Facile synthesis of Ti3C2 MXene-modified Bi2.15WO6 nanosheets with enhanced reactivity for photocatalytic reduction of Cr(VI)

Through a facile hydrothermal method, we have successfully prepared Ti₃C₂/Bi_2.15WO₆ (TC/BWO) composite, and systematically investigated their reactivity for the photocatalytic reduction of Cr(VI) under visible light. X-ray diffraction and Raman analysis confirm the formation of heterostructure between Bi_2.15WO₆ and Ti₃C₂. The resultant 7TC/BWO composite exhibits enhanced photoactivity toward Cr(VI) reduction. After 120 min irradiation, the conversion of Cr(VI) reaches 92.5% with the quasi-first-order kinetic constant of k = 0.0145 min^?1, which is higher than that of pure BWO (30% and k = 0.0005 min^?1). The electrochemical and photoluminescent characterization confirm that the introduction of Ti₃C₂ is conducive to the separation of carriers, thus significantly improves the photocatalytic performance of TC/BWO. Furthermore, the radical capture experiments verify that the electrons are important for enhancing reduction of Cr(VI) to Cr(III). As a result, this research provides a comprehensive understanding of the reduction of Cr(VI) by TC/BWO composite under visible light.     

Far-red-emitting YAl3(BO3)4:Cr3+ phosphors with excellent thermal stability and high luminescent yield for plant growth LEDs

Phosphors-converted LEDs (pc-LEDs) are excellent artificial light sources for indoor plant cultivation, in which the far-red-emitting component (700−780 nm) plays an important role in regulating the photomorphogenesis of plants. Accordingly, highly efficient and thermally stable far-red-emitting phosphors are indispensable for developing high-performance plant cultivation pc-LEDs. Herein, far-red-emitting YAl₃(BO₃)₄:Cr³⁺ (YAB:Cr³⁺) phosphors were synthesized by solid-state reaction, and their photoluminescence characteristics, thermal quenching, quantum yield (QY), and application in pc-LEDs were systematically investigated. The YAB:Cr³⁺ phosphor has an intense broadband absorption to the blue light, simultaneously exhibiting the sharp-line ²E emission and the broadband ⁴ T₂ emission of Cr³⁺ with a QY of ~86.7%. The far-red broadband emissions of YAB:Cr³⁺ centered at ~735 nm show a high resemblance to the active-state (P_FR) absorption of plant phytochrome. Moreover, the YAB:Cr³⁺ phosphor shows the thermally enhanced luminescence at temperatures of 303−393 K and the near-zero thermal quenching up to 423 K. The anomalous thermal enhancement is attributed to the temperature-dependent repopulation between ²E and ⁴ T₂ states. Finally, a pc-LED device was fabricated with the YAB:Cr³⁺ phosphor and blue chip, exhibiting the light out power of ~50.6 mW and energy conversion efficiency of ~17.4% at 100 mA drive current, respectively. The exceptional PL features including suitable excitation/emission wavelengths, suppressed thermal quenching and high QY make YAB:Cr³⁺ phosphors very promising for applications in plant growth pc-LEDs.     

The structure,vacancy characteristics,and magnetic properties of GdMn1-xCrxO3 ceramics

To investigate the evolution of the structural and enhanced magnetic properties of GdMnO₃ systems induced by the substitution of Mn with Cr, polycrystalline GdMn_1-xCr_xO₃ samples were synthesized via solid-state reactions. XRD characterization shows that all GdMn_1-xCr_xO₃ compounds with single-phase structures crystallize well and that Cr³⁺ ions entering the lattice sites of GdMnO₃ induce structural distortion. SEM results indicate that the grain size of the synthesized samples (a few microns) decreases as the Cr substitution concentration increases. Positron annihilation lifetime spectroscopy reveals that vacancy-type defects occur in GdMn_1-xCr_xO₃ ceramics and that the vacancy size and concentration clearly change with the Cr content. The temperature and field dependence of the magnetization curves show that Cr substitution significantly influences the magnetic ordering of the gadolinium sublattice, improving the weak ferromagnetic transition temperature and magnetization of GdMn_1-xCr_xO₃. The enhanced magnetization of GdMn_1-xCr_xO₃ is closely related to the vacancy defect concentration.     

