Optical properties and conductivity of PEDOT:PSS films treated by polyethylenimine solution for organic solar cells

We report on conductivity and optical property of three different types of poly(3,4-ethylenedioxythiophene):polystyrene sulfonate (PEDOT:PSS) films [pristine PH1000 film (PH1000-p), with 5 wt.% ethylene glycol additive (PH1000-EG) and with sulfuric acid post-treatment (PH1000-SA)] before and after polyethylenimine (PEI) treatment. The PEI is found to decrease the conductivity of all the PEDOT:PSS films. The processing solvent of 2-methoxyethanol is found to significantly enhance the conductivity of PH1000-p from 1.1 up to 744 S/cm while the processing solvent of isopropanol or water does not change the conductivity of PH1000-p much. As for the optical properties, the PEI treatment slightly changes the transmittance and reflectance of PH1000-p and PH1000-EG films, while the PEI leads to an substantial increase of the absorptance in the spectral region of 400–1100 nm of the PH1000-SA films. Though the optical property and conductivity of the three different types of PEDOT:PSS films vary with the PEI treatment, the treated PEDOT:PSS films exhibit similar low work function. We demonstrate solar cells with a simple device structure of glass/low-WF PEDOT:PSS/P3HT:ICBA/high-WF PEDOT:PSS cells that exhibit good performance with open-circuit voltage of 0.82 V and fill factor up to 0.62 under 100 mW/cm² white light illumination.     

Influence of Bridgman solidification on microstructures and magnetic behaviors of a non-equiatomic FeCoNiAlSi high-entropy alloy

The non-equiatomic FeCoNiAlSi alloy is prepared by the Bridgman solidification (BS) technique at different withdrawal velocities (V = 30, 100, and 200 μm/s). Various characterization techniques have been used to study the microstructure and crystal orientation. The morphological evolutions accompanying the crystal growth of the alloy prepared at different withdrawal velocities are nearly the same, from equiaxed grains to columnar crystals. The transition of coercivity is closely related to the local microstructure, while the saturation magnetization changes little at different sites. The coercivity can be significantly reduced from the equiaxed grain area to the columnar crystal area when the applied magnetic field direction is parallel to the crystal growth direction, no matter what is the withdrawal velocity. In addition, the alloy possesses magnetic anisotropy when the applied magnetic field is in different directions.     

Impact sensitivities of energetic materials: Exploring the limitations of a model based only on structural formulas

Using a comprehensive set of drop weight impact test data (h₅₀) newly compiled from literature for 308 materials, a recent approach to predict impact sensitivities of nitro compounds is generalized to most explosive substances of interest. Compared to previous ones, this procedure is more thoroughly validated and exhibits a good predictive value. Furthermore, it yields new insight into the physical mechanisms involved, explaining for instance the unexpected desensitization of some oxygen-deficient triazoles upon nitration.     

Optical Properties of One-dimensional Three-component Photonic Band Gap Structure

1　IntroductionMaterialswithPhotonicBandGaps (PBG’s)havebeenwidelystudiedboththeoreticallyandex perimentallyinthepastfew years[1～ 4] .Theexis tenceofgaps,which prohibitthepropagationofelectromagnetic (EM )wavesinacertainrangeoffrequencies,canhavesignificantimpactsbothinsci enceandtechnology .Manypracticalapplicationsofthesestructureshavebeensuggestedanddemon strated ,suchasPhotonicCrystal (PC)microcavi ties[5] ,infraredPC[6] ,PClens[7] ,suppressingspontaneousemission ,manipulatinglight…     

储层应力敏感性影响因素研究

全面分析储层应力敏感性产生的机理认为，外部因素的改变会引起储层产生应力敏感性．而储层岩石物性等内部因素对应力敏感性的强弱起决定性作用。室内岩心应力敏感性评价时．仪器与设备的精度、加载与卸载方式、实验用流体类型以及各种人为因素等都会对评价结果产生影响，其中岩心密封套在高压、高温条件下的密闭性会对实验结果产生较大影响。所以储层应力敏感性不应该从孔隙度和渗透率的高低进行简单评价，中、高渗储层和低渗储层在生产过程也都可能表现出较强的应力敏感性现象。     

