Direct ink writing of vancomycin-loaded polycaprolactone/ polyethylene oxide/ hydroxyapatite 3D scaffolds

Novel inks were formulated by dissolving polycaprolactone (PCL), a hydrophobic polymer, in organic solvent systems; polyethylene oxide (PEO) was incorporated to extend the range of hydrophilicity of the system. Hydroxyapatite (HAp) with a weight ratio of 55–85% was added to the polymer-based solution to mimic the material composition of natural bone tissue. The direct ink writing (DIW) technique was applied to extrude the formulated inks to fabricate the predesigned tissue scaffold structures; the influence of HAp concentration was investigated. The results indicate that in comparison to other inks containing HAp (55%, 75%, and 85%w/w), the ink containing 65% w/w HAp had faster ink recovery behavior; the fabricated scaffold had a rougher surface as well as better mechanical properties and wettability. It is noted that the 65% w/w HAp concentration is similar to the inorganic composition of natural bone tissue. The elastic modulus values of PCL/PEO/HAp scaffolds were in the range of 4–12 MPa; the values were dependent on the HAp concentration. Furthermore, vancomycin as a model drug was successfully encapsulated in the PCL/PEO/HAp composite scaffold for drug release applications. This paper presents novel drug-loaded PCL/PEO/HAp inks for 3D scaffold fabrication using the DIW printing technique for potential bone scaffold applications.     

Suppressed Lattice Disorder for Large Emission Enhancement and Structural Robustness in Hybrid Lead Iodide Perovskite Discovered by High-Pressure Isotope Effect

The soft nature of organic–inorganic halide perovskites renders their lattice particularly tunable to external stimuli such as pressure, undoubtedly offering an effective way to modify their structure for extraordinary optoelectronic properties. Here, using the methylammonium lead iodide as a representative exploratory platform, it is observed that the pressure-driven lattice disorder can be significantly suppressed via hydrogen isotope effect, which is crucial for better optical and mechanical properties previously unattainable. By a comprehensive in situ neutron/synchrotron-based analysis and optical characterizations, a remarkable photoluminescence (PL) enhancement by threefold is convinced in deuterated CD₃ND₃PbI₃, which also shows much greater structural robustness with retainable PL after high peak-pressure compression–decompression cycle. With the first-principles calculations, an atomic level understanding of the strong correlation among the organic sublattice and lead iodide octahedral framework and structural photonics is proposed, where the less dynamic CD₃ND₃⁺ cations are vital to maintain the long-range crystalline order through steric and Coulombic interactions. These results also show that CD₃ND₃PbI₃-based solar cell has comparable photovoltaic performance as CH₃NH₃PbI₃-based device but exhibits considerably slower degradation behavior, thus representing a paradigm by suggesting isotope-functionalized perovskite materials for better materials-by-design and more stable photovoltaic application.     

Electrochemical Quantification of Neurotransmitters in Single Live Cell Vesicles Shows Exocytosis is Predominantly Partial

Exocytosis plays an essential role in the communication between cells in the nervous system. Understanding the regulation of neurotransmitter release during exocytosis and the amount of neurotransmitter content that is stored in vesicles is of importance, as it provides fundamental insights to understand how the brain works and how neurons elicit a certain behavior. In this minireview, we summarize recent progress in amperometric measurements for monitoring exocytosis in single cells and electrochemical cytometry measurements of vesicular neurotransmitter content in individual vesicles. Important steps have increased our understanding of the different mechanisms of exocytosis. Increasing evidence is firmly establishing that partial release is the primary mechanism of release in multiple cell types.     

Improvement of a commercial calcium phosphate bone cement by means of drug delivery and increased injectability

Calcium phosphate cements (CPCs) have been increasingly used as synthetic bone substitutes for repair and regeneration of bone defects given their biocompatibility, resemblance to bone and malleability. Moreover, their use as local antibiotic delivery systems is of main interest against bone infections, avoiding the adverse effects of high dosages of conventional therapy. The main goals of this work were to improve the properties of a commercial CPC (Neocement®), turning it injectable, and to provide it with a new functionality as a drug delivery system able to ensure a sustained release of an antibiotic commonly used in orthopaedics (gentamicin sulphate, GS). For this, the influence of the liquid phase amount (%LP) and type of polymer contained in the formulation (chitosan, Chi, or hydroxypropyl methylcellulose, HPMC) on the basic properties of the material was evaluated. It was found that the formulation containing 42%LP + HPMC+1.87% wt GS was the best one. It showed suitable setting and mechanical properties, and injectability around 87% (much superior to the original Neocement®, with 31%). It ensured a sustained release of GS for at least 14 days, at antibacterial levels. The antibiotic released is highly effective against S. epidermidis, but also presents some antibacterial activity against S. aureus. The CPC revealed to be non-cytotoxic. Moreover, it demonstrated good flowability and connectivity with human cadaveric trabecular bone.     

