Structural regulation and polishing performance of dendritic mesoporous silica (D-mSiO2) supported with samarium-doped cerium oxide composites

Ceria (CeO₂) particles are prevalent polishing abrasive materials. Trivalent lanthanide ions are the popular category of dopants for enriched surface defects and thus improved physicochemical properties, since they are highly compatible with CeO₂ lattices. Herein, a series of dendritic-like mesoporous silica (D-mSiO₂)-supported samarium (Sm)-doped CeO₂ nanocrystals were synthesized via a facile chemical precipitation method. The relation of the structural characteristics and chemical mechanical polishing (CMP) performances were investigated to explore the effect of Sm-doping amounts on the D-mSiO₂/Sm_xCe_1?xO_2?δ (x = 0–1) composite abrasives. The involved low-modulus D-mSiO₂ cores aimed to eliminate surface scratch and damage, resulting from the optimized contact behavior between abrasives and surfaces. The trivalent cerium (Ce³⁺) and oxygen vacancy (V_O) at CeO₂ surfaces were expected to be reactive sites for the material removal process over SiO₂ films. The optimal oxide-CMP performances in terms of removal efficiency and surface quality were achieved by the 40% Sm-doped composite abrasives. It might be attributed to the high Ce³⁺ and V_O concentrations and the enhancement of tribochemical reactivity between CeO₂SiO₂ interfaces. Furthermore, the relationship between the surface chemistry, polishing performance as well as the actual role in oxide-CMP of the D-mSiO₂/Sm_xCe_1?xO_2?δ abrasives were also discussed.     

Fabrication and properties of diatomite ceramics with hierarchical pores based on direct stereolithography

Porous diatomite ceramics with hierarchical pores and high apparent porosity (50.29–56%) were successfully fabricated via direct stereolithography. The pre-ball-milling time, dispersant type and dispersant concentration were systematically investigated to prepare diatomite pastes with high solid loading, low viscosity and a self-supporting effect. The results showed that a pre-ball-milling time of 24 h was more suitable to prepare diatomite pastes with high solid loading, and Span80 at 2 wt% was the optimal dispersant to obtain 40 vol% diatomite paste with a low viscosity and a self-supporting effect. To restrain the formation of defects, a heating rate as low as 0.2 °C/min was allowed to control the pyrolysis rate in the multistage debinding process. At sintering temperatures ranging from 900 °C to 1000 °C, porous diatomite ceramics exhibited a typical bimodal porosity, high apparent porosity and great flexural strength.     

Processing and properties of Nextel™ 720 fiber reinforced alumina-zirconia ceramic matrix composites

The continuous Nextel? 720 fiber-reinforced zirconia/alumina ceramic matrix composites (CMCs) were prepared by slurry infiltration process and precursor infiltration pyrolysis (PIP) process. The introduction of submicron zirconia powders into the aqueous slurry was optimized to offer comprehensively good sintering activity, high thermal resistance and good mechanical properties for the CMCs. Meanwhile, the zirconia and alumina preceramic polymers were used to strengthen the porous ceramic matrix through the PIP process. The final CMC sample achieved a high flexural strength of 200 MPa after one infiltration cycle of alumina preceramic polymer and thermal treatment at 1150 °C for 2 h. The flexural strength retention of the improved CMC sample was 104% and 89% respectively after thermal exposure at 1100 °C and 1200 °C for 24 h.     

Cyclic thermal shock resistance for MgAlON–MgO composites obtained with additions of spent MgO–C brick: Microstructure characteristics,thermal shock parameter and thermal shock mechanism

Thermal shock parameters (R, R''', R'''' and R_st) of MgAlON–MgO composites obtained with additions of spent MgO–C brick were calculated using measured mechanical properties and thermal expansion coefficient, determining their resistance to fracture initiation and crack propagation. The cyclic thermal shock experiments of MgAlON–MgO composites performed from 1398 K to ambient temperature indicate that as number of thermal shock cycle increases, retained strength ratio of MgAlON and MgAlON–4.2 wt%MgO sharply decrease and then keep constant, while that of MgAlON–10.5 wt%MgO and MgAlON–15.7 wt%MgO slowly decrease. The reason for the difference is that MgAlON and MgAlON–4.2 wt%MgO show low value of R''' and R'''', and high value of R and R_st. Moreover, precipitation of impurity containing Fe may play a positive role in improvement of thermal shock resistance of MgAlON–MgO composites. MgAlON?4.2 wt%MgO has the maximum retained strength (55 MPa) even after 5 thermal shock cycles, which is expected to be used in the metallurgical industry.     

Impact of TiO2 nanoparticles and nanowires on corrosion protection performance of chemically bonded phosphate ceramic coatings

The impact of the addition of TiO₂ nanoparticles and nanowires on the morphology, phase characteristics, contact angle, and electrochemical performance of chemically bonded phosphate ceramic coatings (CBPCs) was investigated. The chemical composition and surface morphology of the TiO₂ nanoparticle and nanowire modified with and without (heptadecafluoro-1,1,2,2-tetradecyl) trimethoxysilane were characterized. Results indicated that the hydrophobic –CF₂– and –CF₃ groups were successfully introduced into the TiO₂ nanoparticles and nanowires after modification. Corrosion resistance of CBPCs with TiO₂ was evidently improved compared with that without TiO₂. Such improvement was mainly due to the combined effects of low surface energy materials and micro/nano structures. In addition, CBPCs with TiO₂ nanowires exhibited higher hydrophobicity and corrosion resistance than those with TiO₂ nanoparticles because of the special columnar structure of the nanowires.     

