超声波湿法混炼炭黑/天然橡胶复合材料的性能研究

利用超声波的乳化均质作用,将经水湿润的炭黑与稀释的天然胶乳混合均匀,然后采用蒸发成膜法和胶凝成膜法制备胶膜(炭黑/天然橡胶复合材料),探究制膜方法及超声波处理时间和功率对胶膜性能的影响。结果表明:蒸发成膜法成膜时间过长,打开的炭黑二次结构重新团聚,胶膜中炭黑分散性差,胶膜的拉伸强度较小,而胶凝成膜法稳定性更高,胶膜中炭黑分散性好;超声波处理时间为90 s、功率为840~960 W时,超声波的乳化均质效果最好,炭黑二次结构打开程度更高,此时采用胶凝成膜法制备胶膜,成膜速度快,炭黑来不及团聚,胶膜中炭黑分散性较好和结合橡胶较多,胶膜的拉伸强度较大。     

直流电弧等离子体法制备超细Ag粉研究

采用自行研制的高真空双枪直流电弧金属纳米粉连续制备设备,制备了高纯度的超细银粉,并采用正交试验的方法研究了各工艺参数对粉体产率及粒径分布的影响。利用X射线衍射（XRD）、透射电子显微镜（TEM）和相应选区电子衍射（SAED）以及Simple PCI软件对样品的成分、形貌、晶体结构和粒径分布进行了分析。结果表明：所得银粉纯净无污染,属多晶型结构,平均粒径在38-220nm范围内,粒径分布窄;最大产率比同类研究结果提高了近17倍;电流和充气压力分别是影响产率和粒径分布的显著性因素。     

THEORY DEPOSITION MODEL AND INFLUENCING FACTORS DURING PROCESS OF PREPARING MICRO-LAYER LAMINATE BY EBPVD

This paper briefly introduces the characteristics of electron beam physical vapor deposition (EBPVD) technique and the whole process of preparing micro-layer composite laminate. And several major influencing factors are presented and discussed. It was found that residual gas pressure should be low enough to guarantee the unobstructed transportation of vapor steam and electron beam; the evaporation method and evaporation speed are up to the different vapor pressure deficit of compositions of raw materials; and the substrate temperature could have great influence on the microstructure of the micro-layer laminates.     

真空熔炼AZ91镁合金过程中Mg元素的蒸发行为

在真空Ar气氛中熔炼AZ91镁合金，测定了不同精炼温度下Mg元素的蒸发速率。结果表明，随着精炼温度的升高，Mg元素的蒸发量增大。通过计算可知，Mg的蒸气压是Al的10^9倍，是Zn的46倍，因此主要是Mg的蒸发而导致合金其他元素含量升高。XRD分析表明，蒸发物是Mg元素。结合Mg元素的蒸发机制，在该试验条件下推导出Mg元素蒸发率的计算公式以及Mg元素的表观传质系数、蒸发率与精炼温度的关系，计算得出Mg元素蒸发率为0．86×10^-3-1．35×10^3g／cm^2·s，Mg元素的表观传质系数在2×10^-5-24×10^-5cm／s范围内。     

Si纳米纤维的等离子体制备工艺

本文利用电弧等离子体蒸发制备了纳米Ｓｉ纤维，通过沉积温度场的调节，确定了纤维的最佳沉积温度约６００℃，同时表征了纤维的生长过程，在一定的温度下，Ｓｉ团聚体颗粒间的“颈连接”及颗粒表面的非晶层是导致团聚体自扩散和表面扩散一维生长的直接条件。     

Induction plasma spheroidization of tungsten and molybdenum powders

The melting, evaporation and oxidation behaviors as well as the solidification phenomena of tungsten and molybdenum in induction plasma were studied. Scanning electron microscopy was used to examine the morphology and the cross section of plasma-processed powders. X-ray diffraction was used to analyze the oxides formed on the particle surface of these two metals. The influence of spray chamber pressure on the spheroidization and oxidation phenomena was discussed. The results show that fewer Mo particles than W particles are spheroidized at the same powder feed rate under the same plasma spray condition although molybdenum has a lower melting point. A small fraction of tungsten is evaporized and condensed either on the surface of tungsten particles nearby or on the wall of spray chamber. Tungsten oxides were found in tungsten powder processed under soft vacuum condition. Extremely large grains form inside some spheroidized particles of tungsten powder.     

