Zn对均匀化态Mg-3Sn-Ca镁合金腐蚀性能的影响

研究了Zn元素对均匀化态Mg-3Sn-Ca合金耐腐蚀性能的影响。通过XRD、金相、SEM、失重、析氢、电化学极化曲线和阻抗谱分析了Mg-3Sn-Ca(TX31)和Mg-3Sn-Ca-Zn(TXZ311)2种合金的耐蚀性能。结果表明,Mg-3Sn-Ca合金中主要由CaMgSn及Mg₂Sn相组成,加入Zn元素后晶粒得到显著细化,第二相体积分数增加并呈弥散分布,并有Mg₂Ca相析出。而Zn的添加可显著提高Mg-3Sn-Ca合金的耐蚀性能,这主要归因于TXZ311合金具有更细小的晶粒尺寸以及均匀密集分布的CaMgSn相,使合金在腐蚀过程中形成的钝化膜更加均匀。因此,TXZ311合金的耐蚀性远高于TX31合金。     

浅析油管螺纹加工质量缺陷

本文主要为了改进油管螺纹加工的质量,对油管螺纹在加工过程中存在的质量缺陷进行了分类分析,找出会对质量造成影响的各个因素,杜绝螺纹加工质量缺陷的问题再次发生,并不断的提高我国石油的开采率,促进我国石油业的发展。     

MgCO3在AZ31镁合金中的细化效果及机理

为改善AZ31镁合金铸态组织,用MgCO3对其进行细化,采用扫描电子显微镜、X射线衍射仪和金相显微镜研究了细化工艺参数对AZ31镁合金显微组织及其物相组成的影响.结果表明:在AZ31中添加质量分数为0.6%的MgCO3,于760℃保温10 min细化效果最佳,α-Mg晶粒的尺寸由基体合金的570μm降至100μm,降幅约82.5%.少量多次添加MgCO3的细化效果明显优于单次添加MgCO3的细化效果.研究认为,细化机理是MgCO3反应后生成的部分Al4C3质点作为异质核心细化晶粒,多余的Al4C3质点钉扎晶界阻碍晶粒长大.Al元素随固/液界面前沿被快速推至晶界,生成沿晶界生长的β-Mg17Al12相,起到进一步固定晶界的作用.合金元素的分布均有改变.     

GW103K镁合金熔体超声净化工艺

采用了超声场来处理GW103K镁合金熔体,考察了超声功率和超声处理温度对镁合金熔体净化效果的影响.研究结果表明:熔体净化程度与超声施加功率和熔体温度有关,温度太低和功率太大都不利于超声净化.在本实验条件下:680℃时,超声功率200W,处理时间60s净化效果比较明显;710和730℃时,超声功率160W,处理时间60 s净化效果比较好.铸锭中夹杂物越多电导率越小,电导率可以表征铸锭的净化程度.     

熔体保温条件下溶质Si含量对超声波处理铝合金凝固组织的影响

以工业纯铝、Al-2.5%Si合金、Al-5%Si合金以及Al-7%Si合金为对象,分别研究了保温条件下超声波处理对其凝固组织的影响.结果表明,在保温条件下,溶质Si的含量对超声波处理后铸锭的凝固组织有直接的影响.在694℃无超声波处理时,溶质Si含量大的铸锭,等轴晶细小且分布均匀;而在相同条件下进行超声波处理时,随着溶质Si含量的增多,等轴晶区域也随之增大,由于随着溶质Si含量的增多,细小的二次枝晶以及三次枝晶很容易被声流的搅拌作用所分断,并且破碎的枝晶随着这种搅拌作用而被分散到熔体的各处,从而产生了细化效果.另外,由于超声波的空化作用,对纯铝也有一定的细化效果,但是不如对合金的明显.     

Effect of ultrasonic stirring on temperature distribution and grain refinement in Al- 1.65%Si alloy melt

A series of experiments were conducted for Al-1.65%Si （mass fraction） alloy melt to study the formation of grain refining structure with ultrasonic stirring. The cooling curves of ingots with ultrasonic were measured and compared with those without ultrasonic. At the same time, the effect of the time of ultrasonic stirring on solidification structure of ingots was investigated. The influence of ultrasonic on the grain-refining efficiency of ingots was analyzed. In order to well understand the melts behavior under ultrasonic, by using ammonium chloride solution, the simulation experiment was carried out and the temperature distribution in ingot with or without ultrasonic was compared. The results indicate that the ultrasonic reduces the temperature inhomogeneity of melt, i.e. the ultrasonic helps to homogenize the melt temperature. The effect of stirring and heat generation in ingot start to occur with increasing the time of ultrasonic stirring.     

水利社会学系列文章之二 从秦始皇决策郑国渠说起

大家知道．西汉著名历史学家司马迁在《史记·河渠书冲记载了一则秦始皇决策郑国渠工程的故事，十分引人注目。原文是这样的：“韩闻案之好共事，欲罢之，母令东伐，乃使水工郑国］司说秦，令凿经水，……东往洛三百余里，……中作而觉，秦欲东郑国。郑国日：始臣为间，然渠成亦素之利也。臣为韩延数岁之命，而为秦建万世之功。秦以为然，卒使就渠。渠成而准注填淤之水，溉泽卤之地四万余顷，收皆亩一钟。干是关中为沃野，无凶年，秦以富强，卒井诸侯，固命回郑国渠。”在这则故事中，作者特别强调了两个重要的社会事实：第一个事实是，一项…     

超声波对Al-1％Si合金铸锭力学性能的影响

以Al-1％Si合金为对象,研究了超声波处理对其力学性能的影响,包括抗拉强度、延伸率、硬度和冲击韧性。研究结果表明,合适的超声波处理时间可以大幅度提高合金的抗拉强度、延伸率、硬度和冲击韧性值。通过对试样宏观组织和微观断口的分析,说明超声波的空化作用及声流作用可以细化晶粒,使其凝固组织致密,从而提高了合金的力学性能。