碱式碳酸铅的生产工艺研究

介绍了由氧化铅与冰醋酸在一定温度下反应生成碱式醋酸铅，碱式醋酸铅在一定条件下与二氧化碳反应生成碱式碳酸铅，再经沉淀、抽滤，制得结晶产品。探讨了溶液pH、反应温度、二氧化碳流量、水中的杂质、总铅质量分数等对碱式碳酸铅结晶的影响，得出了制备碱式碳酸铅的最佳工艺条件：pH=6．5时停止通入二氧化碳，反应温度25～30℃，二氧化碳流量控制在0．5～3L／min，把河水或自来水经过离子交换处理，溶液中总铅质量分数控制在2％～5％。     

可见光响应的"Cu核- Cu2O壳"型光催化剂性能的研究

以碱性染料结晶紫为目标污染物,金属卤化物灯为可见光光源,研究了自制的"Cu核-Cu20壳"微粒的光催化性能.实验结果表明,该催化剂对可见光有良好的响应,当固液比为1500,光照120min,质量浓度为60mg/L的结晶紫溶液色度和COD去除率分别达98%和92%.检测结果表明,光催化过程中有氢氧自由基产生,染料发生了彻底的降解.     

Study of the copper leaching in the wet oxidation of phenol with CuO-based catalysts: Causes and effects

Catalytic wet oxidation of phenol as a model pollutant has been performed in a three phase fixed-bed reactor (FBR) by using a commercial catalyst based on copper oxide in order to analyze the variables affecting significantly the copper leaching. It has been found that temperature has an almost negligible influence in the range studied (70–160 °C). On the contrary, an important effect of the pH value was noticed. The copper leaching reduces when the pH of the solution fed to the reactor increases, being almost negligible at pH ≥ 5. Moreover, the composition of the reaction media also influences the leaching. Higher copper concentrations than those expected by the effect of the acid aqueous media have been measured in the reactor effluent when phenol, catechol, hydroquinone, p-benzoquinone and maleic acid are present in the reaction media. On the contrary, oxalic acid has a negative influence on the leaching, since it captures the copper in solution to form copper oxalate which precipitates on the catalyst surface. For a previously acidified medium, the acetic and formic acids do not have any other effect on the copper leaching. It has been also demonstrated that as copper in solution decreases, so does phenol conversion, because the homogeneous catalysis contributes significantly to the oxidation reactions even in fixed-bed reactors.     

氧化锌分散体光反应产生的自由基中间体

溶液中光诱导的电子转移反应已进行了大量的研究。而半导体粉末在水相或非水溶剂中的光化学研究也与自俱增。这种光化学与成像体系、太阳能转换以及光催化或污物的光降解有关。因此,越来越引起人们的重视。 Harbour和Hair用自旋捕捉技术研究了在ZnO-H_2O的分散体系中光合成过氧化氢,并检测到羟基自由基。他们认为氧化锌可能通过水的氧化将O_2还原成H_2O_2,从而使太阳能转换成化学能。人们自然会想到ZnO在其它溶剂中是否-也能观察到溶剂光氧化     

Au/ZnO and Au/Fe2O3 catalysts for CO oxidation at ambient temperature: comments on the effect of synthesis conditions on the preparation of high activity catalysts prepared by coprecipitation

The preparation of Au/ZnO and Au/Fe₂O₃ catalysts using two coprecipitation methods is investigated to determine the important factors that control the synthesis of high activity catalysts for the oxidation of carbon monoxide at ambient temperature. In particular, the factors involved in the preparation of catalysts that are active without the need for a calcination step are evaluated. The two preparation methods differ in the manner in which the pH is controlled during the precipitation, either constant pH throughout or variable pH in which the pH is raised from an initial low value to a defined end point. Non-calcined Au/ZnO catalysts prepared using both methods are very sensitive to pH and ageing time, and catalysts prepared at a maximum pH = 5 with a short ageing time (ca. 0–3 h) exhibit high activity. Catalysts prepared at higher pH give lower activity. However, all catalysts require a short operation period during which the oxidation activity increases. In contrast, the calcined catalysts are not particularly sensitive to the preparation conditions. Non-calcined Au/Fe₂O₃ catalysts exhibit high activity when prepared at pH ≥ 5. Calcined Au/Fe₂O₃ prepared using the controlled pH method retain high activity, whereas calcined catalysts prepared using the variable pH method are inactive. The study shows the immense sensitivity of the catalyst performance to the preparation methods. It is therefore not surprising that marked differences in the performance of supported Au catalysts for CO oxidation that are apparent in the extensive literature on this subject, particularly the effect of calcination, can be expected if the preparation parameters are not carefully controlled and reported.     