Structural and mechanical properties of AlTiN/CrN coatings synthesized by a cathodic-arc deposition process

Monolayered AlTiN and Multilayered AlTiN/CrN coatings were synthesized by a cathodic-arc deposition process, using TiAl (with 50/50 and 33/67 at.%) and Cr elemental cathodes. The atomic ratio of Al/(Ti + Al) in the AlTiN coatings was reduced to 0.44 and 0.61, respectively, compared with the corresponding Ti₅₀Al₅₀ and Ti₃₃Al₆₇ cathode materials. The multilayered AlTiN/CrN films showed smaller crystallite size, larger lattice strain, higher hardness, higher residual stress, and better adhesion strength as well than the monolayered AlTi films. The multilayered Al_0.35Ti_0.22N_0.43/CrN coating exhibited the highest hardness of about 38 GPa and the highest H³/E*² ratio value of 0.188 GPa, indicating the best resistance to plastic deformation, among all the coatings studied.     

Effect of surface modification of metal hydride electrode on performance of MH/Ni batteries

A novel method was applied to the surface modification of the metal hydride(MH)electrode of MH/Ni batteries.Both sides of the electrode were plated with a thin silver film about 0.1μm thick using vacuum evaporation plating technology,and the effect of the electrode on the performance of MH/Ni batteries was examined.It is found that the surface modification can enhance the electrode conductivity and decrease the battery ohimic resistance.After surface modification,the discharge capacity at 5C(7.5A)is increased by 212 mA.h and the discharge voltage is increased by 0.11 V,the resistance of the batteries is also decreased by 32%.The batteries with modified electrode exhibit satisfactory durability.The remaining capacity of the modified batteries is 89%of the initial capacity even after 500 cycles.The inner pressure of the batteries during overcharging is lowered and the charging efficiency of the batteries is improved.     

蒸发法制备Ni－Ti纳米非晶合金粒子

采用气相蒸发法制备纳米量级的Ｎｉ－Ｔｉ非晶合金粒子，研究了各种因素对Ｎｉ－Ｔｉ纳米非晶合金粒子形成的影响，并用透射电子显微镜，高分辨电子显微镜，Ｘ射线衍射仪和能谱等多种手段对纳米非晶合金粒子进行了表征．结果表明，当粒子成分在共晶区Ｎｉ（４０）Ｔｉ（６０）附近时，容易形成非晶；较低惰性气体压力和较高蒸发温度有利于Ｎｉ－Ｔｉ纳米非晶粒子的形成．     

Spin-valve magnetoresistance in Co/Si/（Co/Cu/Co） multilayers

A series of Co/Si/（Co/Cu/Co） multilayers and Co/Si/Co sandwiches were prepared by high vacuum electron-beam evaporation. It was found that a Si spacer （≥0.9 nm） could greatly decrease the interlayer coupling in Co/Si/Co sandwiches and there was no magnetoresistance（MR） or spin-valve MR in them due to the high resistivity of Si spacer. While in Co/Si/（Co/Cu/Co） multilayers, we observed a spin-valve MR of about 0.5% through a nominal 2.7 nm Si spacer at room temperature. The spin-valve MR in Co/Si/（Co/Cu/Co） multilayers was attributed to the enhanced spin polarization of conduction electrons caused by the top Co/Cu/Co sandwich with GMR mechanism and high spin-dependent scattering at Co/Cu interface.