A novel foam glass obtained from solid waste: A sustainable strategy for application in the degradation of an environmental pollutant

Foams glass were obtained from solid waste of flat glass and exhausted alkaline batteries. The physical, chemical, crystalline and morphological properties of the samples were obtained using the Archimedes principle, X-ray diffractometry (XRD), scanning electron microscopy (SEM). The results revealed glass foams with apparent porosities in the range of 55–64% and apparent densities in the range of 0.40–0.79 g cm^?3. The manganese oxide and graphite contained within the cathode of alkaline batteries acted as both oxidizing agents and as foaming agents. The zinc contained in the anode acted as a pore stabilizing agent and the zinc oxide as a semiconductor material. The foam glass that was composed of flat glass with an anode of Zn and ZnO, and a cathode of Mn₂O₃ and Mn₃O₄ (named An8), showed the greatest potential for heterogeneous photocatalysis, with a maximum efficiency of 95.9% after 3 h of treatment of solution containing dye. These results suggest the feasibility of producing foam glass from waste, as well as its potential application in photocatalytic systems, such as in the low-cost treatment of water.     

Ceramics composites from iron ore tailings and blast furnace slag

The search for materials and methods capable of reducing human impacts on the environment is of utmost importance nowadays. This study's primary purpose was to analyze the technical feasibility of ceramic composites production utilizing Fundão Dam's Iron Ore Tailings (IOT), Blast Furnace Slag (BFS) from charcoal, and Foundry Sand (FS) as partial substitutes for the traditional raw materials – sand and clay – for application in building industry materials. The composites were molded in rectangular specimens and fired at temperatures of 900, 950, 1000, 1050, and 1200 °C. The developed materials were analyzed and characterized by X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM), Energy Dispersive Spectroscopy (EDS), Thermogravimetry (TGA), and Differential Thermal Analysis (DTA). The obtained materials had flexural strength modulus of up to 12.19 MPa, water absorption ranging from 2 to 22%, linear shrinkage ranging from 0.02 to 6.50%, and apparent density ranging from 2.03 to 1.63 g/cm³. The study of the internal structure formation process revealed the formation of amorphous structures in the composites. The results demonstrated that these waste materials may be jointly used in construction materials, contributing to the reduction of natural resource extraction, besides enabling their correct disposal, minimizing environmental impacts, and improving the life quality of the surrounding communities.     

High Q×f values of Zn-Ni co-modified LiMg0.9Zn0.1-xNixPO4 microwave dielectric ceramics for 5G/6G LTCC modules

In this work, Zn-Ni co-modified LiMg_0.9Zn_0.1-xNi_xPO₄ (x = 0–0.1) microwave dielectric ceramics were fabricated using a solid state synthesis route. Rietveld refinement of the XRD data revealed that all ceramic samples have formed a single phase with olivine structure. SEM images showed that the samples have a dense microstructure, that agrees with the measured relative density of 97.73 %. Based on the complex chemical bond theory, Raman and infrared reflectance spectra, we postulate that ε_r is mainly affected by the ionic polarizability, lattice and bond energy, while P-O bond plays a decisive role in Q×f and τ_f value. Optimum properties of Q×f ~ 153,500 GHz, ε_r ~ 7.13 and τ_f ~ ?59 ppm/°C were achieved for the composition LiMg_0.9Zn_0.06Ni_0.04PO₄ sintered at 875 ℃ for 2 h. This set of properties makes these ceramics an excellent candidate for LTCC, wave-guide filters and antennas for 5 G/6 G communication applications.     

Fabrication of high-efficiency Yb:Y2O3 laser ceramics without photodarkening

High-efficiency Yb:Y₂O₃ laser ceramics were fabricated using the vacuum-sintering plus hot isostatic pressing (HIP) without sintering additives. High-purity well-dispersed nanocrystalline Yb:Y₂O₃ powder was synthesized using a modified co-precipitation method in-house. The green bodies were first vacuum sintered at a temperature as low as 1430°C and then HIPed at 1450°C. Finally, the samples were air annealed at 800°C for 10 h. Although no sintering aids were used, full density of the samples with excellent optical homogeneity and an inline transmission of 80% at 400 nm could be obtained. Moreover, photodarkening phenomenon was not detected in the ceramics. Preliminary laser experiment with the fabricated ceramics in a two-mirror cavity has demonstrated 32 W continuous-wave (CW) output at ∼1077 nm with an optical-to-optical conversion efficiency of 58.2%. To the best of our knowledge, this is so far the highest CW output power and optical-to-optical conversion efficiency achieved with the Yb³⁺-doped sesquioxide ceramics in a simple two-mirror cavity.     

Effects of sintering temperature and Bi2O3, Y2O3 and MgO co-doping on the dielectric properties of X8R BaTiO3-based ceramics

Bi₂O₃, Y₂O₃ and MgO co-doped BaTiO₃ (BT)-based X8R ceramics were synthesized successfully for the first time. The effects of the sintering temperature and Bi₂O₃, Y₂O₃ and MgO dopants on the dielectric properties were investigated systematically. Bi₂O₃ doping can increase the Curie temperature (T_c), but reduces the overall dielectric permittivity. On the other hand, Y₂O₃ doping is beneficial to the formation of core-shell microstructure and the increase of T_c, whereas MgO can prevent excessive Y₂O₃ from diffusing into grain core, and thereby further contributes to the generation of the core–shell microstructure. The generation of the typical core-shell microstructure was confirmed and investigated in detail by using transmission electron microscopy (TEM). It is argued that the synergistic effects of Bi₂O₃, Y₂O₃ and MgO co-doping in terms of the formation of the core-shell structure and the increase of T_c, can help improve the temperature stability of the dielectric permittivity effectively. Increasing the sintering temperature leads to an increase in the grain size, which in turn leads to an increase in the overall dielectric permittivity due to the grain size effect.