35CrNi2MoVE钢零件的开裂分析

通过裂纹断口宏观形貌、显微组织、裂纹断口显微形貌、显微裂纹特征和残余应力等角度对裂纹产生原因进行分析.结果表明:零件裂纹为淬火裂纹.淬火温度过高,孔边缘残余应力集中导致发生沿晶开裂,针对零件开裂原因,提出严格控制热处理工艺参数、改进零件结构设计、热处理后进行质量检查的建议.     

Synthesis of succinic acid-based polyamide through direct solid-state polymerization method: Avoiding cyclization of succinic acid

Succinic acid is an important synthetic monomer but it is difficult to use it as a precursor for synthesizing high molecular weight polyamide, due to its tendency to perform intra-cyclization reaction at high temperature. In order to solve this problem, in this paper, the direct solid-state polymerization (DSSP) method with the initial reactant, nylon salt which was composed of 1, 5-diaminopentane, succinic acid, and terephthalic acid, was applied to synthesize the bio-based copolyamide PA 5T/54. In comparison with the conventional melting polymerization method, the DSSP method can prevent the cyclization reaction of succinic acid effectively due to the lower reacting temperature as well as the restriction effect of the nylon salt. As a result, the product fabricated by DSSP method has higher molecular weight and much lighter color from red to white. Therefore, the DSSP method is advantageous for the synthesis of the polymers or copolymers composed of the succinic acid as the monomer. Furthermore, the polymerization mechanism proposed in this work can serve as a guidance for the design of the molecular structure and control of the polymerization process.     

高熵形状记忆合金的研究进展

高熵形状记忆合金是在等原子比NiTi合金的基础上,结合高熵合金的概念,逐渐发展起来的一种新型高温形状记忆合金。近年来,已开发出了综合性能优异的(TiZrHf)50(NiCoCu)50系和(TiZrHf)50(NiCuPd)50系高熵形状记忆合金,引起了广泛的关注和研究兴趣。本文从物相组成、微观组织、马氏体相变行为、形状记忆效应和超弹性等角度出发,综述了高熵形状记忆合金的研究进展,并对高熵形状记忆合金未来的研究重点进行了展望。     

Effect of laser power density on the electrochromic properties of WO3 films obtained by pulsed laser deposition

Pulsed laser deposition (PLD) was used to prepare tungsten trioxide (WO₃) films on ITO substrates with a varying laser power density of 4.0–5.5 W/cm². XPS indicated that when the laser power density decreased, the peak positions of the W 4f and O 1s orbits shifted slightly to low energy due to the difference in oxygen vacancies. As the laser power density decreased, W⁶⁺ gradually replaced the lattice position of O^2?, increasing oxygen vacancies in the lattice. The transmittance modulated values (ΔT) were over 44% at 830 nm, indicating strong absorption by the WO₃ thin films in the near-infrared ray. The switching time of the WO₃ thin films between bleached states and coloured states decreased as the laser power density increased due to the amorphous structure, morphology, and lower oxygen deficiency at a high power density. The high ΔT and very fast switching time of t_b (1.09 s) and t_c (6.01 s) demonstrated the excellent electrochromic (EC) properties of the WO₃ films prepared by PLD.     

装配式混凝土木混合结构体系简述

上海电气研混凝土(如皋)建筑科技有限公司——建筑工业化智能创新基地项目,采用装配式混凝土木混合结构,该结构是一种新型的建筑结构体系.其承重的部分采用混凝土结构且可在工厂进行预制,围护结构采用木材制成,可在满足使用等功能的同时降低造价、减轻自重、保护环境,具有很大的发展潜力.     

城市街道峡谷单侧自然通风研究进展

自然通风广泛存在于城市之中，了解城市自然通风建筑室内环境质量现状及存在的问题，是改善城市建筑室内环境质量的基础. 通过文献整理，首先研究城市街道峡谷中单侧自然通风的驱动因素，其次从建筑几何特征、通风能力、污染率、颗粒物浓度以及街谷设施等方面综述单侧自然通风的相关研究，最后提出建议. 研究表明，合理的展弦比、更好的城市布局以及精心的街谷设施设计能够最大限度地利用单侧自然通风，提升城市街道峡谷的室内环境品质.     

基于稠密变形场能量优化的非刚性在线体积重建方法

针对动态非刚性在线重建存在的重建漂移问题,提出了一种基于单个RGB-D传感器的稠密变形场在线融合策略,实现了对非刚性几何形状的动态重建.通过局部平滑和输入约束处理,将空间的最优变形转换为非线性正则变分优化问题,并使用数据并行闪存优化策略,以摄像机捕获速率,实现对非刚性场景的在线跟踪重建.通过实验表明,本文方法实现了对非刚性场景的鲁棒跟踪,减少了在线重建过程中的漂移现象,适用于快速运动和缺乏几何特征的场景重建.     

Dealloying corrosion of anodic and nanometric Mg41Nd5 in solid solution-treated Mg-3Nd-1Li-0.2Zn alloy

The microstructure and chemical compositions of the solid solution-treated Mg-3Nd-1Li-0.2Zn alloy were characterized using optical microscope,scanning electron microscope(SEM),transmission electron microscope(TEM),electron probe micro-analyzer(EPMA)and X-ray photoelectron spectroscopy(XPS).The corrosion behaviour of the alloy was investigated via electrochemical polarization,electrochemical impedance spectroscopy(EIS),hydrogen evolution test and scanning Kelvin probe(SKP).The results showed that the microstructure of the as-extruded Mg-3Nd-1Li-0.2Zn alloy contained α-Mg matrix and nanometric second phase Mg41 Nd5.The grain size of the alloy increased significantly with the increase in the heat-treatment duration,whereas the volume fraction of the second phase decreased after the solid solution treatment.The surface film was composed of oxides(Nd2O3,MgO,Li2O and ZnO)and carbonates(MgCO3 and Li2CO3),in addition to Nd.The as-extruded alloy exhibited the best corrosion resistance after an initial soaking of 10 min,whereas the alloy with 4h-solution-treatment possessed the lowest corrosion rate after a longer immersion(1 h).This can be attributed to the formation of Nd-containing oxide film on the alloys and a dense corrosion product layer.The dealloying corrosion of the second phase was related to the anodic Mg41Nd5 with a more negative Volta potential relative to α-Mg phase.The preferential corrosion of Mg41Nd5 is proven by in-situ observation and SEM.The solid solution treatment of Mg-3Nd-1Li-0.2Zn alloy led to a shift in corrosion type from pitting corrosion to uniform corrosion under long-term exposure.     

工艺参数对动态流量控制法挤压弯管应力的影响

采用有限元模拟和实验研究了挤压钛合金弯曲管件。通过实验验证了工件的形状和尺寸精度,并通过有限元模拟分析了工艺参数对挤出过程中变形体的平均压应力分布情况和挤出弯管件的曲率半径的影响规律。结果表明:有限元模拟中,弯管件的曲率半径误差为6.03%,弯管直径误差为3.82%;在靠近定径带处,平均压应力呈非均匀分布;在焊合腔内,靠近细分流孔区域的平均压应力小于靠近粗分流孔区域的平均压应力,平均压应力的大小顺序在通过粗、细分流孔前后相反;在模具结构固定不变时,弯管件的曲率半径随挤压速度的减小而增大,不随挤压温度的变化而变化。