Effects of genotype and treatment on the antioxidant activity of sweet potato in Taiwan

Six genotypes of sweet potato commercially available in Taiwan, including TNG57, TNG66, TNG68, TYY1, RP and WP, were used as samples in this study of the effects of steaming and kneading with pre-steaming treatments on the antioxidant components and antioxidant properties of methanolic extracts. Steam treatment increased the total phenols contents of all genotypes (2–13 times), flavonoids content of RP (1.3 times) and anthocyanins contents of RP and WP (5–6 times). Steam treatment also increased the reducing power and scavenging DPPH radical effect of sweet potato flours. For the methanolic extracts of steamed and kneaded flours, reducing powers were 0.02–1.70 at 5.0 mg ml⁻¹ and the scavenging effects on DPPH radicals were 19–92% at 2.5 mg ml⁻¹. Both showed the order of RP > WP > TYY1 and TNG66 > TNG57 and TNG68. However, the chelating effect of the six genotypes at 1.0 mg ml⁻¹ ranged from 50% to 73%. Contents of total phenols, flavonoids, and anthocyanins of sweet potato flours were significantly positively correlated with the reducing power and scavenging DPPH radical effects. After steaming and kneading treatments, RP showed the highest increase in the contents of total phenols, flavonoids and anthocyanins among the six genotypes studied.     

Effect of Stoichiometry on Properties of Rare-Earth-Based Hydrogen Storage Alloy for Nickel-Metal Hydride Secondary Battery

Effect of stoichiometry on microstructures, electrochemical properties and PCT characteristics of the alloys MI(Ni0.71Co0.15-Al0.06Mn0.08)x (MI=Lanthanum-rich Michmetal, x=4.6~5.2) have been investigated. The lattice constants a, c, and cellvolumes of non-stoichiometric alloys are bigger than those of the stoichiometric alloy. With the increasing stoichiometry x,the value of a decreases, and the value of c and cell volume increases except for those of the stoichiometric alloy; the plateaupressure of PCT curve, discharge capacity and cycling stability all increase. The alloy with x=5.2 shows the highest dischargecapacity and the best cycling stability among the studied alloys.     

Transport of a surface-applied corrosion inhibitor in cement paste and concrete

Surface-applied corrosion inhibitors are a kind of repair material and usually contain an aminoalcohol and a component forming a salt with the aminoalcohol. According to the manufacturers, this type of inhibitor penetrates very rapidly into concrete; however, the transport mechanisms have not been sufficiently investigated so far. The major part of the study therefore focused on the transport of the ingredients of an inhibitor in cement paste and concrete, which contained an aminoalcohol and a phosphorous compound. It has been shown that the latter forms an insoluble calcium salt in the environment of cement and precipitates quantitatively. It is thus unable to penetrate from the outside into the alkaline concrete zone and cannot develop its inhibiting effect there. The aminoalcohol, on the other hand, is not bound by cement, but remains largely dissolved in the pore liquid, thus providing optimal conditions for high mobility. The analysis of the transport mechanisms involved has revealed that diffusion in the dissolved state is by far the most efficient transport mechanism. While basically the transport of the aminoalcohol via the gaseous phase is possible, it does play an inferior role only. Surprisingly, the substance had hardly been absorbed by concrete by capillary suction, but at first remained close to the concrete surface.     

氟塑料—石墨板式换热器在高温强腐蚀换热工况中的应用

通过氟塑料－石墨板式换热器在化纤生产中高温强腐蚀换热工况中的实际应用，并与常规换热器的使用情况的对比分析，阐述了这种新型换热设备的特点。