Comparison of interfaces in Ti composites reinforced with uncoated and TiB2/C-coated SiC fibres

Interfaces play an important role in determining the mechanical properties of composite materials. The interfaces established between a titanium-alloy matrix (Ti-6Al-4V) and uncoated and TiB₂/C-coated SiC fibres are analysed by scanning electron microscopy, transmission electron microscopy and X-ray techniques. Emphasis is placed upon the interfacial morphology and microstructure, identification of reaction products, and the stability of the coating layer. Complex multi-reaction layers are observed frequently in the interfacial zones. Previous, often contradictory, reports about the interlayers are reviewed. Experimental observation demonstrates that the type and distribution of interlayers vary in a given system, due to prolonged treatment of the samples at temperature. The formation and distribution of the interlayers are discussed further, with respect to these and previous findings. Methods of reducing interfacial reactivity are discussed.     

高能球磨AL─Cu合金固态合成反应研究

采用扫描电镜、能谱分析、Ｘ射线衍射和示差扫描量热分析研究了具有较大负混合焓的Ａｌ＿ｘＣｕ＿（１－ｘ）对称扩散系合金的高能球磨固态合成反应。高能球磨时组元晶粒细化达纳米级，造成纳米晶界亚互溶，为室温固态合成反应创造了条件，球磨强度对反应进程影响显著，在ｘ＝０．３～０．７范围内仅形成一种金属间化合物。     

Zirconium-based intermetallics as heterogeneous catalysts for the fischer-tropsch reaction: I. Zr-Ni-Co catalysts

Alloys of the general formula Zr₅₀Ni_xCO_50-x, where 0 ≦x≧ 50, have been prepared and used in the temperature range 300–400°C, in the pressure range 1–9 barg in a microtubular reactor for the reaction of hydrogen with carbon monoxide to give hydrocarbons. The alloys or intermetallic materials were prepared by argon arc melting, powdered by hydrogen decrepitation and characterised by means of optical microscopy (metallography), scanning electron microscopy with surface analysis and magnetic susceptibility measurements. The selectivity towards higher hydrocarbons increased with (i) increase in the total pressure and (ii) decrease in hydrogen content of the feed gases. The kinetics were found to be of the form: where m = 1.0 ± 0.2 and n = 0. The apparent energy of activation (E_a) lay in the range of 80–130 kJ mole^?1 and there appeared to be a compensation effect between E_a and the pre-exponential factor A. The turnover numbers for the reaction exhibited an activity maximum for alloys of composition around Zr₅₀Ni₄₀Co₂₀ and Zr₅₀Ni₃₀Co₂₀. Magnetic susceptibility measurements indicated that alloys changed their nature from moderately paramagnetic to strongly paramagnetic or even ferromagnetic after use and this is attributed to the conversion of zirconium to zirconium oxide during reaction with the attendant production of free 3d-transition metals. Derived catalysts prepared by air treatment of the hydrogen-decrepitated intermetallics behaved almost identically to the latter materials and gave similar magnetic susceptibility values to used hydrided materials.     

高温钎料PdCu-Ti在氧化铝陶瓷上的润湿性及界面反应

本文采用座滴法试验研究了合金系统ＰｄＣｕ－Ｔｉ在Ａｌ２Ｏ３上润湿性的变化规律，探讨了界面冶金及结合等行为，运用热力学理论对结果进行了分析，随Ｔｉ含量的增加及Ｐｄ含量的减少润湿角逐渐降低，Ｔｉ的加入使界面发生了一个双重变化；液相侧富氧，钛吸收层的生成及随后的固相侧氧化钛的生成，只有界面上生成一氧化钛，才能有较好的润湿行为和较强的结合力。     

Reaction process of monazite and bastnaesite mixed rare earth minerals calcined by CaO-NaCl-CaCl2

The decomposition reactions of monazite and bastnaesite mixed rare earth minerals calcined by CaO-NaCl-CaCl2 were studied by means of TG-DTA and XRD. The results show that the process of the minerals decomposed by CaO involves two steps. The first step occurs in the temperature range of 425-540 ℃, and the main reactions are bastnaesite decomposition, i.e. REOF reacts with CaO to produce RE2O3 and CaF2, and Ce2O3 is oxidized to CeO2. During this step, CaCO3 is formed at about 500 ℃. The second step takes place in the temperature range of 610-700 ℃, and the reactions are monazite decomposition into RE2O3, Ca5F（PO4）3 and Ca3（PO4）2 by CaO and CaF2. In this process, the decomposition ability is improved because CaO from CaCO3 decomposing has high chemical activity. In calcining process, the new formed Ca5F（PO4）3 restrains fluorine that can escape in form of gaseous compound. The decomposition ratio of the mixed rare earth minerals reaches 90.8% at 700 ℃.     

