Influence of SiC microstructure on its corrosion behavior in molten FLiNaK salt

The influence of the microstructure on the corrosion rate of three monolithic SiC samples in FLiNaK salt at 900 °C for 250 h was studied. The SiC samples, labeled as SiC-1, SiC-2, and SiC-3, had corrosion rates of 0.137, 0.020, and 0.043 mg/cm²h, respectively. Compared with grain size and the presence of special grain boundaries (i.e., Σ3), the content of high-angle grain boundaries (HAGBs) appeared to have the strongest influence on the corrosion rate of SiC in FLiNaK salt, since the corrosion rate increased six times as the concentration of high-angle grain boundaries increased from 19 to 32% for SiC-2 and SiC-1, respectively. These results stress the importance of controlling the content of HAGBs during the production process of SiC.     

WavNet — Visual saliency detection using Discrete Wavelet Convolutional Neural Network

In the recent advancements in image and video analysis, the detection of salient regions in the image becomes the initial step. This plays a crucial role in deciding the performance of such algorithms. In this work, a Multi-Resolution Feature Extraction (MRFE) technique that makes use of Discrete Wavelet Convolutional Neural Network (DWCNN) for generating features is employed. An Enhanced Feature Extraction (EFE) module extracts additional features from the high level features of the DWCNN, which are used to frame both channel as well as spatial attention models for yielding contextual attention maps. A new hybrid loss function is also proposed, which is a combination of Balanced Cross Entropy (BCE) loss and Edge based Structural Similarity (ESSIM) loss that effectively identifies and segments the salient regions with clear boundaries. The method is tested exhaustively with five different benchmark datasets and is proved superior to the existing state-of-the-art methods with a minimum Mean Absolute error (MAE) of 0.03 and F-measure of 0.956.     

Optimized microwave absorption properties by tailoring the morphology of carbon coated TiC nanoparticles by N2 pressure

Increasing the dielectric loss capacity plays an important role in enhancing the electromagnetic absorption performance of materials. It remains a challenge to simultaneously introduce multiple types of dielectric losses in the material. In this work, we show that the atomic and interfacial dipole polarizations can be simultaneously enhanced by substituting N species into both carbon coating layers and bulk TiC lattices of a core-shell TiC@C material. Additionally, substitution of N species results more exposed TiC(111) facets and refines the TiC grain sizes in the bulk material, which is beneficial for enhancing the scattering of the external electromagnetic waves. The maximum reflection loss of the N substituted TiC@C material is measured as ?47.1 dB with an effective absorbing bandwidth of 4.83 GHz at 1.9 mm, which illustrates a valuable way to further tuning the electromagnetic absorption performance of this type of materials.     

Effects of upholstery materials on the burning behavior of real‐scale residential upholstered furniture mock‐ups

Fire spread and growth on real‐scale four cushion mock‐ups of residential upholstered furniture (RUF) were investigated with the goal of identifying whether changes in five classes of materials (barrier, flexible polyurethane foam, polyester fiber wrap, upholstery fabric, and sewing thread), referred to as factors, resulted in statistically significant changes in burning behavior. A fractional factorial experimental design plus practical considerations yielded a test matrix with 20 material combinations. Experiments were repeated a minimum of two times. Measurements included fire spread rates derived from video recordings and heat release rates (HRRs). A total of 13 experimental parameters (3 based on the videos and 10 on the HRR results), referred to as responses, characterized the measurements. Statistical analyses based on Main Effects Plots (main effects) and Block Plots (main effects and factor interactions) were used. The results showed that three of the factors resulted in statistically significant effects on varying numbers of the 13 responses. The Barrier and Fabric factors had the strongest main effects with roughly comparable magnitudes. Foam was statistically significant for fewer of the responses and its overall strength was weaker than for Barrier and Fabric. No statistically significant main effects were identified for Wrap or Thread. Multiple two‐term interactions between factors were identified as being statistically significant. The Barrier*Fabric interaction resulted in the highest number of and strongest statistically significant effects. The existence of two‐term interactions means that it will be necessary to consider their effects in approaches designed to predict the burning behavior of RUF.     

Nonlinear dielectric response and positive dielectric tunability in antipolar CaTiSiO5

Dielectric tunability has been extensively investigated in ferroelectric materials, which exhibit a negative tunability of dielectric permittivity in an external electric field. In contrast, positive tunability is rare and has been reported only in a few antiferroelectric materials. We present positive (and negative) tunability in the titanite, CaTiSiO₅. The dielectric property of CaTiSiO₅ was measured up to an extraordinarily high electric field of 40 MV/m. A nonlinear polarization field loop with no hysteresis was obtained. The dielectric permittivity of ε_r ~ 25 increases up to ε_r ~ 40 at 20 MV/m and room temperature. Although titanite has an antipolar structure and is expected to be “antiferroelectric,” its dielectric response in high electric fields up to ~40 MV/m differs from that of conventional antiferroelectrics. We demonstrate that the phase-transition temperature and dielectric tunability could be modulated through the chemical substitution of Ca_1−xLa_xTiSi_1−xAl_xO₅, in which the destabilization of the long-range antipolar order is revealed by transmission electron microscopy analysis. These results indicate that the observed dielectric response to an electric field may originate from the unique features of the antipolar and domain structures in CaTiSiO₅.     

