Transport of a surface-applied corrosion inhibitor in cement paste and concrete

Surface-applied corrosion inhibitors are a kind of repair material and usually contain an aminoalcohol and a component forming a salt with the aminoalcohol. According to the manufacturers, this type of inhibitor penetrates very rapidly into concrete; however, the transport mechanisms have not been sufficiently investigated so far. The major part of the study therefore focused on the transport of the ingredients of an inhibitor in cement paste and concrete, which contained an aminoalcohol and a phosphorous compound. It has been shown that the latter forms an insoluble calcium salt in the environment of cement and precipitates quantitatively. It is thus unable to penetrate from the outside into the alkaline concrete zone and cannot develop its inhibiting effect there. The aminoalcohol, on the other hand, is not bound by cement, but remains largely dissolved in the pore liquid, thus providing optimal conditions for high mobility. The analysis of the transport mechanisms involved has revealed that diffusion in the dissolved state is by far the most efficient transport mechanism. While basically the transport of the aminoalcohol via the gaseous phase is possible, it does play an inferior role only. Surprisingly, the substance had hardly been absorbed by concrete by capillary suction, but at first remained close to the concrete surface.     

氟塑料—石墨板式换热器在高温强腐蚀换热工况中的应用

通过氟塑料－石墨板式换热器在化纤生产中高温强腐蚀换热工况中的实际应用，并与常规换热器的使用情况的对比分析，阐述了这种新型换热设备的特点。     

Nondestructive evaluation of the characteristics of degraded materials using backward radiated ultrasound

The frequency dependency of Rayleigh surface wave is investigated indirectly by measuring the angular dependency of the backward radiation of the incident ultrasonic wave in two kinds of degraded specimens by scuffing or corrosion. Then, the frequency dependency is compared with the residual stress distribution or the corrosion-fatigue characteristics for the scuffed or corroded specimens, respectively. The width of the backward radiation profile increases with the increase of the variation in residual stress distribution for the scuffed specimens. In the corroded specimens, the profile width decreases with the increase of the effective aging layer thickness and is inversely proportional to the exponent, m, in the Paris’ law that can predict the crack size increase due to fatigue. The result observed in this study demonstrates high potential of backward radiated ultrasound as a tool for nondestructive evaluation of subsurface gradient of material degradation generated by scuffing or corrosion.     

长距离油、气、水混输管道内壁流动腐蚀的研究进展

就近几十年来，多相流管线的流动腐蚀（CO2腐蚀，H2S腐蚀，腐蚀/冲蚀协同作用），腐蚀/冲蚀数学模型和设计准则，腐蚀检测，腐蚀防护与控制技术等方面的研究进展进行了综述。指出了当前研究中所存在的一些问题，就多相流的研究方向提出了相应的建议。     

Indicators for inspection and maintenance planning of concrete structures

Based on an idea introduced by Benjamin and Cornell (1970. Probability, statistics and decision for civil engineers. New York: McGaw Hill) and previous works by the authors it is demonstrated how condition indicators may be formulated for the general purpose of quality control and for assessment and inspection planning in particular. The formulation facilitates quality control based on sampling of indirect information about the condition of the considered components. This allows for a Bayesian formulation of the indicators whereby the experience and expertise of the inspection personnel may be fully utilized and consistently updated as frequentistic information is collected. The approach is illustrated on an example considering a concrete structure subject to corrosion. It is shown how half-cell potential measurements may be utilized to update the probability of excessive repair after 50 years. Furthermore in the same example it is shown how the concept of condition indicators might be applied to develop a cost optimal maintenance strategy composed of preventive and corrective repair measures.     

Influence of inhibitor addition on the corrosion protection performance of sol–gel coatings on AA2024

Sol–gel films are actively investigated during the last decade as possible candidates for environmentally friendly pre-treatments. However, the important drawback in this case is the lack of active corrosion protection and self-healing ability.     

High-efficiency finishing process for metal mold by large-area electron beam irradiation

A new finishing process for metal molds by large-area electron beam (EB) irradiation is proposed in this study. In the large-area EB irradiation equipment used here, an EB with high-energy density is irradiated without focusing the beam, and so the EB with a maximum diameter of 60 mm can be used for melting or evaporating metal surface instantly. Experimental results show that the surface roughness decreases from 6 μmRz to less than 1 μmRz in just a few minutes under proper machining conditions. The corrosion resistance of metal mold surface also could be greatly improved by large-area EB irradiation. Furthermore, the surface roughness of tilting surface close to 90° could be well improved. Therefore, large-area EB irradiation method has a possibility to become a high-efficiency finishing process for metal molds.     

Corrosion protection of iron by polypyrrole coatings electrosynthesised from a surfactant solution

This work is a study of the electropolymerisation of pyrrole onto iron electrodes in the presence of sodium bis(2-ethylhexyl) sulfosuccinate in a wide pH interval. The characterisation of the films was done using electrochemical techniques, SEM/EDX and IR spectroscopy. We show that it is possible to synthesise homogeneous, adherent and very compact films in the pH range between 7 and 12 under potentiodynamic, galvanostatic and potentiostatic conditions without substrate dissolution. The effects of various parameters on electrodeposition were investigated. The new procedure for the electrochemical synthesis of polypyrrole results in improved anticorrosion properties. The inhibition is proposed to be due to the sum of a repulsion of chloride ions because AOT remains entrapped in the polymer matrix and the presence of the iron oxide. Advantages of the use of surfactants in the electropolymerisation solution are discussed.     

Determination of instantaneous corrosion rates and runoff rates of copper from naturally patinated copper during continuous rain events

Instantaneous corrosion rates of naturally patinated copper of varying age (16 months, 138 and 145 years) have been determined during continuous rain events in the laboratory with electrochemical impedance spectroscopy using a two-electrode cell. The two-electrode cell was found to yield the same information in bulk rainwater as a conventional three-electrode cell.Relatively constant corrosion rates, between 0.2 and 0.6 μm/y, were determined for samples having a two-layer structure with an inner brownish layer of cuprous oxide and an outer greenish layer of basic copper salts (138, 145 years). Samples with cuprous oxide as the dominating phase of the patina (16 months) showed higher and somewhat increasing corrosion rates during a rain event (from 0.6 to 1.2 μm/y). During a continuous rain event, corrosion rates were found to be approximately 10 (brownish patina) and 25 times (greenish patina) lower than corresponding instantaneous runoff rates. The first flush phenomena of the runoff process, with an increased concentration during first flush and a relatively constant concentration during steady state, was indirectly seen as an increase in solution conductivity during the first rain volume followed by relative constant value. The contribution of the concentration in the first flush to the total annual runoff rate was significant for panels having a greenish layer (138, 145 years) whereas it was negligible for panels having a brownish layer (16 months).