Improving Wear Resistance of the Ni-base Thermal Spray-Welding Coating Using Rare Earths

ＩｍｐｒｏｖｉｎｇＷｅａｒＲｅｓｉｓｔａｎｃｅｏｆｔｈｅＮｉｂａｓｅＴｈｅｒｍａｌＳｐｒａｙＷｅｌｄｉｎｇＣｏａｔｉｎｇＵｓｉｎｇＲａｒｅＥａｒｔｈｓＺｈａｉＧｕａｎｇｊｉｅ（翟光杰）（ＩｎｓｔｉｔｕｔｅｏｆＰｈｙｓｉｃｓ，ＡｃａｄｅｍｉｃａＳｉ...     

激光熔覆Ni基SiC合金涂层组织与性能的研究

利用5kWCO2连续波激光器在16Mn钢基材表面对含20%(体积比)SiC陶瓷粉末的镍基自熔性合金粉末进行激光熔覆得到Ni基SiC合金涂层(NiSiC)。研究了合金涂层的组织形貌及相结构,并用单纯的镍基合金涂层(Ni60)进行了显微硬度及滑动磨损性能的对比试验。结果表明,NiSiC合金涂层由γ枝晶及其间的共晶组织组成,主要组成相为γ-Ni,γ-(Ni,Fe)固溶体和(Cr,Fe)7C3,Cr23C6及(Cr,Si)3Ni3Si等化合物。添加SiC的镍基合金涂层NiSiC比单纯的镍基合金涂层Ni60具有较高的硬度和耐磨性。     

Interfacial reactions in In-Sn/Ni couples and phase equilibria of the In-Sn-Ni system

The In-Sn-Ni alloys of various compositions were prepared and annealed at 160°C and 240°C. No ternary compounds were found; however, most of the binary compounds had extensive ternary solubility. There was a continuous solid solution between the Ni₃Sn phase and Ni₃In phase. The Sn-In/Ni couples, made of Sn-In alloys with various compositions, were reacted at 160°C and 240°C and formed only one compound for all the Sn-In alloys/Ni couples reacted up to 8 h. At 240°C, Ni₂₈In₇₂ phase formed in the couples made with pure indium, In-10at.%Sn and In-11at.%Sn alloys, while Ni₃Sn₄ phase formed in the couples made of alloys with compositions varied from pure Sn to In-12at.%Sn. At 160°C, except in the In/Ni couple, Ni₃Sn₄ formed by interfacial reaction.     

Ni catalyst promotion of a Cis-selective Pd catalyst for canola oil hydrogenation

A Ni catalyst was added to a cis-selective Pd catalyst in an attempt to further improve the Pd catalyst's cis-selectivity and activity for canola oil hydrogenation. The system was tested under reaction conditions known to be suitable for cis-selective hydrogenation with the Pd catalyst (50 ppm Pd, 70 °C, and 5.2 MPa). Although inactive on its own under these conditions, the addition of 100 ppm Ni increased the hydrogenation activity (from 2.12 to 2.49 10⁻² min⁻¹). Further addition of Ni up to 1000 ppm resulted in no further improvements in activity. The trans isomer contents of the oils hydrogenated with Pd and the Pd/Ni systems were similar. The level of conjugated dienes decreased rapidly during hydrogenation with both Pd alone and with the Pd/Ni combination and no changes in conjugation were detected in the presence of the Ni catalyst alone. The increased activity of the Pd/Ni system over Pd alone was attributed to adsorption of catalyst poisons from the oil by Ni.     

电沉积Ni-W合金镀层的X射线光电子能谱分析

采用X射线光电子能谱（XPS）对电沉积Ni-W合金镀层表面膜进行了分析。研究结果表明，Ni-W合金镀层表面存在一层薄的氧化膜，而钨的氧化作用远大于镍，Ni-W合金镀层中W含量的提高对耐蚀性起决定作用。     

高可靠镀Ni／Au工艺及其在微波PTFE电路上的应用

介绍了高可靠电镀Ｎｉ／Ａｕ工艺在ＰＴＦＥ微波印制电路上的应用，并分析了氨基磺酸盐镀软镍和亚硫酸盐镀软金工艺的影响因素及提高Ｎｉ／Ａｕ镀层之间附着力的措施。通过实验及应用证明了与直接镀金工艺相比，在软基材ＰＴＦＥ敷铜箔板上镀Ｎｉ／Ａｕ工艺能大大提高微波电路的可焊性，高温稳定性和长期可靠性，并且用其所制作的微波器件的高频性能也优于直接镀金工业。     

空气中烧成的镍导体及其应用

将空气中烧成的镍导体用于散热制冷片制作工艺中，可降低成本，提高合格率。通过实验得到的最佳值为：镍导体中４号玻璃（ＳｉＯ２＞３０，Ｂ２Ｏ３＞１０，ＰｂＯ＜５５，ＴｉＯ２少许）的含量４．５％，化学镀镍时间５０ｍｉｎ，方阻４７．５ｍΩ／□，附着力８．１Ｎ／ｍｍ２。     

Hydriding and Dehydriding Characteristics of Mechanically Alloyed LaMg_(17) Ni Composite Material

Magnesiumandmagnesiumalloyshavebeenin vestigatedashydrogenstoragematerialsforseveralde cadesbecausefarmorehydrogenbyweightcanbestoredinthemthaninmostoftheothercurrentlyknownhydrogenstoragealloys .Moreover ,thehighnaturalabundanceofMg ,itslightmassandenviron mentalcompatibilitypotentiallymakemagnesiumoneofthemostprospectivecandidatesforfuturehydrogenstoragematerials .Unfortunately ,thepracticalappli cationofMganditsalloyshasbeenlimitedonlytocertainstoragedevicebecauseoftheirpoorhydriding dehydr…     

Characterization of two-phase nickel aluminides produced by pressure-assisted combustion synthesis

Two-phase (B2+L1₂) nickel aluminide intermetallic compounds were synthesized by the pressure-assisted volume combustion synthesis (CS). The production and characterization of the samples containing NiAl+Ni₃Al were investigated. Aluminum (99% pure, 15 μm) and carbonyl nickel (99.8 pure, 4-7 μm) powders were used. The production of intermetallic compound was carried out at 1050 °C under 150 MPa uniaxial pressure in open air atmosphere in an electrical resistance furnace for 60 min. The formation temperature of intermetallic compound was determined by differential scanning calorimeter (DSC) analysis, and exothermic temperature of powder mixture was determined as 653 °C. The characterization of samples was confirmed by optical microscope, SEM and XRD analysis. It was observed that the structure of compound has very low porosity and the formation of NiAl was completed successfully. The relative density of test materials measured according to Archimedes’ principle was 98.04%. The microhardness of test materials was about 351 HVN₁.     

Ni对球墨铸铁热处理的影响

采用电子探针，图象分析仪、差质变分析仪和Ｘ射线衍仪定量研究了Ｎｉ在球铁中的分布和Ｎｉ铸态球铁组成相比例奥氏体中含碳量以及贝氏体转变ＴＴＴ曲线线的影响，结果表明，Ｎｉ在球铁中呈连续负偏析，其加入可以影响球铁组成上比例，并使粤氏体中含碳量和贝氏体转变孕育期期增加。