.     

Al2O3/Yttria‐Stabilized Zirconia Hollow‐Fiber Membrane Incorporated with Iron Oxide for Pb(II) Removal

Removal by absorptive ceramic membranes can simultaneously absorb and separate metal ions from water. Alumina/yttria‐stabilized zirconia (Al₂O₃/YSZ) hollow‐fiber membranes, fabricated using phase inversion and sintering process, were deposited with iron oxide by an in‐situ hydrothermal process. The results showed that α‐Fe₂O₃ was produced and incorporated across the membranes. A reduction in flux was recorded with the deposition of α‐Fe₂O_3. However, it improved the adsorption capacity for heavy metal adsorption. The adsorption‐separation test demonstrated that the optimized membrane is able to completely remove Pb(II) ions after two hours.     

基于步冷试验的2.25Cr-1Mo-0.25V钢母材及焊缝回火脆化研究

对原始态、步冷态、脱脆态和脱脆步冷态2.25Cr-1Mo-0.25V钢母材及焊缝冲击试验结果进行分析,得到了母材和焊缝在不同状态下的韧脆转变温度vTr54.2和FATT以及脆化度ΔvTr54.2和ΔFATT。试验结果表明,步冷试验之后,母材发生较低程度脆化或脱脆现象,但是脆化度或脱脆度较低,表明母材具有良好的抗回火脆化性能;经脱脆试验后,母材和焊缝都发生较高程度的脱脆,表明材料的脆化主要是由于回火脆化引起的,脱脆试验使得材料的韧脆转变温度降低;脱脆步冷试验后,焊缝发生较高程度的脆化,焊缝对脱脆步冷试验的敏感性较高,脱脆步冷试验有效促进了焊缝的脆化。在相同脆化条件下,母材的脆化敏感性低于焊缝,焊缝更易发生脆化。     

Effects of structural characteristics on microwave dielectric properties of low-loss (Zn1-xNix)ZrNbTaO8 ceramics

Low-loss (Zn_1-xNi_x)ZrNbTaO₈ (0.02?≤?x?≤?0.10) ceramics possessing single wolframite structure are initiatively synthesized by solid-state route. Based on the results of Rietveld refinement, complex chemical bond theory is used to establish the correlation between structural characteristics and microwave performance in this ceramic system. A small amount of Ni²⁺ (x?=?0.06) in A-site with the fixed substitution of Ta⁵⁺ in B-site can effectually raise the Q?×?f value of ZnZrNb₂O₈ ceramic, embodying a dense microstructure and high lattice energy. The dielectric constant and τ_f are mainly affected by bond ionicity and the average octahedral distortion. The (Zn_0.94Ni_0.06)ZrNbTaO₈ ceramic sample sintered at 1150?°C for 3?h exhibits an outstanding combination of microwave dielectric properties: ε_r =?27.88, Q?×?f?=?128,951?GHz, τ_f =?–39.9?ppm/°C. Thus, it is considered to be a candidate material for the communication device applications at high frequency.