为了减轻汽车重量,提高燃油消耗,研制了高强度钢帘线用线材。然而,开发高强度钢帘线的难点是必须同时获得高强度和良好的塑性。为了解决这一问题,通过分析拉丝过程中钢丝组织和力学性能的变化,研究了拉丝过程中的分层机理,提高了拉丝的塑性。采用1.0%C过共析钢和优化的拉拔工艺,在实验室可获得4400 MPa级钢帘线。     

Corrosion behaviors of carbon steel induced by life activities of Phaeodactylum tricornutum in a marine environment

Microbiologically influenced corrosion induced by bacteria has been studied for many years. Corrosion is known to be sensitive to the presence of microalgae, such as Phaeodactylum tricornutum. However, the life activity of P. tricornutum that influences the general and localized corrosion of carbon steel is not fully understood. The current study uses a combination of immersion tests and electrochemical experiments with a detailed surface characterization to reveal the naturally formed corrosion products with/without the presence of P. tricornutum. The results show that samples suffer from pitting corrosion and the averaged pit depths are approximately 15 μm under a light–dark cycle condition or a 24-h constant light condition. Meanwhile, the corrosion products are mainly comprised of γ-FeOOH and Fe₃O₄ in a constant light condition. However, γ-FeOOH, Fe₃O₄, and FeCO₃ are found in a light–dark cycle. This study proposes the fundamental mechanisms of the effect of P. tricornutum life activities on the corrosion performance of Q235 carbon steel, to fulfill the knowledge gaps of the presence of microalgae inducing the general and pitting corrosion of carbon steel.     

Influence of aluminum phosphate on the tribocorrosion performance of chemically bonded phosphate ceramic coatings

In this study, chemically bonded phosphate ceramic coatings (CBPCCs) with different contents of aluminum phosphate (AP) are prepared on stainless steel (AISI 304L). Differential scanning calorimetry, X-ray diffraction, contact angle test, and a tribocorrosion experiment are carried out to clarify the role of AP in the tribocorrosion performance of CBPCCs. The results show that, with the increase in the AP content, the enthalpy of curing increases because of the greater formation of the bonding phase AlPO₄. Both in static corrosion and in tribocorrosion, the corrosion current density of CBPCCs achieves the lowest value when the weight ratio of AP to polytetrafluoroethylene is about 0.78. Additionally, the influence mechanism of AP on tribocorrosion is clarified. AlPO₄ from the reaction between AP and Al₂O₃ has excellent mechanical properties and can enhance the wear resistance of CBPCCs by reducing the mechanical wear and the increased wear due to corrosion. The alumina particles wrapped by AlPO₄ can form a dense and smooth surface and change the direction of electrolyte propagation, which leads to the increase in the tribocorrosion resistance of CBPCCs.     

Microstructural and mechanical properties assessment of transient liquid phase bonding of CoCuFeMnNi high entropy alloy

The transient liquid phase (TLP) bonding of CoCuFeMnNi high entropy alloy (HEA) was studied. The TLP bonding was performed using AWS BNi-2 interlayer at 1050 °C with the TLP bonding time of 20, 60, 180 and 240 min. The effect of bonding time on the joint microstructure was characterized by SEM and EDS. Microstructural results confirmed that complete isothermal solidification occurred approximately at 240 min of bonding time. For samples bonded at 20, 60 and 180 min, athermal solidification zone was formed in the bonding area which included Cr-rich boride and Mn₃Si intermetallic compound. For all samples, the γ solid solution was formed in the isothermal solidification zone of the bonding zone. To evaluate the effect of TLP bonding time on mechanical properties of joints, the shear strength and micro-hardness of joints were measured. The results indicated a decrement of micro-hardness in the bonding zone and an increment of micro-hardness in the adjacent zone of joints. The minimum and maximum values of shear strength were 100 and 180 MPa for joints with the bonding time of 20 and 240 min, respectively.     

In Vivo Electrophysiology of Peptidergic Neurons in Deep Layers of the Lumbar Spinal Cord after Optogenetic Stimulation of Hypothalamic Paraventricular Oxytocin Neurons in Rats

The spinal ejaculation generator (SEG) is located in the central gray (lamina X) of the rat lumbar spinal cord and plays a pivotal role in the ejaculatory reflex. We recently reported that SEG neurons express the oxytocin receptor and are activated by oxytocin projections from the paraventricular nucleus of hypothalamus (PVH). However, it is unknown whether the SEG responds to oxytocin in vivo. In this study, we analyzed the characteristics of the brain–spinal cord neural circuit that controls male sexual function using a newly developed in vivo electrophysiological technique. Optogenetic stimulation of the PVH of rats expressing channel rhodopsin under the oxytocin receptor promoter increased the spontaneous firing of most lamina X SEG neurons. This is the first demonstration of the in vivo electrical response from the deeper (lamina X) neurons in the spinal cord. Furthermore, we succeeded in the in vivo whole-cell recordings of lamina X neurons. In vivo whole-cell recordings may reveal the features of lamina X SEG neurons, including differences in neurotransmitters and response to stimulation. Taken together, these results suggest that in vivo electrophysiological stimulation can elucidate the neurophysiological response of a variety of spinal neurons during male sexual behavior.     