Microstructure and some properties of powder-pack borided Ti–5Mo–5V–8Cr–3Al alloy with special attention to the microstructure at the interface TiB/substrate

The borided layer was prepared on the surface of the Ti–5Mo–5V–8Cr–3Al alloy by powder-pack boriding at 1000°C-10h. SEM, EPMA and TEM were used to investigate the effects of alloying elements (Al, V, Mo and Cr) on the growth of TiB whiskers in the borided Ti–5Mo–5V–8Cr–3Al alloy. Wear properties of borided Ti–5Mo–5V–8Cr–3Al alloy were investigated using dry reciprocating friction tests. SEM results show that the thickness of boride layer in Ti–5Mo–5V–8Cr–3Al alloy is thinner than that in the Cp-Ti. This is attributed to the enrichment of alloying elements especially V in TiB/substrate by TEM, which hinders the diffusion of B atoms, thus resulting in the short and thick TiB whiskers in Ti–5Mo–5V–8Cr–3Al alloy. Borided Ti–5Mo–5V–8Cr–3Al alloy has the better wear resistance than as-received alloy.     

咖啡渣活性炭的制备、表征及其对Cr(Ⅵ)的吸附机制研究

以碘吸附值为评价指标，活化时间、活化温度和浸渍比为影响因素，采用响应面法试验设计对磷酸活化法制备咖啡渣活性炭的工艺条件进行优化，并通过静态吸附试验研究了不同吸附时间、溶液pH值和吸附温度条件下，活性炭对水溶液中Cr（Ⅵ）吸附性能的影响，最后利用Langmuir、Freundlich吸附等温方程、准一级动力学方程、准二级动力学方程和颗粒内部扩散方程进行拟合。试验结果表明，制备咖啡渣活性炭的最佳工艺条件为活化时间1 h、活化温度498℃、浸渍比1.72；在此条件下活性炭得率为30.4%，碘吸附值为（799±16）mg/g，比表面积为1 006 m²/g，孔容为0.779 cm³/g、微孔孔容为0.051 cm³/g、平均孔径为3.088 nm。较低pH值和较高温度能够促进活性炭对Cr（Ⅵ）的吸附；Langmuir等温方程能够更好地描述活性炭对Cr（Ⅵ）的吸附效果；活性炭对Cr（Ⅵ）的吸附分3个阶段：快速吸附阶段、慢速吸附阶段和吸附平衡阶段，10 min内可完成吸附总量的79%，360 min内达到吸附平衡，该吸附过程符合准二级吸附动力学方程。分析表明咖啡渣活性炭对Cr（Ⅵ）的吸附主要为单分子层的化学吸附。     

退火温度对0Cr25Al5热轧态盘条钢组织及性能的影响

采用显微组织分析和分子动力学模拟等方法研究了退火温度对0Cr25Al5热轧态盘条钢组织及性能的影响。结果发现,晶粒尺寸随温度的升高逐渐增加并趋于稳定,但是断后伸长率和断面收缩率在950 ℃突然大幅度下降。试样组织形貌在800 ℃和950 ℃退火温度下的OM及SEM分析结果未见明显差别。于是使用分子动力学模拟对0Cr25Al5钢三元体系的自由能进行了计算,发现随着B2结构的FeAl或者DO3结构的Fe₃Al有序相尺寸的增大,系统自由能先减小后增大,其最小值随着退火温度的升高向有序相颗粒尺寸减小的方向移动。在1273 K的高温下仍然会保留60 nm左右大小的有序相颗粒。因此,推测0Cr25Al5钢在大于950 ℃的温度范围内韧性下降是由于60 nm左右的B2结构的FeAl或者DO3结构的Fe₃Al有序相造成,与晶粒尺寸无关。因此,针对该钢种应进行低温退火促使基体组织回复以消除缺陷,从而抑制Fe、Al等基体原子的扩散。     

Hit to Leads with Cytotoxic Effect in Leukemic Cells: Total Synthesis Intermediates as a Molecule Treasure Chest

