钼酸盐及其复配盐对水中钆的缓蚀作用

钆是优良的室温磁致冷工质 ,但在载冷剂水中存在腐蚀现象。本文通过挂片试验 ,研究了钼酸盐及其与硅酸盐、锌盐的复合配方在对水中磁制冷工质钆的缓蚀作用。研究结果表明 ,钼酸盐及其复合配方对工质钆有良好的缓蚀作用 ,并通过正交实验找到了复合配方的最佳配方。     

Research Advance on Magnetocaloric Effect of La-Fe-M（AI，Si） Compounds

Recent research progress on magnetocaloric effect of La-Fe-M (M=Al,Si) compounds was presented. La-Fe-M(M=A1,Si) compounds of high Fe content are excellent soft magnetic materials with NaZn13 structure. The Curie temperature of the compounds can be increased by substituting small amount of Co for Si, Al. The La(Fe1_yCoy)xSi13-x compoundswith an appropriate ratio of Co and Si can produce giant magnetocaloric effect comparable to that for Gd5Si2Ge2 at room temperature. The La(FexSi1-x)13 doped with H can also produce giant magnetocaloric effect at room temperature,which is much greater than that for Gd. For La(FexSi1-x)13 compounds with low Si or high Si contents. The nature of phase transition near Curie temperature induced by temperature and magnetic field was described in detail.     

单、三相中小型隐极同步发电机电磁设计的计算机程序介绍

1 简述隐极同步发电机的电磁设计是一项比较繁琐的计算。我们在计算机上采用BASIC语言编制了一套同步发电机电磁设计程序。本程序适用于单、三相隐极转场式同步发电机计算,功率为1KW—250KW的2、4、6、8……极,50H 和60H 的电机。定子绕组为双层60°或120°相带绕组,也适于单层同心式绕组,整数或分数槽都可用。转子绕组     

La0．7Ce0．3（Fel-xCox）11．44Si1．56（x=0．04、0．06、0．08）合金的结构与磁热效应

通过X射线衍射仪研究了1300℃退火1h后的La0．7Ce0．3（Fel-xCox）11．44Si1．56（x=0．04、0．06、0．08）合金的相结构。采用振动样品磁强计研究了合金的磁性能。结果表明，合金主相具有NaZn13型结构，含有少量α-Fe和LaFeSi杂相；x=0．04、0．06和0．08时，合金的居里温度Tc分别为230．8、261、288．9K，在1．1T的外磁场变化下，等温磁熵变｜ΔSM｜分别为2．44、1．86和1．55J／（kg·K）。     

Microstructure,tensile properties and compressive creep resistance of Mg-(5-8.5)%Sn-2%La alloys

The microstructure,tensile properties and compressive creep resistance of permanent-mould cast Mg-(5-8.5)%Sn-2%La (mass fraction) alloys were investigated.The results show that Mg-(5-8.5)%Sn-2%La alloys are all composed ofα-Mg phase, Mg_2Sn and Mg-La-Sn compounds.Compared with those of Mg-5%Sn binary alloy,the grain size and the content of Mg_2Sn compound in Mg-5%Sn-2%La alloy are decreased.With the increase of Sn content in Mg-(5-8.5)%Sn-2%La alloys,the content of Mg_2Sn compound increases,while that of...     

Mg-5Sn-xGd合金的铸态显微组织

研究了Mg-5Sn-xGd(x=0,0.5,1.0,2.0,4.0,6.0)合金的铸态显微组织.试验表明,随着Gd含量的增加,合金晶界上连续分布的片层状α-Mg Mg2Sn共晶组织逐渐减少并变得不连续.当Gd含量达到4%时,合金中共晶组织基本消失.在共晶组织减少的同时,合金晶界附近同时生成一种细小的不规则形状的Mg-Sn-Gd三元稀土相,随Gd含量的增加,该稀土相的数量增加,DSC分析结果显示该稀土相在582 ℃时可能发生相变.Gd的加入对合金中Sn元素的分布有显著影响.     

Nd改性AZ91合金的显微组织和力学性能

稀土Nd加入AZ91合金中可生成Al-Nd相并细化合金晶粒.Nd含量影响合金中Al-Nd相的种类、形貌、大小和分布,从而改变合金的室温拉伸力学性能.当Nd含量为1.0%时,合金中析出的Al-Nd相主要为针状的Al11Nd3相;当Nd含量为到2.0%时,针状的Al11Nd3相已经比较少,块状的Al2Nd相为主要的Al-Nd相;当Nd含量为到2.5%时,析出的Al-Nd相几乎全部为块状的Al2Nd相.Nd含量由1.0%增加到2.0%时,合金的伸长率、抗拉强度和屈服强度分别增加 33%、14%和4%;Nd含量由1.0%增加到2.5%时,上述三者分别增加44%、18%和6%.     

新型防护电磁波信息泄漏材料的研究进展

对新型防护电磁波信息泄漏材料的研究现状进行了综述.重点介绍和评述了非晶材料、纳米材料、手性材料和稀土材料在电磁波信息泄漏防护材料中的研究进展.     

AZ91+0~2.0%La铸造镁合金的组织和力学性能

利用SEM和XRD等方法研究不同La添加量的AZ91+xLa(x=0%,0.3%,0.5%,0.7%,1.0%,1.5%,2.0%)(质量分数,下同)镁合金的铸态显微组织和相组成,并测试和分析合金的室温力学性能.结果表明:AZ91合金中加入0.3%～2.0%的La后,合金的晶界和枝晶界析出Al11La3化合物,其形态随La含量的增加从针状向片状过渡,同时β-Mg17Al12相的体积分数及尺寸随La加入量的增加而减小.此外,La的加入可明显细化AZ91合金的显微组织,其最佳加入量为1.0%～1.5%.稀土La的加入可以明显改善AZ91合金的力学性能,其原因与稀土细化组织、改变β-Mg17Al12相的体积分数及尺寸、弥散强化等有关.在本试验研究的合金中,AZ91+1.5%La合金力学性能最好,其铸态合金的抗拉强度和断裂延伸率分别达到226 MPa和7.5%.     