Chromium-promoted preparation of forsterite refractory materials from ferronickel slag by microwave sintering

The chromium-promoted preparation of forsterite refractory materials from ferronickel slag was investigated by microwave sintering of the slag with the additions of sintered magnesia and 0–10 wt% chromium oxide (Cr₂O₃). The thermodynamic calculations revealed that the addition of Cr₂O₃ can promote the formations of spinel and liquid phase and maintain high content of forsterite below 1500 °C. The experimental results showed that there existed a stronger promoting effect of Cr₂O₃ additive on the properties of refractory materials in the microwave field than that in conventional sintering. It was attributed to the preferential formation and growth of spinel with stronger microwave absorption than other phases (e.g., enstatite), the existence of more forsterite, and the enhanced densification in association with the presence of more liquid phase at the same temperature. By microwave sintering of the mixture of ferronickel slag, 25 wt% sintered magnesia, and 4 wt% Cr₂O₃ at 1350 °C for 20 min, a superior refractory material with refractoriness of 1801 °C, thermal shock resistance of 6 times, bulk density of 2.97 g/cm³, apparent porosity of 1.4%, and compressive strength of 197 MPa was obtained. Compared with that prepared by conventional sintering at 1350 °C for 2 h, the refractoriness and thermal shock resistance were increased by 175 °C and 100%, respectively. The present study provided a novel method for preparing high-quality refractory materials from ferronickel slag and relevant industrial wastes.     

Theoretical investigation of intrinsic point defects and the oxygen migration behavior in rare earth hafnates

In this work, the composition-dependent point defect types and formation energies of RE₂Hf₂O₇ (RE = La, Ce, Pr, Nd, Pm, Sm, Eu and Gd) as well as the oxygen diffusion behavior are systematically investigated by first-principles calculations. The possible defect reactions and dominant defect complexes under stoichiometric and non-stoichiometric conditions are revealed. It is found that O Frenkel pairs are the predominant defect in stoichiometric pyrochlore hafnates. Hf-RE cation anti-site defects, accompanied by RE vacancies and/or oxygen interstitials, are stable in the non-stoichiometric case of HfO₂ excess. On the other hand, RE-Hf anti-site defects together with oxygen vacancies and/or RE interstitials are preferable in the case of RE₂O₃ excess. The energy barriers for the migration along the V_O48f - V_O48f pathway of pyrochlore hafnates were calculated to be between 0.81 eV and 0.89 eV. Based on these results, a defect engineering strategy is proposed and the pyrochlore hafnates investigated here are predicted to exhibit potential oxygen ionic conductivity.     

涂装车间节水方案企划与实施

某涂装车间在现有节水措施的基础上，通过企划与实施一系列新的技术及精益管理措施，如，磷化出槽喷淋工艺优化、纯水制水率提升、空调冷凝水回用率提升、中水深度处理回用、用水分级管理等，将新鲜水用量从 15. 2 L/m2降至 11. 3 L/m2，达到涂装行业清洁生产评价指标体系（ 2016版）中的 I级标准 12 L/m²要求，处于国内领先水平。     

Achieving fabrication of highly transparent Y2O3 ceramics via air pre-sintering by deionization treatment of suspension

An easy albeit quite effective deionization suspension treatment was adopted to alleviate the detrimental effects related to the hydrolysis of Y₂O₃ in an aqueous medium. Fabrication of highly transparent Y₂O₃ ceramics with a fine grain size via air pre-sintering and post–hot isostatic pressing (HIP) treatment without using any sintering additive was achieved using the treated suspensions. The hydrolysis issue of Y₂O₃ powder in an aqueous medium was effectively alleviated by using deionization treatment, and a well-dispersed suspension with a low concentration of dissolved Y³⁺ species was obtained. The dispersed suspensions were consolidated by the centrifugal casting method, and the green bodies derived from the suspension of 35.0 vol% solid loading showed an improved homogeneity with a relative density of 52.1%. Fully dense Y₂O₃ transparent ceramic with high transparency was obtained by pre-sintering consolidated green compacts at a low temperature of 1400°C for 16 h in air followed by a post-HIP treatment at 1550°C for 2 h under 200 MPa pressure. The sample had a fine average grain size of 690 nm. The in-line transmittance of the sample reached 83.3% and 81.8% at 1100 nm and 800 nm, respectively, very close to the theoretical values of Y₂O₃.     

An Injectable Hydrogel for Simultaneous Photothermal Therapy and Photodynamic Therapy with Ultrahigh Efficiency Based on Carbon Dots and Modified Cellulose Nanocrystals

The convenience of injectable hydrogels that can provide high loading of diverse phototherapy agents and further long-time retention at the tumor site has attracted tremendous interest in simultaneous photothermal and photodynamic cancer therapies. However, to incorporate the phototherapy agents into hydrogels, complex modifications are generally unavoidable. Moreover, these phototherapy agents usually suffer from low efficiency and work at different irradiation wavelengths outside the near infrared windows. Hence, a method for the fabrication of an injectable hydrogel for simultaneous photothermal therapy and photodynamic therapy, through the Schiff-base reaction between amido modified carbon dots (NCDs) and aldehyde modified cellulose nanocrystals is proposed. The NCDs act as both phototherapy agents and crosslinkers to form hydrogels. Significantly, the NCDs demonstrate an extremely high photothermal conversion efficiency of 77.6% which is among the highest levels for photothermal agents and a high singlet quantum yield of 0.37 under a single 660 nm light-emitting diode irradiation. The hydrogels are examined through in vitro and in vivo animal experiments which show nontoxic and effectively tumor inhibition. Thus, the strategy of direct reaction of phototherapy agents and the matrix not only provides new strategies for injectable hydrogel fabrication but paves a new road for advanced tumor treatment.     

Suppressed Lattice Disorder for Large Emission Enhancement and Structural Robustness in Hybrid Lead Iodide Perovskite Discovered by High-Pressure Isotope Effect

The soft nature of organic–inorganic halide perovskites renders their lattice particularly tunable to external stimuli such as pressure, undoubtedly offering an effective way to modify their structure for extraordinary optoelectronic properties. Here, using the methylammonium lead iodide as a representative exploratory platform, it is observed that the pressure-driven lattice disorder can be significantly suppressed via hydrogen isotope effect, which is crucial for better optical and mechanical properties previously unattainable. By a comprehensive in situ neutron/synchrotron-based analysis and optical characterizations, a remarkable photoluminescence (PL) enhancement by threefold is convinced in deuterated CD₃ND₃PbI₃, which also shows much greater structural robustness with retainable PL after high peak-pressure compression–decompression cycle. With the first-principles calculations, an atomic level understanding of the strong correlation among the organic sublattice and lead iodide octahedral framework and structural photonics is proposed, where the less dynamic CD₃ND₃⁺ cations are vital to maintain the long-range crystalline order through steric and Coulombic interactions. These results also show that CD₃ND₃PbI₃-based solar cell has comparable photovoltaic performance as CH₃NH₃PbI₃-based device but exhibits considerably slower degradation behavior, thus representing a paradigm by suggesting isotope-functionalized perovskite materials for better materials-by-design and more stable photovoltaic application.