多孔普鲁士蓝类似物的合成及电催化析氧性能

采用一种简单易行的共沉淀法合成了前驱体镍铁普鲁士蓝类似物NiFe-PBA（NF）,然后通过溶剂热处理获得了镍铁普鲁士蓝纳米多孔材料（NFP）。通过XRD、SEM、TEM、XPS、BET及电化学方法对所得材料进行了结构表征和析氧性能测试。结果表明,NFP相对于前驱体NF,电化学比表面积增大、催化活性位点增多,电催化析氧反应（OER）性能显著提高。在浓度1 mol/L KOH水溶液中,达到10 mA/cm2电流密度时,NFP所需过电位仅为260 mV,比NF（320 mV）前驱体低18.75%,也优于大多数已报道的非贵金属催化剂和商用贵金属催化剂,显示出良好的应用前景。     

磷酸二苯酯催化的2-吲哚甲烷胺衍生物的合成

以磷酸二苯酯为催化剂,3-甲基吲哚类化合物与亚胺通过Friedel-Crafts加成反应一步合成了具有广泛药理活性的2-吲哚基甲烷胺类化合物,对反应条件进行优化。结果表明,当n(3-甲基吲哚类)∶n(亚胺)∶n(磷酸二苯酯)=1.0∶2.0∶0.1,其中,磷酸二苯酯0.0025 mmol,1 mL无水二氯甲烷作溶剂,室温下反应0.5 h时,即可得到高收率2-吲哚基甲烷胺类衍生物（85%~90%）。产物经 1HNMR、13CNMR 和 HRMS 进行了结构确定。     

The Synthesis of Covalent Triazine-Based Frameworks via Friedel–Crafts Reactions of Cyanuric Chloride with Thienyl and Carbazolyl Derivatives for Fluorescence Sensing to Picric Acid,Iodine and Capturing Iodine

A multifunctional thiophene-based covalent triazine framework (TTPATTh) with triphenylamine as core is synthesized by Friedel–Crafts reaction of cyanuric chloride with thienyl derivative for the first time. The yield of TTPATTh (99.59%) is far higher than that of the carbazole-based CTF (TTPATCz, 47.03%). TTPATTh and TTPATCz possess high BET surface areas with 1235 and 2501 m² g^–1 as well as high pore volumes with 1.60 and 2.23 cm³ g^–1, respectively. TTPATTh and TTPATCz have high thermal stability with high thermal decomposition temperatures of 514 and 598 °C in nitrogen atmosphere. With the introduction of triazine rings, the fluorescence sensing sensitivities of TTPATTh and TTPATCz to picric acid and iodine are improved significantly. Especially for TTPATTh, the K_sv values reach 5.95 × 10⁵ and 1.61 × 10⁴ L mol^–1, and LODs reach 1.02 × 10^–12 and 1.86 × 10^–12 mol L^–1. To the best of the knowledge, this is the most sensitive value among thiophene-based porous organic polymers to PA and I₂. Furthermore, TTPATTh and TTPATCz can also adsorb iodine in vapor phase, cyclohexane solution and aqueous solution, and release iodine by heating or in ethanol solution. The efficiency of controlling the release of iodine is higher than that in ethanol.     

Synthesis and characterization of poly acrylic acid/graphite oxide nanocomposite

1　INTRODUCTIONOrganic intercalatedlayeredsolidshavebeenstudiedbyscientistsindifferentfieldsformanyyearsbecauseoftheirnew physicalandchemicalpropertiessuchaselectricalproperties[1] ,mechanicalproper ties ,thermalbehavior[2 ] ,surfaceandinterfacialproperties[3] .Graphiteoxide (GO)hasbeenstudiedformany years ,itsstructuralmodel[4 6 ] ,formationprocessandkinetics[7,8] havebeenstudiedindetail.IthasbeenreportedthatGOpossessesC OHande poxidefunctionalgroups[9] whichmakegraphiteox ideeasilyabs…     

固液挤压下陶瓷粒子增强铝基复合材料组织特点及其形成机制

本文使用接触反应法制备ＴｉＣｐ／ＬＹ１２复合材料熔体，然后经固液挤压直接制取复合板材与棒材。使用背散射扫描电镜对Ｔ６处理后的复合板材组织特点进行观察，揭示了颗粒的分布特征、基体组织特点及其成因。