Densification mechanism and microstructure characteristics of nano- and micro- crystalline alumina by high-pressure and low temperature sintering

Fully dense ceramics with retarded grain growth can be attained effectively at relatively low temperatures using a high-pressure sintering method. However, there is a paucity of in-depth research on the densification mechanism, grain growth process, grain boundary characterization, and residual stress. Using a strong, reliable die made from a carbon-fiber-reinforced carbon (C_f/C) composite for spark plasma sintering, two kinds of commercially pure α-Al₂O₃ powders, with average particle sizes of 220 nm and 3 μm, were sintered at relatively low temperatures and under high pressures of up to 200 MPa. The sintering densification temperature and the starting threshold temperature of grain growth (T_sg) were determined by the applied pressure and the surface energy relative to grain size, as they were both observed to increase with grain size and to decrease with applied pressure. Densification with limited grain coarsening occurred under an applied pressure of 200 MPa at 1050 °C for the 220 nm Al₂O₃ powder and 1400 °C for the 3 μm Al₂O₃ powder. The grain boundary energy, residual stress, and dislocation density of the ceramics sintered under high pressure and low temperature were higher than those of the samples sintered without additional pressure. Plastic deformation occurring at the contact area of the adjacent particles was proved to be the dominant mechanism for sintering under high pressure, and a mathematical model based on the plasticity mechanics and close packing of equal spheres was established. Based on the mathematical model, the predicted relative density of an Al₂O₃ compact can reach ～80 % via the plastic deformation mechanism, which fits well with experimental observations. The densification kinetics were investigated from the sintering parameters, i.e., the holding temperature, dwell time, and applied pressure. Diffusion, grain boundary sliding, and dislocation motion were assistant mechanisms in the final stage of sintering, as indicated by the stress exponent and the microstructural evolution. During the sintering of the 220 nm alumina at 1125 °C and 100 MPa, the deformation tends to increase defects and vacancies generation, both of which accelerate lattice diffusion and thus enhance grain growth.     

Effects of Different Short-Term UV-B Radiation Intensities on Metabolic Characteristics of Porphyra haitanensis

The effects of ultraviolet (UV) radiation, particularly UV-B on algae, have become an important issue as human-caused depletion of the protecting ozone layer has been reported. In this study, the effects of different short-term UV-B radiation on the growth, physiology, and metabolism of Porphyra haitanensis were examined. The growth of P. haitanensis decreased, and the bleaching phenomenon occurred in the thalli. The contents of total amino acids, soluble sugar, total protein, and mycosporine-like amino acids (MAAs) increased under different UV-B radiation intensities. The metabolic profiles of P. haitanensis differed between the control and UV-B radiation-treated groups. Most of the differential metabolites in P. haitanensis were significantly upregulated under UV-B exposure. Short-term enhanced UV-B irradiation significantly affected amino acid metabolism, carbohydrate metabolism, glutathione metabolism, and phenylpropane biosynthesis. The contents of phenylalanine, tyrosine, threonine, and serine were increased, suggesting that amino acid metabolism can promote the synthesis of UV-absorbing substances (such as phenols and MAAs) by providing precursor substances. The contents of sucrose, D-glucose-6-phosphate, and beta-D-fructose-6-phosphate were increased, suggesting that carbohydrate metabolism contributes to maintain energy supply for metabolic activity in response to UV-B exposure. Meanwhile, dehydroascorbic acid (DHA) was also significantly upregulated, denoting effective activation of the antioxidant system. To some extent, these results provide metabolic insights into the adaptive response mechanism of P. haitanensis to short-term enhanced UV-B radiation.     

Highly oriented α-Al2O3 transparent ceramics shaped by shear force

Alumina platelets were arranged horizontally in submicron alumina particles by shear force in the flow of slurries during casting. The obtained alumina green bodies with platelets were pressureless-sintered in vacuum, producing ceramics with thoroughly oriented grains and high transmittance. The effects of sintering parameters on the densification, microstructure evolution, and orientation degree of alumina ceramics were investigated and discussed. The results showed that the densification, grain size, orientation degree, and in-line transmittance were increased with increasing sintering temperature. The enhancement of orientation degree was mainly coherent with grain growth. The grain-oriented samples exhibited a much higher in-line transmittance (at 600 nm) of 61 % than that of the grain random sample (29 %). Moreover, the transmission remained a high level in the ultraviolet range (<300 nm).     

Bi-templated grain growth maximizing the effects of texture on piezoelectricity

Templated grain growth is beneficial for piezoelectric materials, the properties of which become the best in their single crystalline form. Nevertheless, a textured ceramic prepared by a templated grain growth technique often fails in exhibiting as good properties as expected in single crystals even with a high degree of orientation factor. Here, we propose a new strategy for maximizing texturing effect by suppressing the growth of untextured matrix grains. The textured ceramics made by our method, so-called bi-templated grain growth, are featured by ultrahigh piezoelectric properties (d₃₃ = ～1,031 pC/N, d?g = ～59,000, k_p = ～0.76). A special emphasis is on the achieved electric-field-induced strain of 0.13 % at 1 kV/mm, which is as high as that of single crystals. This work demonstrates that not only the degree of texture but also the coarsening of untextured matrix grains should be well-controlled to best exploit the templated grain growth technique.     

