Preparation, Characterisation and Catalytic Behaviour of a New TeVMoO Crystalline Phase

TeM_xMo_1.7O mixed oxides (M = V and/or Nb; x = 0-1.7) have been prepared by calcination of the corresponding salts at 600 °C in an atmosphere of N₂. A new crystalline phase, with a Te/V/Mo atomic ratio of 1/0.2-1.5/1.7, has been isolated and characterised by XRD and IR spectroscopy. This phase is observed in the TeVMo or TeVNbMo mixed oxide but not in the TeNbMo mixed oxide. The new crystalline phase shows an XRD pattern similar to Sb₄Mo₁₀O₃₁ and probably corresponds to the M1 phase recently proposed by Aouine et al. (Chem. Commun. 1180, 2001) to be present in the active and selective MoVTeNbO catalysts. Although these catalysts present a very low activity in the propane oxidation, they are active and selective in the oxidation of propene to acrolein and/or acrylic acid. However, the product distribution depends on the catalyst composition. Acrolein or acrylic acid can be selectively obtained from propene on Nb-free or Nb-containing TeVMo catalysts, respectively. The presence of both V and Nb, in addition to Mo and Te, appears to be important in the formation of acrylic acid from propene.     

电沉积法制备铜分散电极

研究了电沉积制备铜分散电极的方法,通过对阴极极化曲线的测试,考察了电流密度及不同冲击电流方式对铜粉粒度的影响。结果表明:适当的电流密度、合适的分散剂、间歇式的电流是得到较细铜粉的条件。同时对铜分散电极的电化学性质进行初步测试,结果表明铜粉细化以后,铜分散差电池的电动势值有所上升。     

再磨与擦洗对提高钼精矿质量影响试验研究

就再磨与擦洗对提高钼精矿质量的影响进行了试验研究。结果表明 ,增加Ⅲ段再磨、Ⅳ段擦洗作业可有效地提高钼精矿质量     

In situ formation of multi scale reinforcing phases to improve performance of Al2O3-SiC C castables

In order to improve the physical properties and slag corrosion resistance of refractory materials for hot metal pretreatment, different contents of composite metal powders (CMP) were introduced into Al2O3-SiC-C refractory castables. The effect of CMP on the microstructure, physical properties and slag corrosion resistance of Al2O3-SiC-C refractory castables were studied. The results show that the multi scale reinforcing phases including flake crystals, rod shaped fibers, filamentous fibers and whiskers are in situ formed in the samples with addition of CMP, which result to the improvement of the cold modulus of rupture and cold crushing strength. When the addition of CMP is 6 wt.%, the high temperature modulus of rupture increases by 231%, the thermal shock resistance increases by 77% after thermal shock by water cooling 5 times and the percentage of the slag resistant area reduces by 37.2%.     

聚苯硫醚复合涂层的耐磨性能

研究了用固体润滑石墨、碳化硅、二硫化钼等填料改性的聚苯硫醚 (PPS)涂层的耐磨性能。实验结果表明 ,聚苯硫醚复合涂层具有优良的耐磨性 ;加入适量 ( 3 0 % )的石墨、碳化硅等固体润滑剂 (石墨 :碳化硅 =2∶3 ) ,可以有效提高涂层的耐磨性能 ,而二硫化钼和三氧化二铬的减摩效果更佳     

Dynamic modes of Ti combustion in a coflow of N<Subscript>2</Subscript>-Ar mixture

Combustion of bulk density Ti powder (containing 20 wt % TiN as a diluent) in a coflow of N₂-Ar mixture was investigated upon variation in the nitrogen content of the gaseous mixture. The obtained data are believed to open up new horizons for fabrication of layered and composite ceramics by infiltration-mediated combustion.      

Characteristics of Milk Powders Produced by Spray Freeze Drying

Skim and whole milk powders were manufactured at lab scale by spray freeze drying (SFD), using liquid nitrogen as the cryogen. The polydispersity of droplet/particle sizes was limited using an encapsulator nozzle to atomize the feed. Particle morphology was examined using a scanning electron microscope. Samples were compared with equivalent spray-dried powders in tests of wettability and dissolution in water. The spray freeze-dried powders were found to be highly porous, with a uniform structure of pores throughout the entire particles. When tested in water, SFD skim milk powders wetted roughly three times as fast as industrially spray-dried agglomerated skim milk powders and were observed to dissolve rapidly by breaking down into smaller particles.     

注射成形粘结NdFeB磁体:工艺·性能·应用

综合介绍了几种适于注射成形粘结NdFeB磁体的磁粉制备方法及特点；讨论了粘结剂、改性剂及磁场取向对注射成形NdFeB磁体最终磁性能的影响及其应用市场。在此基础上，指出了今后开展研究工作的方向。     

籼米淀粉超微粉体的制备及其性质

研究了籼米淀粉超微粉体的一种新的制备方法 ,通过正交实验确定了酶处理淀粉的最佳条件 ,考察了淀粉的溶解度和膨润力。结果表明 ,酶处理淀粉的最佳工艺参数为 :水解温度４５℃ ,时间为２５ｈ ,酶用量为水解淀粉的４５%。随着粒径的减小 ,淀粉的溶解度增大 ,膨润力下降。