Ultrasonic-assisted wetting and soldering of AlN ceramic by using a nonactive solder (Sn9Zn) in air

AlN ceramic was successfully wetted and then joined with nonactive Sn9Zn eutectic solder assisted by ultrasonication in air. The effect of ultrasonic time on the formation of joint was studied. Results indicated that the defect-free joint can be obtained at an ultrasonic time of 5 s. Two regions, namely, AlN/Sn (s,_s) and AlN/Zn (s,_s), were found in the bonding interface. Zn and O accumulated in the AlN/Sn (s,_s) interface. An amorphous and nanocrystalline layer of ZnO formed in the hard-wet AlN surface. And Zn (s,_s) directly bonded with AlN. The low temperature and fast bonding of the AlN was attributed to the high pressure and temperature caused by cavitation effect. The shear strength of the joint increased from 10.6 MPa to 30.7 MPa when the ultrasonic treatment time increased from 5 s to 150 s. With the prolongation of ultrasonic time, more AlN ceramic particles entered the solder and acted as the reinforcing phase.     

Metal chlorides-promoted ammonia absorption of deep eutectic solvent

Ammonia is considered as a promising hydrogen or energy carrier. Ammonia absorption or adsorption is an important aspect for both ammonia removal, storage and separation applications. To these ends, a wide range of solid and liquid sorbents have been investigated. Among these, the deep eutectic solvent (DES) is emerging as a promising class of ammonia absorbers. Herein, we report a novel type of DES, i.e., metal-containing DESs for ammonia absorption. Specifically, the NH₃ absorption capacity is enhanced by ca. 18.1–36.9% when a small amount of metal chlorides, such as MgCl₂, MnCl₂ etc., are added into a DES composed of resorcinol (Res) and ethylene glycol (EG). To our knowledge, the MgCl₂/Res/EG (0.1:1:2) DES outperforms most of the reported DESs. The excellent NH₃ absorption performances of metal–containing DESs have been attributed to the synergy of Lewis acid–base and hydrogen bonding interactions. Additionally, good reversibility and high NH₃/CO₂ selectivity are achieved over the MgCl₂/Res/EG (0.1:1:2) DES, which enables it to be a potential NH₃ absorber for further investigations.     

Adenine-functionalized conjugated polymer as an efficient photocatalyst for hydrogen evolution from water

Conjugated polymers have emerged as a promising class of organic photocatalysts for photocatalytic hydrogen evolution from water splitting due to their adjustable chemical structures and electronic properties. However, developing highly efficient organic polymer photocatalysts with high photocatalytic activity for hydrogen evolution remains a significant challenge. Herein, we present an efficient approach to enhance the photocatalytic performance of linear conjugated polymers by modifying the surface chemistry via introducing a hydrophilic adenine group into the side chain. The adenine unit with five nitrogen atoms could enhance the interaction between the surface of polymer photocatalyst and water molecules through the formation of hydrogen bonding, which improves the hydrophilicity and dispersity of the resulting polymer photocatalyst in the photocatalytic reaction solution. In addition, the strong electron-donating ability of adenine group with plentiful nitrogen atoms could promote the separation of light-induced electrons and holes. As a result, the adenine-functionalized conjugated polymer PF6A-DBTO2 shows a high photocatalytic activity with a hydrogen evolution rate (HER) of 25.21 mmol g^?1 h^?1 under UV-Vis light irradiation, which is much higher than that of its counterpart polymer PF6-DBTO2 without the adenine group (6.53 mmol g^?1 h^?1). More importantly, PF6A-DBTO2 without addition of a Pt co-catalyst also exhibits an impressive HER of 21.93 mmol g^?1 h^?1 under visible light (λ > 420 nm). This work highlights that it is an efficient strategy to improve the photocatalytic activity of conjugated polymer photocatalysts by the modification of surface chemistry.     

Stress-strain behavior of geotextile: A proposed new indirect calculation using the static puncture test (CBR test)

Some of the main applications of geosynthetics include use as a hydraulic barrier in sanitary landfills, as a reinforcement element and in pavement engineering. In most cases, these materials are subject to the overlapping effects of tensile strength and puncture. This paper presents a review of indirect methods for calculation of stress and strain averages by means of the California Bearing Ratio (CBR) puncture strength test. In addition, a new calculation method is proposed based on the Kirchhoff plate theory, which interprets the behavior of thin circular plates subjected to a uniform normal loading. This new method enables analysis of the stress-strain in each stretch of the geosynthetic. The methodology is applied to four woven geotextiles of different weights. The results of the new calculation method yielded a better stress-strain correlation with direct tensile strength tests, presenting the smallest relative errors compared to the other indirect calculations reviewed. With the aid of a disk and pins, vertical displacement values at different points in the geotextiles were measured and showed good agreement with analytical predictions. Therefore, the static puncture test combined with the new proposed calculation method is a good alternative for determining the stress-strain parameters of geotextile.     

