不同基体炭C/C复合材料的摩擦磨损性能

以炭纤维针刺毡为预制体,采用化学气相沉积法(CVI)和结合液相浸渍树脂或沥青法制备了热解炭为粗糙层与光滑层结构的准三维C/C复合材料,并研究了这些材料在0.6 MPa的模拟刹车压力下的摩擦磨损性能与磨损机理.研究表明:基体炭为粗糙层热解炭与树脂炭的C/C复合材料摩擦表面能形成较厚且连续的自润滑摩擦膜,摩擦稳定性最好,摩擦因数适中,氧化磨损小,磨损机理主要为膜的部分脱落、氧化磨损与相对较小的磨粒磨损;基体炭为光滑层热解炭与树脂炭或沥青炭的C/C复合材料摩擦表面形成的摩擦膜较薄且不连续,摩擦稳定性差,摩擦磨损较大,磨损机制主要为膜的部分脱落、磨粒磨损与更严重的氧化磨损;随着密度的升高,C/C复合材料摩擦稳定性增加,摩擦因数增加,磨损降低;基体炭为单一沥青炭的C/C复合材料,由于没有热解炭对纤维的保护,纤维断裂多,线性磨损尤其大,磨损机理主要为大量的磨粒磨损与氧化磨损.     

Electrochemical characteristic of chemical-mechanical polishing of copper with oxide passive film

1　INTRODUCTIONThankstoitslowresistivityandhighelectromi grationresistance ,copperappearstobeaverypromisingsubstituteforaluminumininterconnec tions[1] .However ,copperisverydifficulttopattern ,andonlychemical mechanicalpolishing (CMP)tech nologycanresolvethisproblem[2 ] .CMPwasinitiallyinvestigatedandopenedoutfrom 1980soverseas[3] ,anditisthebestandonlyglobalplanarizationtech nologyatpresent ,butkeepsholdofbusinesssecretsallthetime .Fayolleetal[2 ] researchedCMPprocessofcopperwhereFe(…     

熔铸TiAl合金热等静压处理的研究

通过测定弯曲性能、观察金相组织和断口形貌，探讨了热等静压处理（ＨＩＰ）对改善ＴｉＡｌ合金弯曲延性的作用机理。研究表明，经１２００℃，１５０ＭＰａ，２ｈ热等静压处理后，合金的弯曲延性得到显著的改善。弯曲延性改善的作用机理主要为：适当的热等静压处理消除了铸态合金内原有的铸造缺陷；合金中形成了由均匀分布的γ等轴细晶粒和α２＋γ两相片层晶粒构成的金相组织，这种组织能延缓裂纹萌生而承受较大的塑性变形。     

粉末冶金TiAl合金排气门的研制

利用元素粉末冶金方法制备了TiAl合金排气阀。为提高排气门杆部的致密度、均匀度 ,设计了特有的径向热压工艺 ,并从理论上分析了与该工艺相关的压坯密度、致密化和应力变化规律。制备出高径比为 10 .7,密度为 3.79g/cm3 的粉末冶金TiAl合金汽车发动机排气门     

全层状TiAl合金层片生长及其影响因素

利用光学显微镜(OM)和TEM，研究了全层状TiAl合金的层片间距的影响因素及与各因素的关系。实验结果表明，全层状TiAl合金的层片间距与冷却速度和合金中铝含量有关，层片间距与冷却速度呈反比关系，并随着合金中铝含量的增加而增加。同时，以层片生长的台阶机制为基础，推导出了全层状TiAl合金在连续冷却过程中层片间距的数学表达式，推导结果与实验结果相符。     

粉末冶金法制备云母/羟基磷灰石玻璃陶瓷

为了获得良好的可加工性和生物活性,采用粉末冶金法制备了云母/羟基磷灰石玻璃陶瓷.随着烧结温度的提高,材料的力学性能有所增加.在1100℃下、保温1.5 h可以获得材料的最佳力学性能,其相对密度、抗弯强度和断裂韧性分别为95%、124 MPa和2.1 MPa·m1/2.随着温度的提高,烧结过程中玻璃相的扩散速度加快并填充到剩余的孔隙中,使得材料的相对密度增加,从而提高了材料的抗弯强度.断裂韧性的提高来源于材料中高长径比的云母晶体相互交错的微观结构.     

Microstructure and properties of cutting magnesium-brass containing no lead

1 INTRODUCTIONLead-brass has excellent cutting ability , me-chanical and physical properties and is one of themost widely used copper alloys . The occupationratio of brass tube to all kinds of tubes reaches90 % in developed countries . The cutting lead-brass is a dual-phase brass and fine lead particlesdistribute dispersivelyin grains and on grain boun-ries . Theleadin wasted brass can easily beleachedand dissolvedinto soil .If the wasted lead-brass isburned in air ,the lead will become p…     

Phase transition of lithiated-spinel Li2Mn2O4 at high temperature

1 Introduction Lithium manganese oxides are the most attractive cathode materials for rechargeable lithium-ion batteries because of their low-cost and less toxicity when compared with either cobaltates or nickelates[1?3]. Among these oxides, the spinel-fr…     

Calculation of cooling rate of amorphous aluminum alloy melt-spun ribbons

Based on the heat transfer theory and liquid solidification theory, the heat transfer during the rapid solidification process of amorphous ribbons prepared by melt spinning was approximately modeled by one-dimensional heat conduction equation. Besides, integration with the temperature gradient, the relationship between the ribbon thickness and solidification time was derived according to the boundary conditions of ribbon-copper wheel. A simply theoretical model was obtained to calculate the cooling rates of aluminum amorphous ribbons. According to the above theoretical model, the critical cooling rate of aluminum amorphous ribbons by melt spinning is above 10^6 K/s, which proves that the aluminum based alloys belong to the marginal glass forming ability of alloys. The calculated results are in good agreement with other estimated values reported previously.     

粘结剂组成对粘结剂和喂料热性能的影响

研究制备了PW，BO，OP3大系列10种组成的粘结剂及相应10种W-Ni-Fe粉末与粘结剂的混合料。并采用热失重-差热分析(TGA-DTA)分析了粘结剂和喂料的热性能。研究结果表明，粘结剂组成对粘结剂和喂料的热性能如熔点、热分解温度和热分解曲线有很大的影响。通过此变化可以更为准确地确定不同粘结剂组成的喂料中的粘结剂脱除工艺和脱除方式。