In vivo Targeting of DNA Vaccines to Dendritic Cells via the Mannose Receptor Induces Long-Lasting Immunity against Melanoma

Herein, we report effective, C-type lectin mannose receptor (MR)-selective, in vivo dendritic cell (DC)-targeting lipid nanoparticles (LNPs) of a novel lipid-containing mannose-mimicking di-shikimoyl- and guanidine head group and two n-hexadecyl hydrophobic tails (DSG). Subcutaneous administration of LNPs of the DSG/p-CMV-GFP complex showed a significant expression of green fluorescence protein in the CD11c⁺ DCs of the neighboring lymph nodes compared to the control LNPs of the BBG/p-CMV-GFP complex. Mannose receptor-facilitated in vivo DC-targeted vaccination (s.c.) with the electrostatic complex of LNPs of DSG/pCMV-MART1 stimulated long-lasting (270 days post B16F10 tumor challenge) antimelanoma immunity under prophylactic conditions. Remarkably, under therapeutic settings, vaccination (s.c.) with LNPs of the DSG/pCMV-MART1 complex significantly delayed melanoma growth and improved the survival of mice with melanoma. These findings demonstrate that this nonviral delivery system offers a resilient and potential approach to deliver DNA vaccines encoding tumor antigens to DCs in vivo with high efficacy.     

氮含量及固溶温度对21-6-9奥氏体不锈钢组织和硬度的影响

为了探讨氮含量及固溶温度对21-6-9不锈钢组织和硬度的影响,分别在950、1000、1050和1100 ℃对3种不同氮含量的热轧态21-6-9不锈钢进行1 h固溶处理,通过光学显微镜观察其组织结构,结合Thermo-Calc热力学计算对试验钢的微观组织进行分析,并对其进行硬度测试。结果表明,0.20%~0.28%N的21-6-9不锈钢热轧后沿轧制方向析出铁素体,且钢中铁素体经950~1100 ℃固溶处理可消除,当N含量达到0.34%时,试验钢中不再出现铁素体。随着固溶处理温度的升高,21-6-9不锈钢的晶粒组织长大,硬度降低。N含量的增加可显著提高固溶态21-6-9不锈钢的硬度,其增加程度随固溶处理温度的升高而减弱。     

Corrosion behavior of T24, T92, VM12, and AISI 304 steels exposed to KCl–NaCl–K2SO4–Na2SO4 salt mixtures

The corrosion mechanisms of T24, T92, VM12, and AISI 304 steels are studied under the influence of NaCl–KCl, NaCl–Na₂SO₄, and KCl–K₂SO₄ salt mixtures in a dry air atmosphere at 650°C for 15 days. NaCl–KCl was the most aggressive deposit and AISI 304 stainless steel exhibited the highest corrosion resistance. There was no relation between the Cr content of the ferritic steels and their corrosion resistance in NaCl–KCl. In contrast, the resistance of high-Cr steels was better when exposed to NaCl–Na₂SO₄ and KCl–K₂SO₄. The high-Cr and the low-Cr steels were more susceptible to NaCl–Na₂SO₄ and to KCl–K₂SO₄, respectively.     

Nacre-Inspired,Liquid Metal-Based Ultrasensitive Electronic Skin by Spatially Regulated Cracking Strategy

The realization of liquid metal-based wearable systems will be a milestone toward high-performance, integrated electronic skin. However, despite the revolutionary progress achieved in many other components of electronic skin, liquid metal-based flexible sensors still suffer from poor sensitivity due to the insufficient resistance change of liquid metal to deformation. Herein, a nacre-inspired architecture composed of a biphasic pattern (liquid metal with Cr/Cu underlayer) as “bricks” and strain-sensitive Ag film as “mortar” is developed, which breaks the long-standing sensitivity bottleneck of liquid metal-based electronic skin. With 2 orders of magnitude of sensitivity amplification while maintaining wide (>85%) working range, for the first time, liquid metal-based strain sensors rival the state-of-art counterparts. This liquid metal composite features spatially regulated cracking behavior. On the one hand, hard Cr cells locally modulate the strain distribution, which avoids premature cut-through cracks and prolongs the defect propagation in the adjacent Ag film. On the other hand, the separated liquid metal cells prevent unfavorable continuous liquid-metal paths and create crack-free regions during strain. Demonstrated in diverse scenarios, the proposed design concept may spark more applications of ultrasensitive liquid metal-based electronic skins, and reveals a pathway for sensor development via crack engineering.     

Direct View on the Origin of High Li+ Transfer Impedance in All-Solid-State Battery

Large interfacial resistance plays a dominant role in the performance of all-solid-state lithium-ion batteries. However, the mechanism of interfacial resistance has been under debate. Here, the Li⁺ transport at the interfacial region is investigated to reveal the origin of the high Li⁺ transfer impedance in a LiCoO₂(LCO)/LiPON/Pt all-solid-state battery. Both an unexpected nanocrystalline layer and a structurally disordered transition layer are discovered to be inherent to the LCO/LiPON interface. Under electrochemical conditions, the nanocrystalline layer with insufficient electrochemical stability leads to the introduction of voids during electrochemical cycles, which is the origin of the high Li⁺ transfer impedance at solid electrolyte-electrode interfaces. In addition, at relatively low temperatures, the oxygen vacancies migration in the transition layer results in the formation of Co₃O₄ nanocrystalline layer with nanovoids, which contributes to the high Li⁺ transfer impedance. This work sheds light on the mechanism for the high interfacial resistance and promotes overcoming the interfacial issues in all-solid-state batteries.