To explore the feasibility and related mechanism of MFC biosensor for wastewater detection under the action of combined heavy metals. Cyclic voltammetry (CV) and scanning electrochemical impedance spectroscopy (EIS) were used to explore the related bioelectrochemical process. The response of the reactor to single/combined heavy metals, low/high heavy metal concentrations, and the differences in ohmic resistance (Rs) and charge transfer resistance (Rct) were investigated using Ni as the core heavy metal and the combined action of Cd, Cu and Zn. The results indicated that there was a linear relationship between the concentration and output voltage of the MFC biosensor under the action of combined heavy metals (R² = 0.8803–0.973). However, the internal resistance (Rint) of the MFC biosensor under the action of single heavy metal was far less than that of the combined heavy metal group, and the power density (19.849 W m^?3) was 4 times that of the combined heavy metal group (3.109–4.589 W m^?3). The Rs of the biosensors in the combined heavy metal group were 0.868Ω and 0.860, which were higher than 0.768Ω of the single heavy metal sensor. With the increase of the concentration of heavy metals in the influent, the increase of Rct was more obvious in the combined group, while the Rs in the single group significantly increased (P < 0.05). The results imply that it is possible for MFC biosensors to be used in the detection of actual water polluted by various heavy metals, but the biosensor performance is mainly limited by Rct, which needs to be further improved.     

Good dielectric performance and broadband dielectric polarization in Ag,Nb co-doped TiO2

Due to the demand of miniaturization and integration for ceramic capacitors in electronic components market, TiO₂-based ceramics with colossal permittivity has become a research hotspot in recent years. In this work, we report that Ag⁺/Nb⁵⁺ co-doped (Ag_1/4Nb_3/4)_xTi_1−xO₂ (ANTOx) ceramics with colossal permittivity over a wide frequency and temperature range were successfully prepared by a traditional solid–state method. Notably, compositions of ANTO0.005 and ANTO0.01 respectively exhibit both low dielectric loss (0.040 and 0.050 at 1 kHz), high dielectric permittivity (9.2 × 10³ and 1.6 × 10⁴ at 1 kHz), and good thermal stability, which satisfy the requirements for the temperature range of application of X9R and X8R ceramic capacitors, respectively. The origin of the dielectric behavior was attributed to five dielectric relaxation phenomena, i.e., localized carriers' hopping, electron–pinned defect–dipoles, interfacial polarization, and oxygen vacancies ionization and diffusion, as suggested by dielectric temperature spectra and valence state analysis via XPS; wherein, electron-pinned defect–dipoles and internal barrier layer capacitance are believed to be the main causes for the giant dielectric permittivity in ANTOx ceramics.     

电网设备线夹开裂原因

某电力公司变电站用铝合金设备线夹在运行过程发生批次开裂事故,通过宏观观察、断口分析、化学成分分析、力学性能测试、冷冻模拟试验等方法,对设备线夹的开裂原因和开裂机理进行了分析。结果表明:设备线夹焊缝存在焊接缺陷,导致焊缝强度下降;设备线夹接线管底部存在积水空间,寒冷天气下积水结冰,体积膨胀,使焊缝承受设计工况外的负载而过载开裂,造成了线夹开裂。     

基于改进相干增强扩散与纹理能量测度和高斯混合模型的导光板表面缺陷检测方法

针对液晶屏(LCD)导光板表面缺陷检测方法存在漏检率和误检率较高,对产品表面复杂渐变的纹理结构适应性差的问题,提出一种基于改进相干增强扩散(ICED)与纹理能量测度和高斯混合模型(TEM-GMM)的LCD导光板表面缺陷检测方法。首先,构建ICED模型,基于结构张量引入平均曲率流扩散(MCF)滤波,使得相干增强扩散(CED)模型对缺陷的细线状纹理有良好的边缘保持效果,并利用相干性得到缺陷纹理增强和背景纹理抑制的滤波后图像;然后,根据Laws纹理能量测度(TEM)提取图像纹理特征,将图像的背景纹理特征作为离线阶段高斯混合模型(GMM)的训练数据,使用期望最大化(EM)算法估计GMM参数;最后,计算待检测图像各像素的后验概率,并将其作为在线检测阶段缺陷像素的判断依据。实验结果表明,该检测方法在导光颗粒随机、规则两种分布的缺陷图像测试数据组上的漏检率和误检率分别为3.27%、4.32%和3.59%、4.87%。所提检测方法适用范围广,可有效检测出LCD导光板表面划痕、异物、脏污和压伤等类型的缺陷。     

大直径埋地管道应力应变有限元分析与计算

利用通用分析软件ABAQUS，应用“生死单元” 技术，模拟了基坑开挖、填埋过程对Φ1 620 mm×20 mm大直径埋地管线应力应变的影响。通过对不同埋深管体应力应变的有限元分析，得出施加内压2.5 MPa，埋深8 m时，管体受到的等效应力最大（130 MPa），未超过材料的屈服强度，管体并未发生塑性变形，管体横向最大位移为2.47 mm。通过理论计算校核，埋深8 m时，管体水平方面最大变形量为12.5 mm，远小于标准规定的48.6 mm，管体径向稳定性可靠。     

某X65钢级输气管道环焊缝泄漏失效分析

针对某X65输气管道环焊缝泄漏失效问题，通过无损探伤、硬度试验、金相组织分析、扫描电镜分析等方法，对钢管环焊缝进行了分析研究。分析结果显示，焊接接头组织未见明显异常，但裂纹附近存在疏松组织，该疏松组织主要元素为铁和氧，以及少量铝、硅、钙、硫元素。研究表明，该疏松组织为焊接时未清理干净的焊渣，在外力和内压作用下，夹渣处裂纹相互贯穿形成穿透性裂纹，裂纹由内表面向外表面扩展，导致焊缝产生开裂而发生泄漏。     

Up-pulling force analysis for ESC hollow cylindrical casting

Electroslag casting(ESC)is an important method to produce high quality castings.In this study,the ESC up-pulling inner mold method(EUPIM)was used to produce hollow cylindrical castings with the multiple consumable electrodes.The radial deformation,the axial and radial internal stress of the inner mold,and the axial internal stress of the slag shell were analyzed using the finite element method(FEM)with the aid of ANSYS software.The ProCAST software was used to calculate the specific heat,heat conductivity and density curve of Cu.Simulation results show that the radial deformation,the axial and radial internal stress of the inner mold,and the axial internal stress of the slag shell near the slag-metal interface of hollow cylndrical casting gradually increase from 0 s to 360 s after the ESC starting(slagging)process but before applying the up-pulling force.The suitable initial up-pulling moment of the inner mold is at around 180-198 s after the starting process.     

微间隙共形圆柱接触力模型的适用性分析

针对目前间隙铰接副接触力模型无法有效表述不同材料耗散阻尼效应,以及不适用于微间隙共形接触的问题,分析各种接触力模型中弹性接触力和耗散阻尼力计算方法的优缺点,提出一种普适性的圆柱内接触力分析模型。该模型将接触力描述为接触深度的显式函数,并将其适用范围有效地扩展至微间隙和低恢复系数工况。采用含间隙铰接副的曲柄-滑块机构进行动力学分析,对所提出接触力进行验证,计算结果表明:所提出的普适性接触力模型体现了微间隙时更高的接触刚度和低恢复系数时显著的阻尼效应,从而可为不同材料和间隙尺寸的间隙铰接副力学分析提供更为完备的计算模型。