高速钢强韧化深冷处理研究

研究了深冷处理对高速钢力学性能及高速钢刀具使用寿命的影响．实验结果表明，深冷处理可明显改善高速钢的红硬性、强度和韧性，刀具的使用寿命显著提高．     

高速钢强韧性深冷处理研究

研究了深冷处理对高速钢力学性能及高速钢刀具使用寿命的影响。实验结果表明，深冷处理可明显改善高速钢的红硬性、强度的韧性，刀具的使用寿命显著提高。     

高速钢深冷处理及其机理研究

研究了深冷处理对Ｗ１８Ｃｒ４Ｖ和Ｗ６Ｍｏ５Ｃｒ４Ｖ２两种高速钢微观组织结构和力学性能的影响。实验结果表明，深冷处理使高速钢刀具使用寿命显著提高，深冷处理过程中马氏体的分解及超微细碳化物的析出是高速钢力学性能得以改善的重要原因之一。     

Ca及时效处理对ZA102镁合金组织和力学性能的影响

利用SEM、X射线衍射、拉伸性能测试、显微硬度测试等手段研究了合金元素Ca及时效处理对ZA102镁合金铸态组织和力学性能的影响。结果表明1%的Ca对合金铸态组织的改善效果最为明显,τ相(Mg32(Al,Zn)49)由断续网状变为细小的块状且分布弥散,ε相(MgZn)变得更加细小,同时形成了分布弥散的Al2Ca强化相,此时合金的抗拉强度和拉伸性能达到最大值,抗拉强度达到174 MPa、伸长率达到6%、硬度达到86 HV。如果Ca的含量超过1%合金的晶粒开始变大并且合金元素有偏聚的趋势,并导致其力学性能降低。对铸态试验合金在360℃×10 h+180℃(T6)下进行时效处理,结果表明经过T6处理后能进一步改善合金的组织和力学性能。     

激冷薄带Al-Sr中间合金的变质效果研究

采用单辊甩带方法制备了Al-10%Sr激冷薄带中间合金.利用DSC、SEM、XRD等测试手段研究了激冷薄带Al-10%Sr中间合金对A356铝硅合金的变质效果.结果表明:Al-10%Sr激冷薄带中间合金的相组成中出现了单质Sr,并在衍射角0°～14°间出现了非晶的漫散峰.采用Al-10%Sr激冷薄带中间合金对A356合金变质处理后,其共晶开始温度由576℃降低到571.3℃,共晶潜热则增加了39.2 J/g;变质后的A356合金经T6处理后,其共晶硅多呈点状(低倍)或球状、卵状(高倍),基体组织中树枝状α(Al)固溶体组织明显增多,初晶Si相消失;电导率(20.07 S/μm)比A356合金提高了14.9%,变质效果良好.     

不锈钢在稀硫酸介质中的腐蚀磨损行为SCIEI

测定了300系不锈钢在稀硫酸介质中磨损率、摩擦系数及钝化膜破坏后的修复时间,还观察了磨痕形貌。实验表明高合金化的不锈钢磨蚀失重大于一般的304不锈钢。本文结果预示着发展耐磨蚀合金的道路不同于耐蚀合金。     

合金元素对铸造奥氏体不锈钢组织及耐蚀性能的影响

本文研究了Cr、Mo等合金元素对铸造奥氏体不锈钢析出相的成份、结构及形貌的影响,测定七种铸造奥氏体不锈钢在20％H_2SO_4及含有不同Cl~-浓度的20％H_2SO_4中的均匀腐蚀速度、稳定电位和极化曲线,实验结果表明:合金元素Cr、Mo促进了针状σ相析出,合金元素     

Effects of supersonic fine particle bombarding on thermal cyclic failure lifetime of thermal barrier coating

Thermal barrier coating ( TBC) consisting of a NiCoCrAlY bond coat ( BC) and a ZrO2-8 wt. % Y2O3 topcoat ( TC) was fabricated on the nickel-base superalloy by air plasma spray ( APS) . The BC was treated by supersonic fine particle bombarding ( SFPB) . Thermal cyclic failure and residual stress in thermally grown oxide ( TGO) scale were studied by SEM with EDS and ruby fluorescence spectroscopy ( RFS) . As shown in the results,after treated by SFPB,thickening of TGO was relatively slow,which reduced the level of growth stress. The TBC with SFPB treatment was still remained well undergoing 350 times of thermal cycle. However,after thermal cycle with the same times,the separation of TC was observed in TBC without SFPB treatment. The residual stress analysis by RFS showed that the residual stress of SFPB-treated TBC increased with the increasing number of thermal cycle. The residual stress of conventional TBC reached a value of 650 MPa at 350 times of cycle and that of SFPB-treated TBC only reached 532 MPa at 400 times of cycle. The BC with SFPB treatment after 400 times of cycle was analyzed by RFS,the high stress value was not observed in local thickened region of TGO. Thermal cycling resistance of TBC can be improved by the SFPB technology.     

高速钢低温渗碳及复合处理工艺研究

研究了Ｗ１８Ｃｒ４Ｖ高速钢在５５０℃下的低温固体渗碳工艺及低温渗碳＋深冷复合处理工艺。结果表明，与淬火回火态高速钢相比，经低温渗碳及复合工艺处理后硬度，红硬性得到改善，刀具的耐用度明显提高。     

组织遗传对粒状贝氏体钢力学性能的影响