Epitaxial Growth of 2D Materials on High-Index Substrate Surfaces

Recently, the successful synthesis of wafer-scale single-crystal graphene, hexagonal boron nitride (hBN), and MoS₂ on transition metal surfaces with step edges boosted the research interests in synthesizing wafer-scale 2D single crystals on high-index substrate surfaces. Here, using hBN growth on high-index Cu surfaces as an example, a systematic theoretical study to understand the epitaxial growth of 2D materials on various high-index surfaces is performed. It is revealed that hBN orientation on a high-index surface is highly dependent on the alignment of the step edges of the surface as well as the surface roughness. On an ideal high-index surface, well-aligned hBN islands can be easily achieved, whereas curved step edges on a rough surface can lead to the alignment of hBN along with different directions. This study shows that high-index surfaces with a large step density are robust for templating the epitaxial growth of 2D single crystals due to their large tolerance for surface roughness and provides a general guideline for the epitaxial growth of various 2D single crystals.     

A thermal perspective of flash sintering: The effect of AC current ramp rate on microstructure evolution

In flash sintering experiments, the thermal history of the sample is key to understanding the mechanisms underlying densification rate and final properties. By combining robust temperature measurements with current-ramp-rate control, this study examined the effects of the thermal profile on the flash sintering of yttria-stabilized zirconia, with experiments ranging from a few seconds to several hours. The final density was maximized at slower heating rates, although processes slower than a certain threshold led to grain growth. The amount of grain growth observed was comparable to a similar conventional thermal process. The bulk electrical conductivity correlated with the maximum temperature and cooling rate. The only property that exhibited behavior that could not be attributed to solely the thermal profile was the grain boundary conductivity, which was consistently higher than conventional in flash sintered samples. These results suggest that, during flash sintering, athermal electric field effects are relegated to the grain boundary.     

Biocompatibility and electron microscopy studies of epitaxial nanolaminate (Al0·5Ti0.5)N/ZrN coatings deposited by Arc-PVD technique

The ability to combine layers with high mechanical strength and additional physicochemical properties, such as biocompatibility, makes the use of multilayer coatings attractive for various applications. The transition from single layer to nanolaminate architecture can improve the mechanical performance of the coatings by increasing the number of interfaces and decreasing the modulation period of the layers. The microstructural study of the nanolaminate (Al_0·5Ti_0.5)N/ZrN coating with a modulation period λ of ≃ 20 nm was carried out using the TEM-HRTEM method. It was found that the coatings of (Al_0·5Ti_0.5)N/ZrN series consisted of two phases: the fcc-(Ti,Al)N solid solution obtained by isomorphic substitution of Ti atoms with Al ones in the TiN crystal lattice and the cubic ZrN phase. ZrN layers had a high texture structure with [111]-preferred growth texture and made a dominant effect on the nucleation and growth of (Al_0·5Ti_0.5)N layers. The epitaxial growth process was the most pronounced for fcc-(Ti,Al)N (111)||fcc-(ZrN) (111) and fcc-(Ti,Al)N (200)||fcc-(ZrN) (200) grains. Finally, the new coating demonstrated high biocompatibility, failure to toxicity and supported U2OS osteogenic cells proliferation within 7 days of cultivation.     

地表径流速度对城市内涝影响规律

为分析地表径流速度对城市内涝的影响,采用一维地下排水管网与二维城区地形的动态耦合模型,选取大连市某排水区块作为研究区域,设置4种地表径流速度10种设计降雨场景,模拟分析在不同重现期设计降雨及不同地表径流速度下研究区的内涝积水特性。结果表明:随着地表径流速度降低,管道排水压力变小,管道排水达标率最高可提升48.05%,且降雨重现期越短,地表径流流速对管道排水压力的削减效果越明显;地表径流流速对检查井溢流量影响显著,随着地表径流速度降低,检查井溢流量峰值最高可减小2 750 m~3,峰现时间最长可滞后56 min,同时随着降雨重现期增长,地表径流流速对检查井溢流量的削减效果减弱;研究区低、高风险区淹没面积随地表径流速度降低,最高可分别减小1.64万、8.37万m~2,但中风险区淹没面积变化反复。     

Nitrogen-doped cobalt sulfide as an efficient electrocatalyst for hydrogen evolution reaction in alkaline and acidic media

The enhancement in intrinsic catalytic activity and material conductivity of an electrocatalyst can leads to promoting HER activity. Herein, a successful nitrogenation of CoS₂ (N–CoS₂) catalyst has been investigated through the facile hydrothermal process followed by N₂ annealing treatment. An optimized N–CoS₂ catalyst reveals an outstanding hydrogen evolution reaction (HER) performance in alkaline as well as acidic electrolyte media, exhibiting an infinitesimal overpotential of ?0.137 and ?0.097 V at a current density of ?10 mA/cm² (?0.309 and ?0.275 V at ?300 mA/cm²), corresponding respectively, with a modest Tafel slope of 117 and 101 mV/dec. Moreover, a static voltage response was observed at low and high current rates (?10 to ?100 mA/cm²) along with an excellent endurance up to 50 h even at ?100 mA/cm². The excellent catalytic HER performance is ascribed to improved electronic conductivity and enhanced electrochemically active sites, which is aroused from the synergy and mutual interaction between heteroatoms that might have varied the surface chemistry of an active catalyst.