漂珠低密度水泥浆由于密度低、强度高、体系稳定而在油田低压易漏层及低压油气层长封固段固井作业中获得了广泛的应用。但近年来,由于漂珠的产量越来越少,油田低成本要求急需开发代替漂珠的新型减轻材料,以满足配制低密度水泥浆的需求。开发了BCL-10S低密度混合减轻材料,其物化性能与漂珠相当,用它作减轻剂配制的低密度水泥浆性能与用漂珠作减轻剂配制的低密度水泥浆性能相媲美,并已经在长庆油田获得了应用。     

乐滩灌区输水隧洞穿合山煤矿采空区处理设计

分析了乐滩灌区工程北干渠溯河隧洞段长约1.06 km穿合山煤矿采空区的地质情况.借鉴高速公路煤矿采空区的成功处理经验,通过科学分析,对采空区变形和区域内覆岩的稳定性做了评价,论述了输水线路穿采空区段采取全充填压力注浆法的工程处理方法.     

Processing of Yttria-Alumina Coated Silicon Nitride Slips by Slip Casting

Si₃N₄powders coated with 6 wt% Y₂O₃and 4 wt% Al₂O₃were prepared by coprecipitation. The resulting powders were dispersed in water at different pH values and with addition of various amounts of ammonium polyacrylate (NH₄PA) to produce 32 vol% slips. The influence of the amount of NH₄PA solution added and pH on the rheological properties of 32 vol% coated Si₃N₄slips were studied. In addition, the sintered density of cast samples was determined and related to the degree of slip dispersion. The adsorption of the NH₄PA on the coated particle surface was rather high and the surface became saturated near 0.86 mg/m²at pH 9.2. High NH₄PA concentrations (1.7–3 wt%) were necessary to obtain well dispersed 32 vol% coated Si₃N₄slips at pH 9.2. The best stabilization was obtained with the addition of 2.3 wt% NH₄PA; in this condition, the viscosity reached a minimum value of 35 mPa.s at 100 s^–1. The slip viscosity increased with increasing pH from 9.2 to 10.2. Slips with low viscosities gave a more dense packing of cast samples and consequently higher sintered density values.     

钻井液用BDY-1便携式堵漏仪

在堵漏过程中，对堵漏材料和堵漏浆配方的优选是决定堵漏成功的关键。为了能在现场对堵漏进行评价，研制出BDY－1便携式堵漏仪，该堵漏仪主要由不锈钢钢柱圈钢，压力表等加工而成，该堵漏仪体积小，重量轻，价格低，仅为国产堵漏仪的1／20。试验结果表明BDY－1便携式堵漏仪操作简便，可快速对堵漏材料进行评价并筛选出堵漏配方；数据重复性好，准确可靠，能达到进口或国产堵漏仪的水平；在模拟漏层选定后，可采用多套压力梯度，对堵漏浆封堵效果进行评价，在压力梯度选定后，可评价堵漏浆对不同类型漏层的封堵效果；如果扩大压力范围，可对封堵后的漏层进行破裂试验，从而确定合理的钻井施工参数；适用现场操作和应用。     

用注凝成型技术制备莫来石陶瓷坯体

用注凝成型技术，通过控制合成莫来石粉料的细度，调节好pH值在单体和交联剂的比例，制备出稳定性好的料浆和强度高的生坯。     

粉煤灰降失水水泥浆在天然气井固井中的研究与应用

长庆天然气田属于低压、低渗透气田,存在承压能力较低的地层,固井设计要求全井段封固,并且采用双级双凝施工工艺。但由于用于低密度水泥浆中的漂珠生产量降低,价格上升,研究应用替代产品是固井技术发展的方向。在一级领浆中研究应用了粉煤灰水泥浆体系,其性能和固井质量可完全满足固井要求。粉煤灰水泥浆体系价格低和固井质量优良,使其成为漂珠水泥浆体系的替代配方。     

氧化铝/锌合金复合材料界面的SEM观察

利用挤压铸造制备氧化铝／锌合金复合材料，在扫描电镜（ＳＥＭ）上观察复合材料的界面。结果表明，在复合材料中纤维与基体间存在致密界面层，合金元素通过适当的化学反应可改善纤维与基体间的结合；在凝固过程中，纤维／基体界面上的硅在共晶体的共生生长过程中起了领先相作用，导致复合材料的共晶转变是由铝硅共晶转变和锌铝共晶转变两者组成。     

Anodising potential influence on well-ordered nanostructures formed by anodisation of aluminium in sulphuric acid

High-density structures with relatively well-ordered nanopore arrays have been obtained by the self-ordering growth of nanopores occurring during anodisation of aluminium in sulphuric acid. The resulting array of well-ordered nanopores strongly depends on an applied voltage of anodising, temperature and a procedure of synthesis. Regular arranged hexagonal arrays on aluminium with a relatively uniform pore diameter, interpore distance, and depth of pores exceeding 90 μm, can be formed by the self-ordering two-step anodising at 1 °C. The interpore distance and the pore diameter were evaluated on anodised aluminium layers obtained at different cell potentials ranging from 15 to 25 V. The detailed analyses of their uniformity were performed from SEM images. The analysis of a pore arrangement defects was made from SEM top view images taken on samples anodised at various cell potentials. The defect maps, known as Delaunay triangulations, of the arrangement of about 1000 pores were constructed for different applied anodising potentials. The percentage of pores that are not six-fold coordinated by the neighbouring pores indicates the percentage of defected surface.     

降低氧化铝生产中熟料折合比的探讨

在氧化铝生产过程中，熟料折合比是烧结法一项重要的综合性指标，本文通过对熟料折合比的定义、计算公式的剖析，分析了生产过程中影响熟料折合比的主要因素，对有效降低熟料折合比的措施进行了探讨。     

棕刚玉粉中Al2O3含量分析方法的探讨

对耐火材料——棕刚玉粉的质量分析控制，提出了用实用性的检测方法测定其Al2O3含量。通过与国家标准分析方法的对比试验，证实快速实用分析方法测定棕刚玉粉中Al2O3含量是可行的。