Threshold and growth mechanism of fatigue cracks under mode II and III loadings

ABSTRACT The fatigue crack growth behaviour of 0.47% carbon steel was studied under mode II and III loadings. Mode II fatigue crack growth tests were carried out using specially designed double cantilever (DC) type specimens in order to measure the mode II threshold stress intensity factor range, ΔK_IIth. The relationship ΔK_IIth > ΔK_Ith caused crack branching from mode II to I after a crack reached the mode II threshold. Torsion fatigue tests on circumferentially cracked specimens were carried out to study the mechanisms of both mode III crack growth and of the formation of the factory‐roof crack surface morphology. A change in microstructure occurred at a crack tip during crack growth in both mode II and mode III shear cracks. It is presumed that the crack growth mechanisms in mode II and in mode III are essentially the same. Detailed fractographic investigation showed that factory‐roofs were formed by crack branching into mode I. Crack branching started from small semi‐elliptical cracks nucleated by shear at the tip of the original circumferential crack.     

Low-cycle fatigue properties of eutectic solders at high temperatures

This paper details the deformation mechanism and low‐cycle fatigue life of eutectic solder alloys at high temperature (around 0.8T_m). Grain boundary sliding generally nucleates a wedge‐type cavity that reduces the low‐cycle fatigue life of metals. In this study, grain boundary sliding has promoted intergranular failure contributing to the reduction in fatigue life of Sn–Ag–Cu alloy. However, grain boundary sliding has exerted no deleterious effects on fatigue resistance of eutectic Pb–Sn and Bi–Sn alloys. The phase boundary sliding with very fine microstructure induces exceptional ductility in these alloys leading to superior low‐cycle fatigue endurance for theses eutectic Pb–Sn and Bi–Sn alloys.     

一种基于PWM的半桥型开关电源

主要介绍了由SG3525组成的半桥型开关稳压电路的结构和工作原理，阐述了PWN集成电路SG3525的特性和主要功能。实践表明：该系统工作稳定，运行效果良好。     

实验应变／应力模态分析若干问题的进展评述

本文评述了实验应变／应力模态分析进展的若干基本问题。主要是：应变响应与位移响应的关系；应变频响函数矩阵的特点及其测量方法；应变模态的加权正交性及其识别方法；以及其他问题。     

珠江口盆地开平凹陷油气聚集条件分析

珠江口盆地自新生代以来,曾先后受到不同方向张应力的作用,造成了不同时期构造体系的交叉叠合.中中新世以来构造运动强烈,并具有东强西弱的特点,对油气的运移与聚集产生了重要影响.开平凹陷的剧烈断裂和断陷活动始于始新世,并在同期沉积了巨厚的文昌组.晚渐新世以后,由于断裂活动非常微弱,在成熟的烃源岩与其上地层之间缺乏有效的油源断层,因而自生自储、近距离运移可能是开平凹陷油气聚集的基本特征.在凹陷内部,因重力滑动和欠压实泥岩共同作用所形成的KPll-1构造带可能是该区最具有油气远景的地区.     

The TDCPR Management Mode of Engineering Equipment

The Three Gorges Project is a very large project,and its structure is very complex.Interna-tional advanced engineering equipment is broadly used.The state of equipment running directly influ-ences project building qualities and limited time.According to the factud conditions of the Three Gor-ges Project,the characteristics of engineering equipment are analyzed.At the same time ,some theories about equipment management are induced ,and the TDCPR management mode of engineering equip-ment of the Three Gorges Project is put forwared in order to gain the aim of managing and using equip-ment well and speeding up the project construction.     

ATM协议的测试研究及其应用

协议一致性测试和互操作性测试是保证不同厂商的ＡＴＭ产品和服务实现完全的互通的重要技术手段，本文分析了ＡＴＭ协议的测试需求，提出了适合的测试结构和测试描述技术，并结合适配层协议ＣＰＡＡＬ５讨论了协议集成测试系统ＰＴＴＳ在ＡＴＭ协议测试中的应用。     

广州中城广场主体工程施工技术

广州中城广场工程结构形式复杂，平面曲折多角。施工中在应用多种模板体系、泵送混凝土、无粘结预应力楼板及核心筒部分小平台滑模等方面，采用了多项新技术，保证了工程质量，加快了工程进度。     

多棒高功率固体激光器动态模匹配研究

采用光学矩阵分析了多元热透镜谐振腔内模式的动态匹配特征,给出了平平腔参数调整的关系式,实验结果与理论分析相符,并在两棒连续Nd:YAG系统上得到0W～530W功率范围的稳定输出.