Synthesis of Janus polyaniline–polyelectrolyte complex membrane via in situ confined polymerization

Polyelectrolyte complex (PEC) membranes prepared from poly(styrene sulfonate) (PSS) and poly(diallyldimethylammonium chloride) (PDADMAC) were modified by crossflow polymerization of aniline (ANI). The PEC membranes were used as separators in a two-compartment setup where ANI monomer and ammonium persulfate (APS) oxidant diffused through the membranes to form polyaniline (PANI). APS and ANI having different distributions throughout the membranes, the reaction led to the asymmetric polymerization of PANI on one face of each PEC membrane thus producing Janus membranes. Due to the excess PANI content, the membrane displayed distinct asymmetric electrical conductivities on each face. Interestingly, very different ANI polymerizations were obtained when nonstoichiometric PEC membranes having different molar ratio of cationic and anionic polyelectrolytes (P⁺:P^? represents PDADMAC:PSS) were used and transport of APS was fastest through the 2:1 PEC when compared to the 1:2 PEC. In all experiments, the polymerization was most intense on the ANI side of the membranes. Also, the influence of NaCl both during PEC fabrication and during polymerization was studied and found to have some effect on the solute permeability. Results showed that a higher content of PANI was formed on PEC membranes having excess P⁺ and with no NaCl added during PEC fabrication. Although X-ray diffraction confirmed the presence of PANI on both sides of each membrane, scanning electron microscopy images demonstrated that both sides of each membrane had different PANI content deposited. Electrical conductivity measurements using a four-point probe setup also showed that the PEC–PANI exhibits asymmetric electrical property on different sides. © 2021 Society of Industrial Chemistry.     

Predictive environmental hydrogen embrittlement on fracture toughness of commercial ferritic steels with hydrogen-modified fracture strain model

In this work, a practical numerical model with few parameters was proposed for the prediction of environmental hydrogen embrittlement. The proposed method adopts hydrogen enhanced plasticity-based mechanism in a fracture strain model to describe hydrogen embrittlement. Fracture toughness degradation of three commercial steels SA372J70, AISI4130 and X80 in high pressure hydrogen environment were investigated. Firstly, governing equations for hydrogen distribution and material damage evolution was established. Hydrogen enhanced localized flow softening effect was coupled within fracture strain dependency on stress triaxiality. Then, the numerical implementation and identification process of model parameters was described. Model parameters of the investigated steels were determined based on experiment results from literatures. Finally, with the calibrated model, fracture toughness reduction of the steels was predicted in a wide range of hydrogen pressure. The prediction results were compared with experimental results. Reasonable accuracy was reached. The proposed method is an attempt to reach balance between physical accurate prediction and engineering practicality. It is promising to provide a simplified numerical tool for the design and fit for service evaluation of hydrogen storage vessels.     

Scallops as a new source of food protein: high-intensity ultrasonication improved stability of oil-in-water emulsion stabilised by myofibrillar protein

In this study, the effect of high-intensity ultrasound (HIUS) (200 and 400 W for 0, 5, 10 and 15 min respectively) on conformational changes, physicochemical, rheological and emulsifying properties of scallop (Patinopecten yessoensis) myofibrillar protein (SMP) was investigated. HIUS-treated SMP had lower α-helix content and higher β-sheet content compared with the native SMP. HIUS treatment induced the unfolding of SMP and increased the surface hydrophobicity. The particle size of SMP decreased and the absolute zeta-potential increased after ultrasonication, which in turn increased the solubility of SMP. The conformational changes and the improvement of physicochemical properties of SMP increased the ability for SMP to lower the interfacial tension at the oil–water interface and increased the percentage of adsorbed protein. As a result, the emulsifying properties, rheological properties of SMP and storage stability of emulsions were also improved. In conclusion, HIUS treatment has future potential for improving the emulsifying properties of SMP.     

基于人工神经网络的智能化架空线路应变快速解调方法北大核心

为了提高智能化光纤复合架空线路态势感知的实时性,将人工神经网络方法应用于光纤沿线应变解调,确定了神经网络的结构。编程实现了基于洛伦兹模型的最小二乘谱拟合方法和神经网络方法,采用不同信噪比和布里渊频移的布里渊谱训练神经网络,将它们应用于某光纤复合架空线路沿线光纤应变的测量,从不同角度比较了两种方法的计算结果。计算结果表明,神经网络方法能有效获得光纤沿线的布里渊频移进而获得应变,具有与谱拟合方法相似的准确性,但应变解调时间仅约为谱拟合方法的1/20000。研究结果为提高智能光纤复合架空线路态势感知的实时性提供了参考。     

Numerical study of strain development in high-density polyethylene geomembrane liner system in landfills using a new constitutive model for municipal solid waste

Tensile strain development in high-density polyethylene (HDPE) geomembrane (GMB) liner systems in landfills was numerically investigated. A new constitutive model for municipal solid waste (MSW) that incorporates both mechanical creep and biodegradation was employed in the analyses. The MSW constitutive model is a Cam-Clay type of plasticity model and was implemented in the finite difference computer program FLAC?. The influence of the friction angle of the liner system interfaces, the biodegradation of MSW, and the MSW filling rate on tensile strains were investigated. Several design alternatives to reduce the maximum tensile strain under both short- and long-term waste settlement were evaluated. Results of the analyses indicate that landfill geometry, interface friction angles, and short- and long-term waste settlement are key factors in the development of tensile strains. The results show that long-term waste settlement can induce additional tensile strains after waste placement is complete. Using a HDPE GMB with a friction angle on its upper interface that is lower than the friction angle on the underlying interface, increasing the number of benches, and reducing the slope inclination are shown to mitigate the maximum tensile strain caused by waste placement and waste settlement.     

