The mechanism for the colour change of iron chromium black pigments in glazes through transmission electron microscopy techniques

Black iron-chromium (Fe-Cr) bearing oxide pigments are generally utilised as effective colourants in a wide variety of applications. However, in the case of their use within ZnO-containing glazes, they yield an undesirable brown colour instead of expected black colour. In order to understand the colour change in this system, we report the use of focused ion beam (FIB) sample preparation technique followed by the use of analytical transmission electron microscopy (TEM) characterisation techniques. According to the results, the formation of a reaction layer between the pigment and glaze was identified with an average composition of Zn_0.48Fe_0.79Cr_1.32O₄. Additionally, the valance of Fe was determined as 3+ in the pigment grain, whereas 2+ in the reaction layer and the glaze, respectively. Therefore, it was concluded that the colour change is occurring as result of the valence variation of Fe, the formation of Zn_0.48Fe_0.79Cr_1.32O₄ compound and the outward diffusion of Fe into the glaze.     

产业化生产优质系列云母珠光颜料

常州涂料化工研究院以优质白云母为原料,开发出净化分级、云母活化、四氯化钛控制水解包膜 和连续化煅烧等技术,在100t/a工业装置上生产出系列优质云母珠光颜料,质量接近国外名牌产品水平,产品 性价比高,80％以上用来出口。     

薯莨色素的提取和性能研究

本文研究从薯莨中提取天然色素的方法，并对色素的稳定性，抗氧化性及抑菌性进行了试验．实验证明，该色素是一种多功能的天然色素．测定色素的主要成份是单宁．     

提高以草浆为主的低定量涂布纸不透明度的研究

在选择好对不透明度有利的优质功能颜料及其最佳添加量范围的研究基础上,又从性能价格比方面进一步探讨颜料的搭配对不透明度的影响,结果得出了由高岭土、UFGCC和优质功能颜料组成的三元体系优越于由高岭土和优质功能颜料组成的双元体系的结论,其中UFGCC添加量为20份左右,煅烧土20－30份,钛白添加量为7．5份左右。     

温光处理对节瓜幼苗光合作用的影响

试验以江心4号节瓜为试材,研究了温光处理对节瓜苗期叶片光合作用的影响,结果表明:低温导致了叶片光合色素含量明显降低,且随处理时间的延长而下降;低温下强光促进光合色素含量降低。低温处理下叶绿素a/叶绿素b比值明显提高,且随处理时间的延长而上升。低温下叶绿体类囊体解体、排列无序、联结断开,基粒片层肿涨,淀粉粒、质体球增加,淀粉粒体积变大;持续低温强光导致了叶绿体膜的解体;常温弱光下类囊体排列混乱、质体球增加。低温下叶片Fv/Fm明显下降,低温下强光明显降低Fv/Fm。低温、强光都会造成Fv/Fo的下降,而且低温和强光存在互作。低温下乙醇酸氧化酶活性上升,低温下强光增强了乙醇酸氧化酶活性,低温下较强的光呼吸有利于防御低温光抑制造成的伤害。     

美国地锦色素提取剂的选择及其稳定性影响因素的研究

通过实验确定美国地锦色素的提取剂的选择，并测定各种因素对该色素稳定性的影响。结果表明：30％酸性乙醇是美国地锦色素的较好提取剂。实验数据显示：光照、温度、酸碱、氧化还原剂、食品添加剂以及金属离子对该色素的稳定性影响都不大。该色素是稳定性好的食品添加剂。     

吸附树脂AB-8精制栀子黄色素的工艺研究

采用大孔吸附树脂柱层析柱分离天然产物栀子黄，以AB-8大孔吸附树脂为研究对象，探讨了树脂对栀子黄的静态吸附率和吸附流速、洗脱流速、流脱方式对树脂吸附的影响，得到AB-8树脂吸附栀子黄较为合适的工艺．以AB-8树脂为吸附剂，采用超声波提取法获得的色素粗提液为吸附液，吸附流速1．5mL／min，并采用梯度洗脱法对柱上色素进行了洗脱，洗脱流速2．5mL／min．精制后色素溶液A238／A440从2．12降到0．64，精制色素得率89．27％，色素色价达到221．24．     

pH值对天然绿色棉颜色的影响

主要研究了pH值对天然绿色棉颜色的影响变化规律,并用测色配色系统测试处理后织物的明度变化△L值、色调变化△a、△b值,结果表明绿棉在酸性条件下明度增大,红黄色光增加;在碱性条件下明度降低,红蓝色光增加.采用化学方法检验绿棉色素的主要官能团,并结合绿棉织物的颜色变化规律证明绿棉色素中含有黄酮类化合物.     

TB/TiO2复合白色颜料的微观形态与组成特征研究

介绍了对TB/TiO2复合白色颜料的微观形态与组成特征进行的研究.TB/TiO2复合白色颜料由固体包核物颗粒TB和其表面包覆的结晶TiO2所组成,TiO2在TB表面形成均匀的包覆层.TB/TiO2复合白色颜料因此具有与钛白粉类似的颜料性能.     

钴-钛系列随角异色功能颜料的制备及性能研究

采用具有干涉色的云母钛作为基质材料,通过湿化学法制备随角异色功能颜料.用XRD、多角度色度仪、X-Rite MA-86Ⅱ5角度分光光度仪对颜料进行分析表征.考察实验条件对颜料随角异色效果的影响,分析了角度变化对颜料明度和颜色变化趋势的影响.结果表明,在具有干涉色的云母钛表面包覆氧化钴膜,能够制得变色效果较好的随角异色颜料,制备此种颜料的最佳反应条件是:反应温度70～80℃,pH9.5～10.5之间,加料速度2～3滴/min,煅烧温度900℃,煅烧时间60min,改变云母钛的干涉色可以制得多种颜色的随角异色颜料,随着观察角度的增加,颜料的明度增加,颜料呈现3种颜色变化.