搅拌法制备漂珠增强铝基复合材料的熔体分层与控制

采用液态搅拌法制备漂珠增强铝基复合材料过程中, 当颗粒含量较低时, 熔体容易分层。为了了解颗粒在铝熔体中的分布情况, 对试样的不同位置进行扫描电镜分析。结果表明, 在试样的底部有明显的纯铝层,而漂珠在上部的铝熔体中分布均匀。漂珠向熔体上部移动的速度主要取决于漂珠颗粒与铝熔体的密度差、颗粒直径、颗粒体积分数及铝熔体粘度。原料确定后, 只能通过增加铝熔体的粘度或减少浇铸过程的时间来减少纯铝层的产生。因此, 可以采用下浇铸式方法和快速冷却装置, 使颗粒来不及向上运动而被凝固在铝熔体中, 形成漂珠在铝熔体中均匀分布的复合材料。      

Effect of strain rate on microstructure and mechanical properties of a Mg-9Li-2Zn alloy sheet

1 IntroductionMagnesium-Lithiumalloyis thelightest alloy at present .Its properties are as follows :high specific ri-Fig .1 The phase diagramof Mg-Li alloygidity ,i mpact ductility , machining,electromagnetic shielding,and shockproof etc .[1 ,2].In additionit can be reclai med,reused,and don't pollute environment ,thus it is called a“green”alloyfor 21st century .Magnesiumis a hexagonal closepacked metal and has poorformability . However ,it is well knownthat the addition of lithi-umto mag…     

Study on sintering technique of NiFe_2O_4/SiCp used as matrix of inert anodes in aluminium electrolysis

1IntroductionResearch demonstratedthat NiFe2O4spinel used as matrix of inert anode was appropriatein aluminiumelectrolysis[1,2].NiFe2O4spinel is with chemical inertness and electrochemical stability,but alsois in pos-session of high temperature resistance,high stress and hardness[3].But then its electro conductibility,toughness and resistance to thermal shock can't meet a demand when it is used in aluminiumelectrolysis,resultedin the anode cracked and the purity of the electrolytic Al bastar…     

超轻Mg-Li-Al系变形镁合金冷轧及热处理后的组织和性能

研究了超轻变形镁合金Mg (5% ~ 22%)Li 2%Al冷轧性能,热处理特性以及机械性能。合金的密度为1.206~1.642g/cm3。在室温条件下β相合金(16%和22%(质量分数)Li)具有非常良好的延展性,压下极限可达到90%以上。研究了Mg Li Al 系变形镁合金铸锭经不同温度、时间均匀化退火后的组织性能。对均匀化后的合金锭进行了冷轧,轧后板材在不同温度下进行了退火,研究其再结晶行为及组织性能。结果表明, Mg 9Li 2Al 2Ca合金在573K温度均匀化退火12h后合金铸锭组织均匀,有利于冷轧开坯变形;而对于Mg 9Li 2Al 合金, 523K 温度均匀化退火24h后组织较好。冷轧合金板材在573K温度退火1h 可发生完全再结晶,生成细小均匀的等轴晶组织。     

Effect of additive V_2O_5 on sintering mechanism and properties of inert anodes of NiFe_2O_4 spinel

1 IntroductionThe idea of usinginert anodes (also called non-consumable or oxygen-producing anodes) in aluminumproductionis as old as the Hall-Heroult process ,dating backto one of theinventors ,Charles Martin Hall .Aninert anode is intended to replace a consumable carbon anode ,the cell reactionis Al2O3+3/2C 2Al +3/2CO2(1)The requirements for lowenergy consumption,lowproductioninvest ment andreducingthe emission ofgreenhouse gas speed the research for inert anodes in aluminumproduction. …     

MnO2对镍铁尖晶石惰性阳极材料性能的影响

尝试在合成镍铁尖晶石过程中添加一定量MnO2 以提高试样的性能。采用高温固相反应法制备掺杂MnO2 的镍铁尖晶石惰性阳极材料,研究了掺杂MnO2 对制品密度,收缩率和抗腐蚀性的影响。研究结果表明MnO2 能够促进烧结,提高制品的密度,并能够改善制品的抗腐蚀能力,添加 1% MnO2 后试样的腐蚀率为纯尖晶石试样的1/7。试样经 X射线衍射分析发现,添加 MnO2 后无新相出现,MnO2 与 NiFe2O4形成固熔体,Mn4 离子取代了部分 Fe3 离子,材料仍是镍铁尖晶石结构。     

SiC晶须增强NiFe2O4基惰性阳极材料烧结工艺研究

为改善铝电解惰性阳极用NiFe2O4 尖晶石材料存在的不足,首次采用固态合成法制备了NiFe2O4/SiCw 复合材料。利用扫描电子显微镜观察显微组织,由X射线衍射分析物相,研究了烧结温度和保温时间对体积密度、气孔率和微观结构的影响,通过DTA分析证明了低于1200℃时NiFe2O4 与SiC的热力学相容性,试验结果表明,当烧结温度为1180℃时试样微观结构最为均匀致密,当烧结时间>6h时密度和气孔率的变化趋于稳定, NiFe2O4/SiCw 复合材料最佳的烧结工艺为1180℃×6h。     

镍铁钨三元合金的电镀研究

在镍铁合金镀液中加入钨酸盐，研究镍铁钨三元合金电镀工艺及镀层性能、结构。结果表明，钨能有效地强化镍铁合金的机械性能而不改变其基本结构。     

溶胶—凝胶法制备TiO2薄膜的工艺研究

以钛酸四丁酯为原料,乙醇为溶剂,采用溶胶—凝胶法制备TiO₂薄膜,利用旋转粘度计、光学显微镜和扫描电子显微镜研究了浓度、加水量、TiO₂溶胶黏度、水解抑制剂种类及用量对镀膜效果的影响。在此基础上,采用浸渍—提拉法经过三次镀膜在载玻片上成功制备出均匀、致密的TiO₂薄膜。     

合成工艺对NiFe2O4基惰性阳极性能的影响

为得到制备NiFe2O4基惰性阳极的最佳条件,利用正交实验法确定合适的工艺条件.考虑了影响惰性阳极制品的4个主要因素,每个因数又设计3个水平,通过正交实验极差分析研究了各因素对制品气孔率的影响,并确定了影响因素的主次.实验结果表明:对烧结后试样气孔率影响最大的因素是烧结温度,其次是纳米粉含量,再次是成型压力,最后是烧结时间;添加合适量的纳米粉,提高烧结温度和保温时间,增大成型压力等都有利于降低样品的气孔率.最佳工艺条件为:纳米粉质量分数20%,成型压力200MPa,烧结温度