Direct View on the Origin of High Li+ Transfer Impedance in All-Solid-State Battery

Large interfacial resistance plays a dominant role in the performance of all-solid-state lithium-ion batteries. However, the mechanism of interfacial resistance has been under debate. Here, the Li⁺ transport at the interfacial region is investigated to reveal the origin of the high Li⁺ transfer impedance in a LiCoO₂(LCO)/LiPON/Pt all-solid-state battery. Both an unexpected nanocrystalline layer and a structurally disordered transition layer are discovered to be inherent to the LCO/LiPON interface. Under electrochemical conditions, the nanocrystalline layer with insufficient electrochemical stability leads to the introduction of voids during electrochemical cycles, which is the origin of the high Li⁺ transfer impedance at solid electrolyte-electrode interfaces. In addition, at relatively low temperatures, the oxygen vacancies migration in the transition layer results in the formation of Co₃O₄ nanocrystalline layer with nanovoids, which contributes to the high Li⁺ transfer impedance. This work sheds light on the mechanism for the high interfacial resistance and promotes overcoming the interfacial issues in all-solid-state batteries.     

Improved electric-field-induced strain and strong photoluminescence properties in novel Er3+-modified 0.93Bi0.5Na0.5TiO3-0.07BaTiO3 multifunctional ceramics

Recently, the progress of electronic devices toward miniaturization has strongly promoted development of multifunctional materials possessing multiple desirable properties. In this study, we develop and fabricate 0.93Bi_0.5Na_0.5TiO₃-0.07BaTiO₃-xEr multifunctional ceramics which show simultaneously considerable electric-field-induced strain and bright green light emission properties. With the introduction of Er³⁺, the ceramics gradually transform from non-ergodic relaxor phase to ergodic relaxor phase which could reversibly transform to ferroelectric phase under the electric field. As a result, with improving Er³⁺ content, the shape of the polarization-electric field loops of the ceramics become pinched, and it is obvious that the negative strain disappears while the positive strain gradually increases and reaches a maximum value 0.46% at x = 1.2 mol%. Besides, After the ceramics are poled, the light emission peak are greatly enhanced attributed to the decreased crystal symmetry and increased domain size, and is the strongest at x = 1.2 mol%. These results indicate that 0.93Bi_0.5Na_0.5TiO₃-0.07BaTiO₃-xEr ceramics are good candidates for developing multifunctional optoelectronic devices.     

Inhibition of stress corrosion cracking in 304 stainless steel through titanium ion implantation

The effects of titanium ion implantation on the stress corrosion cracking (SCC) behaviour of 304 austenitic stainless steel were studied. Slow strain rate tests (SSRTs) were conducted on 304 steel in air and in 5?wt-% NaCl solution. The microscopic effects of ion implantation were evaluated by Stopping and Range of Ions in Matter Procedures (SRIM). Fracture morphologies and microstructures were investigated by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The fracture surfaces illustrate that ion implantation significantly inhibits the corrosion pits that initiate SCC. A dense passive film, which inhibits SCC, was formed during the ion implantation process. SCC initiation was restrained due to the dense dislocation nets that were generated by titanium ion implantation.

Highlights

• Ion implantation inhibits SCC susceptibility.

• The lack of Cr at the grain boundary leads to the expansion of SCC along the grain boundary.

• Implantation-induced damage leads to high-density dislocations.

• The surface was amorphised due to high-density dislocations.

     

Effects of carbon nanotubes and interphase properties on the interfacial conductivity and electrical conductivity of polymer nanocomposites

L_c is the minimum length of carbon nanotubes (CNTs) required for efficient transfer of filler conductivity to polymer matrix in polymer CNT nanocomposites (PCNTs). In this work, L_c is correlated with the dimensions of the CNTs and the interphase thickness. Subsequently, the interfacial conductivity as well as the effective length and concentration of CNTs are expressed by CNT and interphase properties. Moreover, a simple model for the tunneling conductivity of PCNTs is developed with these effective terms. The impacts of all parameters on L_c, the interfacial conductivity, the fraction of CNTs in the networks and the conductivity of the PCNT are explained and justified. In addition, the predictions of the percolation threshold and conductivity are compared with the experimental results of several samples. The desirable values of interfacial conductivity are achieved by thin, short and super‐conductive CNTs, high waviness and a thick interphase. However, thin and long CNTs, low waviness, a thick interphase, poor tunneling resistivity due to the polymer matrix and a short tunneling distance advantageously affect the conductivity of PCNTs, because they produce large conductive networks. The predictions also show good agreement with the experimental measurements of percolation threshold and conductivity, which confirms the developed equations. © 2020 Society of Chemical Industry