岩石龟裂系数法在火山岩裂缝储集层预测中的应用

 本文针对辽河东部凹陷油燕沟中生界火山岩的具体特征，采用纵波波速的比值——“龟裂系数”裂缝分析法［1,2,3］，研究了火山岩裂隙发育程度。综合龟裂系数裂缝分析及其他方法发现，该区中生界火山岩有效储集层的测井相特征主要表现为低密度、低中子、高声波时差和高伽马值等特征。此法的关键在于根据不同火山岩的岩性，选用合适的岩石骨架参数，在此基础上利用测井约束地震反演计算火山岩的层速度，进而计算出龟裂系数，然后根据已钻至火山岩井孔的测井相特征编制出火山岩预测厚度图。     

轴齿轮断齿失效分析

通过对轴齿轮断口形貌、硬度测试及金相组织等试验进行分析表明，齿根处没有进行硬化处理造成齿根处抗疲劳性能不足是导致轴齿轮疲劳断裂的主要原因，另外齿根过渡处倒角过小，且存在纵向刀痕引起了较大应力集中也是导致轴齿轮疲劳断裂的原因。     

40Cr钢复合热处理强韧化

用光学及电子显微镜(SEM.TEM)观察不同热处理的40Cr 钢的冲击及断裂韧性断口、及金相组织,阐明其间相互关系;断口结构可反映断裂特征,组织情况;细化晶粒提高强度、塑性和冲击韧性,但却减少脆断的特性距离 l 因而降低 K_(1c)模;减少碳(杂质)偏聚而使其呈较均匀地分布,从而减少可诱发塑坑的较粗大的碳(杂质)化合物的析出,即增加塑坑的间距 di 以及增加塑断组成物。从而都可增加断裂临界应变 ef,都可以提高 K_(1c)40Cr 复合热处理既靠先超高温淬、回火以减少碳(杂质)偏聚,改善其分布,以反增加位错马氏体从而提高 K_(1c),也靠后淬、回火细化晶粒而提高强度、塑性和冲击韧性,各自发挥长处达到强韧化。     

油泵柱塞和轴承外套失效分析

对断裂的油泵柱塞、轴承外套从成分、组织、工艺等方面进行了检验分析。结果表明，柱塞首先断裂，断裂后的柱塞碎片卡住了轴承外套，使轴承外套过载脆断。而柱塞的断裂是由于热处理不当，造成淬火加热温度过高，使柱塞的显微组织出现粗大的针状马氏体，并引起淬火裂纹，导致柱塞的韧性下降，脆性增大，随着载荷作用和液压油的渗入，裂纹进一步扩展，当裂纹扩展笃柱塞有效载面积承受不了全部工作应力时，发生脆性断裂。     

长庆上古生界气层CO2增能压裂工艺

长庆上古气藏物性差,压力系数低,水锁伤害大,采用常规水力压裂,入井液返排困难,气井产量低。在储层改造地质研究的基础上,通过对CO2泡沫压裂技术进行室内攻关,引进开发了CO2泡沫压裂酸性交联技术,优化了CO2泡沫方案设计及现场施工工艺,配套了CO2增能压裂工艺技术。经过现场应用,充分说明了CO2增能压裂是一项行之有效的工艺技术,对于提高单井产量和长庆气田整体开发水平都是有益的。     

Rapid determination of the fracture toughness of metallic materials using circumferentially notched bars

Three types of material whose fracture toughness tests were previously performed by using circumferentially notched bars, namely (1) a dual-phase steel with three different morphologies; (2) an Al-Zn-Mg-Cu-wrought alloy; and (3) Al-Si-cast alloys with three different Si contents, were investigated in terms of accuracy and reliability of the testing method. Also, the advantages of using circumferentially notched bars for fracture toughness determination of metallic materials were discussed. With the help of stress concentration factors, which are associated with the bluntness of the notch, correction factors for the fracture toughness calculations are derived. The corrected fracture toughness values are found to be close to the uncorrected ones, implying that the testing procedure is reliable.     

集成压裂机组研制

针对我国油田特定区决施工特点，通过对油田现用设备使用情况的分析和具体区决施工参数的统计，提出了集成压裂机组研制内容和配置，研制开发了集成压裂机组。产品结合了2000型压裂泵输出功率大、压力和排量覆盖范围合理的条件，集成了压裂车、混砂车、管汇车和仪表车的功能，实现了单台设备完成试压、压裂、酸化、防砂等多种施工流程，改变了常规施工作业设备种类和人员多、操作指挥复杂的施工模式，为油田提供了适合工艺要求的设备。     

金线断口的分析

运用扫描电子显微镜技术，对金线断口观察分析，讨论金线在拉伸过程中断裂时断口形貌及断裂的原因，发现，断裂是由于金锭中的气体和杂质引起的，并提出改进生产工艺的意见。     

Microstructure-related fracture toughness and fatigue crack growth behaviour in toughened, anhydride-cured epoxy resins

Fracture toughness and fatigue crack propagation (FCP) of plain and modified anhydride-cured epoxy resin (EP) were studied at ambient temperature. Liquid carboxyl-terminated acrylonitrile-butadiene (CTBN) and silicon (SI) rubber dispersions were used as tougheners for the EP. The morphology of the modified EP was characterized by dynamic mechanical analysis (DMA) and by scanning electron microscopy (SEM). The fracture toughness, K_c, of the compositions decreased with increasing deformation rate. K_c of the EP was slightly improved by CTBN addition and practically unaffected by incorporation of the SI dispersion when tests were performed at low cross-head speed, v. Both modifiers improved K_c at high v, and also the resistance to FCP, by shifting the curves to higher stress intensity factor ranges, ΔK, by comparison with the plain EP. It was established that both fracture and fatigue performance rely on the compliance, J_R, at the rubbery plateau, and thus on the apparent molecular mass between crosslinks, M_c. The failure mechanisms were less dependent upon the loading mode (fracture, fatigue), but differed basically for the various modifiers. Rubber-induced cavitation and shear yielding of the EP were dominant for CTBN, whereas crack bifurcation and branching controlled the cracking in SI-modified EP. The simultaneous use of both modifiers resulted in a synergistic effect for both the fracture toughness at high deformation rate and the FCP behavior.     

The combined effects of curing and environmental exposure on fracture properties of woven carbon/epoxy laminates

This paper concerns a study of the combined effects of curing conditions and environmental exposure on the ultimate properties of two commercial woven carbon/epoxy laminates. Curing parameters (heating rate and applied pressure) were varied so as to obtain six different conditions for each material. Moisture saturation was also achieved by exposing some of the cured samples to environmental conditions of 70°C and 95% relative humidity. Four different tests (tensile, impact, Mode I and Mode II interlaminar fracture resistance) were therefore performed, and the results obtained on the different materials before and after moisture saturation compared. Neither curing pressure nor heating rate nor moisture absorption were observed to have any practical effect on tensile and impact properties. On the contrary, one noticeable effect was the interlaminar fracture resistance of the laminates. The results are discussed and interpreted in terms of damage formation and stress intensification mechanisms.