Establishment of a color tolerance for yarn-dyed fabrics from different color-depth yarns

Yarn-dyed fabric is often woven from warp and weft yarns in the same color depth to ensure a uniform color appearance. The difference in color depth between warp and weft tends to result in the uneven color of the yarn-dyed fabric. This article aims to establish a color tolerance for yarn-dyed fabric that can be woven with a qualified color appearance but from the warp and weft yarns in different color depths. A total of 27 yarn-dyed fabric samples in three color series (red, yellow, and blue) were evaluated by using the yarn-dyed fabric from warp and weft yarns in the same color depth of 2% (on weight of fabric, owf) as the standard. Visual assessment and instrumental measurement of color were carried out to establish the color tolerance ellipse that was defined as CMC (Color Measurement Committee) color differences (2:1) of no more than 1.00. It was found that the color strengths (K/S) and color differences (ΔE_CMC(2:1)) of these fabric samples for each color series had linear relationships with the color depths of warp and weft yarns. The color tolerance ellipses indicated that, even though the warp and weft yarns had an apparent color difference, they could be woven in fabrics with relatively uniform color appearance and meet the requirements for yarn-dyed fabric. This work provided valuable insight into the production of qualified yarn-dyed fabrics from unqualified dyed yarns.     

异种铁素体耐热钢接头界面组织及其影响

综述了铁素体与铁素体异种金属焊缝（dissimilar metal welds，DMWs）接头界面组织及其影响。结果表明，在焊后热处理或运行温度下的铁素体钢DMWs接头的不均匀界面组织中，通常会形成脱碳层和增碳层。在铁素体钢DMWs焊接接头界面组织影响因素中，焊缝金属的化学成分有重要影响；焊后热处理规范（温度和时间）、工作温度下运行时间的影响较为突出；焊接工艺参数的影响亦不可忽略。异种钢接头界面处近缝区裂纹的产生，以及接头的蠕变强度随Larson Miller 参数增大而下降等不利影响，均为异种钢界面碳迁移行为所导致。焊缝成分控制法是接头界面组织控制或改善的必要条件，而脱碳层部位转移法能有效防止裂纹发生，亦是接头安全运行的重要工艺措施之一。     

Microstructural and mechanical properties assessment of transient liquid phase bonding of CoCuFeMnNi high entropy alloy

The transient liquid phase (TLP) bonding of CoCuFeMnNi high entropy alloy (HEA) was studied. The TLP bonding was performed using AWS BNi-2 interlayer at 1050 °C with the TLP bonding time of 20, 60, 180 and 240 min. The effect of bonding time on the joint microstructure was characterized by SEM and EDS. Microstructural results confirmed that complete isothermal solidification occurred approximately at 240 min of bonding time. For samples bonded at 20, 60 and 180 min, athermal solidification zone was formed in the bonding area which included Cr-rich boride and Mn₃Si intermetallic compound. For all samples, the γ solid solution was formed in the isothermal solidification zone of the bonding zone. To evaluate the effect of TLP bonding time on mechanical properties of joints, the shear strength and micro-hardness of joints were measured. The results indicated a decrement of micro-hardness in the bonding zone and an increment of micro-hardness in the adjacent zone of joints. The minimum and maximum values of shear strength were 100 and 180 MPa for joints with the bonding time of 20 and 240 min, respectively.     

Development of mullite fibers and novel zirconia-toughened mullite fibers for high temperature applications

Polycrystalline mullite fibers and novel zirconia-toughened mullite (ZTM) fibers with average diameters between 9.7 and 10.3 μm containing 3, 7 and 15 wt.-% tetragonal ZrO₂ (ZTM3, ZTM7, ZTM15) in the final ceramic were prepared via dry spinning followed by continuous calcination and sintering in air. A shift in the formation of transient alumina phases and tetragonal ZrO₂ to higher temperatures with increasing amounts of ZrO₂ was observed. Concomitantly, the mullite formation temperature was lowered to 1229 °C for ZTM15 fibers. X-ray diffraction revealed formation of the desired tetragonal crystal structure of ZrO₂ directly from the amorphous precursor. Room temperature Weibull strengths of 1320, 1390 and 1740 MPa and Weibull moduli of 9.5, 7.1 and 9.0 were determined for mullite, ZTM3 and ZTM15 fibers, respectively. Average Young’s moduli ranged from 190 to 220 GPa. SEM images revealed crack-free fiber surfaces and compact microstructures independent of the amount of ZrO₂.     

Flash joining of alumina ceramics under a small current density

The ceramic joining using electric field (E-field) has garnered significant research attention due to the decreased joining barrier and enhanced reliability. However, the underlying mechanism of E-field assisted joining remains unclear. Herein, we report the rapid joining of alumina ceramics using a small current. Moreover, the E-field is applied in both perpendicular and parallel directions to the faying surfaces, demonstrating a significant difference in terms of joint strength. These results indicate that the E-field generates defects and promotes the joining process by facilitating ionic diffusion.     

基于C#持久蠕变强度外推功能的实现

持久蠕变强度外推是预测材料在高温高压环境下工作寿命的有效方法。目前常用的外推方法有等温法和参数法。这两种方法都是通过在实验室中采用较短时间的试验，获取试验数据后，通过Excel或者MATLAB等数据处理软件进行数据的拟合处理和外推计算。这些数据归纳统计和数学建模的过程有时需要耗费试验人员的大量精力。介绍了持久蠕变强度外推的软件实现方法，该功能包含在持久蠕变试验设备配备的软件中，试验完成后，软件直接根据试验结果进行数据拟合和持久蠕变强度的外推计算，无需试验数据的统计和建模，大大提高了持久蠕变强度外推计算的效率。