Synthesis and characterization of functional gradient copolymers of glycidyl methacrylate and butyl acrylate

Epoxy-functional spontaneous gradient copolymers of glycidyl methacrylate (G) and n-butyl acrylate (B) were synthesized via atom transfer radical polymerization (ATRP). The copolymerization reactions were carried out in toluene solution at 70 °C, using methyl 2-bromopropionate (MBrP) as initiator and copper chloride with N,N,N′,N′′,N′′-pentamethyldiethylenetriamine (PMDETA) as the catalyst system. The kinetic behaviour of the statistical copolymerizations was studied in a wide composition interval with molar fractions of G ranging from 0.10 to 0.75. The synthesized copolymers were characterized by size exclusion chromatography (SEC) and nuclear magnetic resonance (NMR) spectroscopy. ¹H NMR was employed to determine the copolymer composition, demonstrating the gradient character of the copolymers along the main chain in the whole monomer conversion interval. Apart from this, the sequence distribution and stereoregularity were analyzed. These microstructural experimental data agreed well with those calculated from Mayo-Lewis terminal model (MLTM) and a Bernoullian statistic with an isotacticity parameter of σ_G = 0.28 and a coisotacticity parameter of σ = 0.30.     

丙烯酸高碳醇酯的合成

介绍了降凝剂中间体丙烯酸高碳醇酯的合成和产品分离提纯方法。考察了合成条件对酯化反应的影响，结果表明，在原料丙烯酸与十八醇摩尔比1．2：1，阻聚剂对苯二酚用量占原料总量1．5％，催化剂对甲苯磺酸用量占原料总量1．5％，反应温度80-86℃，回流反应时间6h条件下，酯化率最高达89％。产品分离提纯方法与传统分离方法比较，所需分离时间短，洗涤用水量少，而产品收率远高于传统分离方法，达95％以上。     

丙烯酸酯与甲基丙烯酸酯的共聚及性能研究

采用悬浮聚合法，以丙烯酸－２－乙基－己酯与甲基丙烯酸十二酯为单体，合成了共聚型高吸油性树脂。研究了共聚单体的配比、交联剂用量、引发剂用量诸因素对高吸油性树脂的性能影响。制得的树脂可以吸其自身质量的１１．８倍的煤油、１４．７倍的苯、６．５倍的泵油。     

Studies on cross-linked polyurethane acrylate-based electrolyte consisting of reactive vinyl/divinyl diluents

A series of cross-linked polyurethane acrylate (PUA) electrolytes have been prepared by using 4,4′-methylene bis(phenyl isocyanate), polyethylene glycol, hydroxyethyl methacrylate and different reactive vinyl/divinyl diluents, such as methyl methacrylate (MMA), ethyl acrylate and acrylonitrile, tripropylene glycol diacrylate (TPGDA). The electrolytes were prepared by UV radiation induced cross-linking of the PUA-diluent mixture followed by swelling in a liquid electrolyte (LP-30). Depending upon the composition of the components, these electrolytes exhibited a wide range of mechanical and electrical properties. The system containing MMA as reactive diluent showed highest conductivity, but poor mechanical properties and stability in the liquid electrolyte. The TPGDA cross-linked system possesses a good combination of ionic conductivity and stability in liquid electrolytes. These systems showed good compatibility with Li-electrodes and sufficient electrochemical stability to allow safe operation in rechargeable Li-batteries.     

有机纤维材料用软膜乳液阻燃剂的制备

采用甲醛、尿素、三聚氰胺、脒基脲磷酸盐为原料,以硼砂、硼酸、氨水为pH调节剂合成了保护胶;在保护胶存在下,以预乳化的丙烯酸酯混合单体于82-88℃共聚合成乳液,将其涂布于有机纤维材料,干燥后得软膜透明阻燃涂层。用其处理的涤棉布阻燃性能为:损毁长度68mm、续燃时间1s、阴燃时间3s、氧指数62、吸附干量287g/kg,处理的纸板的阻燃性能为:平均炭化长度77mm、平均续焰时间2s、平均续灼燃时间32s、吸附干量283g/kg。     

有机硅丙烯酸酯增深剂的制备及应用

由乙烯基三乙氧基硅烷与KH-550、丙烯酸酯类单体在阴/非离子表面活性剂存在下，通过乳液聚合制得带蓝光的半透明有机硅丙烯酸酯乳液．该乳液粘度小，有机硅质量分数15％，总固体质量分数30％，该增深剂既可单独使用，也可与氨基硅油乳液复配，经蓝色16电力纺、黑色03双绉等真丝产品增深，其增深度可达15％，但亲水性有所下降．     

硫磷化丙烯酸酯的合成及应用

以硫磷化合物和丙烯酸酯为原料，合成了硫磷化丙烯酸酯极压抗磨剂，该剂具有良好的热氧化安定性，水解安定性及抗乳化性能。用该剂复配抗氧剂，金属钝化剂，防锈剂及其它抗磨剂所调制的复合剂应用于32^#HM抗磨液压油中模拟数据全部达到标准要求指标。     

UV-固化光纤色标油墨

报导了一类新型的化学功能材料———ＵＶ固化光纤色标油墨。该材料由可ＵＶ固化的有机硅环氧安息香酸丙烯酸酯（ＳＥＢＡ）和脂环族环氧丙烯酸酯（ＡＣＥＡ）两种光敏预聚物为基料，以自行合成的光敏染料———分散红氨基甲酸酯丙烯酸酯（ＲＵＡ）、分散蓝氨基甲酸酯丙烯酸酯（ＢＵＡ）和吖啶黄氨基甲酸酯丙烯酸酯（ＹＵＡ）为着色剂，加入必要的添加剂配制而成的ＵＶ固化光纤色标油墨。该色标油墨已在光纤生产中得到应用。