Investigation on thermal conductivity and mechanical properties of Si3N4 ceramics via one-step sintering

High thermal conductivity Si₃N₄ ceramics were fabricated using a one-step method consisting of reaction-bonded Si₃N₄ (RBSN) and post-sintering. The influence of Si content on nitridation rate, β/(α+β) phase rate, thermal conductivity and mechanical properties was investigated in this work. It is of special interest to note that the thermal conductivity showed a tendency to increase first and then decrease with increasing Si content. This experimental result shows that the optimal thermal conductivity and fracture toughness were obtained to be 66 W (m K)^-1 and 12.0 MPa m^1/2, respectively. As a comparison, the nitridation rate and β/(α+β) phase rate in a static pressure nitriding system, i.e., 97% (MS10), 97% (MS15), 97% (MS20) and 8.3% (MS10), 8.3% (MS15), 8.9% (MS20), respectively, have obvious advantages over those in a flowing nitriding system, i.e., 91% (MS10), 91% (MS15), 93% (MS20) and 3.1% (MS10), 3.3% (MS15), 3.3% (MS20), respectively. Moreover, high lattice integrity of the β-Si₃N₄ phase was observed, which can effectively confine O atoms into the β-Si₃N₄ lattice using MgO as a sintering additive. This result indicates that one-step sintering can provide a new route to prepare Si₃N₄ ceramics with a good combination of thermal conductivity and mechanical properties.     

Revealing cracking and breakage behaviours of gibbsite particles

Mitigating gibbsite particle cracking and breakage during industrial alumina production can increase the quality of smelter grade alumina product by reducing the ultrafine particle content. Therefore, it is essential to investigate the particle cracking during static calcination and the breakage of calcined gibbsite particles under external force. In this work, we investigated the impact of the calcination ramping rate and the crystallite size on gibbsite particle cracking during static calcination. A slow ramping rate and a large pristine crystallite size tend to increase particle cracking. Apart from the study of particle cracking behaviour, we also investigated the breakage of calcined gibbsite particle under external force. Cracks on the particle surface can initiate breakage within the crystallite and along the grain boundary under external force. The breakage within crystallite occurs as the cleavage of the crystallite, while the breakage along the grain boundary leads to the shedding of a whole crystallite. We further explored the factors influencing the strength of calcined gibbsite particles. With increasing calcination temperature, the strength of particle increases when gibbsite converts to boehmite, and then decreases when boehmite converts into amorphous alumina. Particles containing smaller crystallites and calcined with fast ramping rates exhibit higher resistance to breakage.     

Self-Adaptive Control System for Additive Manufacturing Using Double Electrode Micro Plasma Arc Welding

Wire arc additive manufacturing(WAAM)has been investigated to deposit large-scale metal parts due to its high deposition efficiency and low material cost.However,in the process of automatically manufacturing the high-quality metal parts by WAAM,several problems about the heat build-up,the deposit-path optimization,and the stability of the process parameters need to be well addressed.To overcome these issues,a new WAAM method based on the double electrode micro plasma arc welding(DE-MPAW)was designed.The circuit principles of different metal-transfer models in the DE-MPAW deposition process were analyzed theoretically.The effects between the parameters,wire feed rate and torch stand-off distance,in the process of WAAM were investigated experimentally.In addition,a real-time DE-MPAW control system was developed to optimize and stabilize the deposition process by self-adaptively changing the wire feed rate and torch stand-off distance.Finally,a series of tests were performed to evaluate the con-trol system's performance.The results show that the capability against interferences in the process of WAAM has been enhanced by this self-adaptive adjustment system.Further,the deposition paths about the metal part's layer heights in WAAM are simplified.Finally,the appearance of the WAAM-deposited metal layers is also improved with the use of the control system.     

某微细粒嵌布磁铁矿选矿工艺研究

针对某微细粒磁铁矿进行了全磁选流程和磁选-反浮选流程对比试验研究。结果表明,在最终磨矿细度相当的情况下,2种工艺流程都获得了产率48%左右、TFe品位66%左右、回收率80%左右的铁精矿指标,而采用磁选-反浮选流程的第三段磨矿量比全磁选流程减少了2/3。磁选-反浮选流程具有显著的节能降耗优势。     

天然气水合物储层泥质细粉砂挡砂介质堵塞规律与微观挡砂机制

中国南海海域部分天然气水合物储层中地层砂为高泥质含量细粉砂，开采防控砂难度较大。针对高泥质细粉砂挡砂机制问题，使用粒度中值为10.13 μm的泥质细粉砂样品，模拟单向气液携砂流动条件，使用绕丝筛板、金属烧结网、金属纤维、预充填陶粒4类挡砂介质在20~80 μm挡砂精度下进行挡砂模拟实验，采用显微成像系统观察挡砂介质内部及表面砂粒沉积与堵塞动态，分析介质流通性能和挡砂性能变化，总结堵塞规律、微观挡砂机制与形态及其控制因素。研究结果表明，不同类型和精度的挡砂介质对泥质细粉砂的堵塞总体呈现堵塞开始、堵塞加剧和堵塞平衡3个阶段。随着驱替进行，挡砂介质渗透率逐渐降低，幅度会高达90%以上；同时过砂速度减缓，最终过砂率为5%~10%。根据堵塞规律和微观图像分析，提出了粗组分分选桥架、局部砂团适度挡砂、整体砂桥阻挡等挡砂介质对泥质细粉砂的3种微观挡砂机制。以粗组分分选桥架挡砂机制为主的挡砂工况下，挡砂介质堵塞渗透率较高，但过砂率超过15%，挡砂效果较差；以整体砂桥挡砂机制为主时，过砂率在10%以下，挡砂性能较好，但各类挡砂介质的堵塞渗透率不足1 D，流通性能较差。局部砂团适度挡砂机制为主时介质挡砂性能及流通性能介于两者之间。挡砂介质对天然气水合物储层泥质细粉砂的微观挡砂机制和形态受挡砂介质类型、精度、地层砂特征以及流动条件等因素控制，其规律对于水合物泥质细粉砂防控砂优化有指导意义。