A comparative study on pyrolysis reactivity and gas release characteristics of biomass and coal using TG-MS analysis

Pyrolysis reactivity and gas release characteristics of biomass and coals were comparatively investigated using TG-MS. In addition, chemical compositions and structures of tested samples were determined to correlate pyrolysis gas release characteristic. It was found that pyrolysis reactivity and gaseous product release were hardly varied with pyrolysis heating rate. Furthermore, pyrolysis rates of two biomass samples were greater than those of coals, which were mainly attributed to the chemical compositions and the gaseous product evolution process. The result also showed that gaseous product release during pyrolysis process was related to the presence of different functional groups in samples.     

压裂管汇无损检测方法改进

:按照现有无损探伤检验标准检验合格的压裂管汇在压裂作业时出现了管件刺漏、爆裂等情况。分析了压裂管汇中管件结构的特点和现有的无损检测方法的适用性。增加了管件的检测部位,改进了检测方法,并研制出了能检测不同形状和尺寸管件的超声波探头和比对试件。采用改进的无损检测方法,检测出不合格管件数增加44.9%。新增加检测部位后,检测出不合格管件数增加63.7%。目前已应用改进的无损检测方法1 a多,在压裂作业时未出现高压管件刺漏或爆裂情况。     

Headspace fingerprinting approach to identify the major pathway influencing volatile patterns of vinasse-cured duck processed by high pressure,as well as its impact on physicochemical and sensory attributes

As a decisive attribute, flavour could be influenced by HP treatments through multiple physical and chemical pathways within the high pressure (HP)-assisted meat curing process. This investigation aimed to identify the major pathway influencing volatile flavour patterns of two representative vinasse-cured duck (VCD) products with HP treatments (150–300 MPa/15 min), including wet and dry types, by employing headspace fingerprinting as an untargeted approach. Results suggested that HP treatments greatly lowered moisture contents and increased Warner-Bratzler shear force and thiobarbituric acid reactive substances of the cured samples. According to multivariate models, the volatile flavour patterns of the HP-processed VCD could be clearly separated from the unprocessed samples, but the VCD pressurised at different intensities represented similar volatile fingerprinting, which was validated by e-nose analysis. The discriminant analysis (OPLS-DA) model outlined vinasse-derived ethanol, acetic acid, 3-methyl-1-butanol, 2-methyl-1-butanol, phenethyl alcohol and 2-methyl-3-octanone as the major discriminant aromas across the unpressurised and pressurised samples.     

Dual pH‐ and thermal‐responsive nanocomposite hydrogels for controllable delivery of hydrophobic drug baicalein

Hydrogels have been widely used as mild biomaterials due to their bio‐affinity, high drug loading capability and controllable release profiles. However, hydrogel‐based carriers are greatly limited for the delivery of hydrophobic payloads due to the lack of hydrophobic binding sites. Herein, nano‐liposome micelles were embedded in semi‐interpenetrating poly[(N‐isopropylacrylamide)‐co‐chitosan] (PNIPAAm‐co‐CS) and poly[(N‐isopropylacrylamide)‐co‐(sodium alginate)] (PNIPAAm‐co‐SA) hydrogels which were responsive to both temperature and pH, thereby establishing tunable nanocomposite hydrogel delivery systems. Nano‐micelles formed via the self‐assembly of phospholipid could serve as the link between hydrophobic drug and hydrophilic hydrogel due to their special amphiphilic structure. The results of transmission and scanning electron microscopies and infrared spectroscopy showed that the porous hydrogels were successfully fabricated and the liposomes encapsulated with baicalein could be well contained in the network. In addition, the experimental results of response release in vitro revealed that the smart hydrogels showed different degree of sensitiveness under different pH and temperature stimuli. The results of the study demonstrate that combining PNIPAAm‐co‐SA and PNIPAAm‐co‐CS hydrogels with liposomes encapsulated with hydrophobic drugs is a feasible method for hydrophobic drug delivery and have potential application prospects in the medical field. © 2018 Society of Chemical Industry     

Validation of a 3D multiphase-multicomponent CFD model for accidental liquid and gaseous hydrogen releases

As hydrogen-air mixtures are flammable in a wide range of concentrations and the minimum ignition energy is low compared to hydrocarbon fuels, the safe handling of hydrogen is of utmost importance. Additional hazards may arise with the accidental spill of liquid hydrogen. Such a release of LH2 leads to a formation of a cryogenic pool, a dynamic vaporization process, and consequently a dispersion of gaseous hydrogen into the environment. Several LH2 release experiments as well as modeling approaches address this phenomenology. In contrast to existing approaches a new CFD model capable of simulating liquid and gaseous distribution was developed at Forschungszentrum Jülich. It is validated against existing experiments and yields no substantial lacks in the physical model and reveals a qualitatively consistent prediction. Nevertheless, the deviation between experiment and simulation raises questions on the completeness of the database, in particular with regard to the boundary conditions and available measurements.