In situ synchrotron X-ray studies on copper-nickel 5 V Mn oxide spinel cathodes for Li-ion batteries

Partial substitution of Mn in lithium manganese oxide spinel materials by Cu and Ni greatly affects the electrochemistry and the cycle life characteristics of the cathode. Substitution with either metal or a combination of both metals in the spinel lattice structure reduces the 3.9-4.2 V potential plateaus associated with the conversion of Mn³⁺ to Mn⁴⁺. Higher potential plateau associated with oxidation of the substituted transition elements is also observed. These substituents also significantly alter the onset of Jahn-Teller distortions in the 3 V potential plateau. Synchrotron based in situ X-ray absorption (XAS) was used to determine the exact nature of the oxidation state changes in order to explain the overall observed capacities at different potential plateaus. The studies on LiCu_0.5Mn_1.5O₄ show single phase behavior in the 4-5 V potential region with a good cycle life. Lower cycle life characteristic observed in cycling LiNi_0.5Mn_1.5O₄ and LiNi_0.25Cu_0.25Mn_1.5O₄ versus Li metal are ascribed to coexistence of several phases in this potential region. However, LiCu_0.5Mn_1.5O₄ shows onset of Jahn-Teller distortions in the 3 V potential plateau, in contrast to LiNi_0.5Mn_1.5O₄ and LiNi_0.25Cu_0.25Mn_1.5O₄ cathode materials.     

三盐基硫酸铅的生产工艺条件研究

介绍了氧化铅法中硝酸铅法生产三盐基硫酸铅两种生产工艺 ,对氧化铅法中硫酸的加入量、酸度、温度、时间等生产条件进行了研究 ,确定了最佳生产工艺条件 ,并对两种方法进行了简单对比     

Sintering of Pt/Al2O3 reforming catalysts: EXAFS study of the behavior of metal particles under oxidizing atmosphere

The effect of an oxidative atmosphere (300 °C) is studied on fresh and sintered unchlorinated naphtha reforming catalysts containing 0.6–1% Pt. The TPR profiles show that only one species is formed using our experimental conditions, regardless of the mean crystallite size of the metal particles. The structural information supplied by EXAFS compared with cuboctahedral particle modeling, implies that such species is a surface platinum oxide, the structure of which is close to that of PtO₂, but largely distorted. This is true whether the catalyst is sintered or not.     

氧化铁生产废液的治理和利用

氧化铁生产产生的含铁硫酸铵废液和洗涤废水中含有铁、硫酸根、铵等离子。采用化学沉淀、过滤、蒸发等方法处理该废水可回收废水中的硫酸铵、氧化铁、处理后的废水可回用于生产。     

氧化石墨烯/石蜡复合相变乳液的制备及对流传热特性

为提高石蜡相变乳液的传热性能，通过添加氧化石墨烯(GO)，制备了GO/石蜡复合相变乳液并对其相关性能进行了表征。搭建了流动阻力、对流换热试验台，对比研究了石蜡相变乳液及GO/石蜡复合相变乳液的流动阻力特性和对流换热特性，试验结果表明，由于GO的亲水性，复合相变乳液都表现出较好的稳定性。当GO的质量分数为0.01％、0.02％、0.03％时，复合相变乳液的热导率分别增加了20.01％、30.50％、35.18％。添加GO使乳液的流动阻力略有增加，直管段最大增加了6.70%，90°弯管处最大增加了13.20%；对流传热系数随着GO浓度的增加而增大，当GO浓度为0.03％时，对流传热系数最大提高了43.90％。