A previously designed and developed 12-step total synthesis that includes [1,1′-biphenyl]-2-amine and carbazole intermediates and that ultimately produces the carbazole alkaloid carbazomycin G was exploited as a screening compound library with the goal of identifying potential lead compound(s) with cytotoxic effect. These compounds were investigated by using in-vitro tests involving the two human cell lines HL-60 and MOLM-13, which both model acute myeloid leukaemia (AML). The in-vitro biological test results were used together with the molecular structures of the various intermediates in a concise SAR analysis. Several of the intermediates revealed cytotoxicity (IC₅₀<10⁻⁴ M), although the final natural product carbazomycin G did not reveal cytotoxicity versus the two said human cell lines.     

基于双应力加速寿命试验的关节轴承寿命预测与可靠性分析

自润滑关节轴承寿命主要是由衬垫的磨损性能决定的,但衬垫的磨损一般是非线性的,使得寿命难以预测。采用同时改变载荷和摆频2种应力的方法进行加速寿命试验,建立以pv值、磨损量退化数据为输入参数,寿命值为输出参数的灰色神经网络预测模型。经验证该预测模型对关节轴承寿命预测的最大误差仅为7.33%,平均误差仅为3.892%。对不同加速应力下自润滑关节轴承可靠性进行评估,结果表明,关节轴承的可靠性在L_(10)(可靠度为90%时的寿命)之前下降趋势缓慢,然后迅速下降,pv值越大可靠性下降越迅速;随着pv值的增大,关节轴承寿命近似呈指数下降,经验证可用逆幂率加速模型反映二者关系。     

伞帽用高铬铸铁在热强碱腐蚀环境下的磨损分析

针对氧化铝行业中常用的Cr28和Cr20高铬铸铁伞帽在相同工况条件下的磨损机理进行分析,并对比研究了实际生产中两种失效材料的成分、组织及性能。结果表明,伞帽部件在高温强碱腐蚀条件下受到外界冲刷时,磨损量由微切削磨损与变形磨损这两种机制共同决定。含铬量较高的Cr28高铬铸铁,其冲刷和抗腐蚀磨损性能均优于Cr20高铬铸铁。伞帽服役寿命主要受浆料和表层的铸铁材料两大因素影响。两种试验材料经淬火+回火处理后,基体组织中主要为回火马氏体+M₇C₃型碳化物+少量残留奥氏体,其中含铬量较高的Cr28高铬铸铁中共晶碳化物含量更高,且分布更加弥散,其平均硬度值为64.0 HRC,高于Cr20高铬铸铁的60.2 HRC。最终确定Cr28高铬铸铁作为伞帽材质更能满足氧化铝生产及设备检修周期的需要。     

Simultaneous degradation of RhB and reduction of Cr(VI) by MIL-53(Fe)/Polyaniline (PANI) with the mediation of organic acid

MIL-53(Fe)/polyaniline (PANI) composite was prepared by in situ depositing PANI on the surface of MIL-53(Fe) and their catalytic performances on the simultaneous removal of RhB and Cr(VI) were investigated. The elimination efficiency of both RhB and Cr(VI) reached more than 98% under pH=2 where hydrochloric acid and citric acid were used to adjust the pH. The results indicated that MIL-53(Fe)/PANI revealed an obvious pH response to the degradation of RhB, while citric acid promoted the Cr(VI) photoreduction. UV-Vis spectra, EIS, and photocurrent response experiments showed that MIL-53(Fe)/PANI had a better light response and carrier migration ability than MIL-53(Fe). The transient absorption spectra also exhibited that the lifetimes of photo-generated carriers were prolonged after the conductive polymer deposition on the MIL-53(Fe) surface. Scavenger experiments demonstrated that the main active species were ·O₂^- and OH. Combined with activity evaluation results, and the possible photocatalytic mechanism of MIL-53(Fe)/PANI on RhB oxidation and Cr(VI) reduction was proposed. The addition of conductive polymer can effectively improve the light response of the catalyst under acidic conditions, and meanwhile citric acid also provided a new mediation for the synergistic degradation of multiple pollutants. Good activity and stability of the catalysts made the scale-up purification of acid water feasible under UV-Vis light.