L360QS/316L不锈钢复合钢管焊接工艺和性能研究

介绍了?准355.6 mm×(10+3) mm规格L360QS+316L不锈钢复合钢管的新型焊接工艺,即首先采用TIG焊在复合钢管管端进行堆焊预处理,然后再采用氩气保护TIG焊进行对焊操作。为评价环焊缝的性能,焊后对其焊接接头进行了拉伸试验、冲击试验、硬度测试、晶间腐蚀及应力腐蚀试验。试验结果表明,采用该工艺焊接的L360QS+316L不锈钢复合钢管环焊缝焊接接头性能良好,且具备耐晶间腐蚀和应力腐蚀性能;堆焊层起到了很好的隔离作用,保证了焊缝的质量。     

非结构化P2P覆盖网络通信协议研究

针对各种基于流言机制的通信协议在构造非结构化P2P覆盖网络中,其适用范围缺乏广泛的实证问题,提出了一个通用的协议框架——基于流言机制的节点采样服务,以执行高效和可靠的节点采样服务。在这种协议框架下通过实验分析了8种通信协议的差异。实验表明,采用不同的通信协议,所构造的非结构化P2P覆盖网络就表现出多种不同的行为特性,为构造非结构化P2P覆盖网络中选取通信协议提供了重要的参考依据。     

钢板-超薄UHPC-TPO组合桥面静力和疲劳试验研究

为探明钢-超薄UHPC （Ultra-high Performance Concrete）-TPO （Thin Polymer Overlay）组合桥面基本力学性能,设计5块钢-超薄UHPC-TPO组合板进行抗弯静力试验及疲劳试验。静力试验结果表明：在负弯矩作用下,UHPC层的开裂强度为22.1～24.3MPa;TPO先于UHPC进入非线性阶段。疲劳试验结果表明：若将此方案应用于虎门大桥悬索桥,则UHPC层在设计应力幅下疲劳开裂寿命可达925.7万次,TPO层将不会因疲劳而开裂;疲劳加载后,组合板剩余弯拉强度均值为26.9kN,整体抗弯刚度与静力试验结果相比仅下降13%。研究表明,钢桥面-超薄UHPC-TPO组合桥面具有优良的抗弯拉性能。     

基于VxLAN组网的云数据中心互联方案

从VxLAN技术实现现状、云数据中心底层承载网络现状等维度,多视角地对基于VxLAN组网的云数据中心之间的互联互通方案进行了研究与测试验证,并分析了各种方案的优缺点及适用场景。通过本文的研究,以期为运营商的云数据中心发展提供相关技术参考。     

overlay SDN实现异构兼容的关键技术

云计算的规模化发展对数据中心网络提出了新的挑战,要求应用SDN技术对数据中心网络进行虚拟化,以满足多租户环境下灵活调整的动态网络需求,overlay SDN是实现数据中心网络虚拟化的核心技术。研究了overlay SDN网络虚拟化的关键技术,提出了商业overlay SDN存在的兼容性问题,分析了overlay SDN 实现异构兼容的主要方法,并提出了基于开源和白盒交换机实现异构兼容的overlay SDN架构。     

Observations of the spallation modes in an overlay coating and the corresponding thermal barrier coating system

Abstract

The oxidation dynamics of an overlay coating and the corresponding thermal barrier coating system are presented. The particular systems examined are composed of a nickel-based superalloy with an air plasma-sprayed NiCrAlY bond coat and the thermal barrier coating system consists of air plasmasprayed yttria stabilized zirconia layer. Failure can occur in these systems by crack propagation within the ceramic outer layer at the interface with the bond coat. Defects, such as microcracks and pores, are common in plasma-sprayed coatings and within the thermally grown oxide scales. These can act as initiation sites for cracks. The subsequent growth of these cracks can lead to loss of the outer protective materials. Considerable information is available by microscopic examination of sections through test specimens that have been held at temperature for varying amounts of time. By careful sample preparation it is possible to monitor the development of the oxide scale formed during high temperature testing and the sites of failure. Identification of the initiation sites and growth of cracks is important in understanding the spallation process. In this study, scanning electron microscopy is used to provide evidence of the processes involved in the two systems. A comparison of the two coating systems reveals the effect the outer ceramic layer has on the oxide scale growth, and the spallation processes crucial to the understanding of the failure mechanisms of these coating systems.     

新城疫病毒自然宿主细胞膜受体的鉴定

目的鉴定鸡源副黏病毒F48E9株的自然宿主细胞膜受体。方法采用蛋白膜提取试剂盒提取鸡胚成纤维细胞膜蛋白,用改进的间接ELISA方法检测鸡源副黏病毒分离株F48E9与细胞膜的结合活性,利用病毒铺覆蛋白印迹技术(VOPBA)鉴定新城疫病毒(NDV)的自然宿主细胞膜受体。结果NDV与鸡胚成纤维细胞膜有很强的结合力,在转印鸡胚成纤维细胞膜蛋白的PVDF膜上有几条明显的疑似受体条带,相对分子质量介于35000～60000之间。结论初步鉴定了NDV自然宿主细胞膜的受体,其疑似受体蛋白的性质及在新城疫病毒致病中的作用尚有待进一步研究。     

钢桥面铺装防水粘结材料性能评价方法与力学作用分析

总结了防水粘结材料在钢桥面铺装中的作用,阐述了钢桥面铺装防水粘结材料常用的试验方法,介绍了钢桥面铺装防水材料的力学作用,为钢桥面铺装结构和材料的设计与施工提供了技术指导。     

SA387 Grade11 CL.2与SB409 N08810的焊接

通过自过渡降比法和合理的焊接工艺措施,验证了Cr-Mo钢与镍合金材料的直接对接焊的可行性,为工程应用提供了理论依据。     

基于代理的协同计算模型研究与实现

针对大规模多数据源实时协同计算结构模型的可扩展进行研究.分析目前协同计算体系结构的缺点,提出一个三层的协同计算结构模型.然后给出该模型中最重要的覆盖层的构建方法,即以自治域为单位征集或部署代理节点,并在每个自治域选出一个或多个代理作为核心代理,核心代理节点采用点对点的Pastry协议互联构成自治域间的覆盖网.实验结果表明,该模型具有良好的可扩展性.