噻吩在镍基非晶态合金上的吸附和脱附

应用静态吸附、动态吸附、程序升温脱附和程序升温还原等实验方法，考察了噻吩在Ni基非晶态合金上的吸附和脱附行为。常温下，噻吩分子首先吸附在清洁的Ni表面，并立刻被活化，发生氢解反应，C-S键断裂，释放出烃类部分，S留在Ni原子上。噻吩可以在Ni基非晶态合金表面发生强度不同的化学吸附。弱化学吸附的噻吩可以脱附；强化学吸附的噻吩不会脱附，而在高温下发生氢解反应。     

Performance and Commercial Application of the Promoter LCC-A for Maximization of Propylene Yield

1 Introduction Propylene as an important feedstock for organic chemicals is mainly originated from steam cracking and catalytic cracking processes. During the FCC process the propylene content varies with the FCC catalyst and process technology adopted, resulting in significant difference in propylene concentration in the cracked product——LPG. The conventional FCC pro- cess generally gives a propylene yield of around 4%, while the FCC process with maximization of propylene yield can in…     

Cu基络合物催化甲醇液相氧化羰化反应

针对甲醇液相氧化羰基化法合成碳酸二甲酯(DMC)工艺,开发了新型Cu基络合催化剂(CuB rnLm)。对CuB rnLm催化剂的活性及其稳定性进行了研究。实验结果表明,采用该催化剂,甲醇转化率和DMC选择性较高;元素价态和物质结构分析表明,CuB rnLm催化剂循环使用5次后仍保持较好的稳定性。采用正交设计和中心响应曲面法设计实验,并使用S tatistica软件进行统计分析,寻求出反应的主要影响因素,并得到优化的工艺条件:反应温度100~110℃、反应压力3.0~3.5M Pa、反应时间4~6h、CuB rnLm催化剂质量浓度(以甲醇的体积计)0.15~0.20g/mL。在此工艺条件下,甲醇转化率可达23%以上,DMC的选择性为96%~98%。     

新型高K栅介质ZrO2薄膜材料的制备及表征

采用超高真空电子束蒸发法制备了新型高 K栅介质-非晶 ZrO2薄膜. X射线光电子能谱 (XPS) 中 Zr3d5/2 和 Zr3d3/2 对应的结合能分别为 182.1eV和 184.3eV, Zr元素的主要存在形式为 Zr4+,说明薄膜由完全氧化的 ZrO2组成 ,并且纵向分布均一.扩展电阻法( SRP)显示 ZrO2薄膜的 电阻率在 108Ω@ cm以上,通过高分辨率透射电镜( HR- XTEM)可以观察 ZrO2/Si界面陡直,没有 界面反应产物 ,证明 600℃快速退火后 ZrO2薄膜是非晶结构.原子力显微镜( AFM)表征了薄膜的 表面粗糙度,所有样品表面都很平整,其中 600℃快速退火样品 (RTA)的 RMS为 0.480nm.     

井下乳化/水热催化裂解复合降黏开采稠油技术研究

实验考察了胜利孤东稠油井下催化水热裂解和乳化/催化水热裂解降黏效果。所用催化剂为水溶性铁镍钒体系,Fe3+∶Ni2+∶VO4+=5∶1∶1,100 g稠油与30 g 0.5%催化剂水溶液在240℃反应24小时。原始黏度(50℃)11.0和8.36 Pa.s的两种稠油裂解并静置除水后,黏度降低76.2%和75.6%,室温放置60天后降黏率下降小于3个百分点,气相色谱显示裂解后轻组分明显增加,红外光谱显示稠油组分发生脱羧反应且芳环数减少。讨论了稠油催化水热裂解反应机理。所用化学助剂JN-A在油水中均可溶,耐温达250℃,耐矿化度达50 g/L,其水溶液以30∶100的质量比与稠油混合时形成低黏度的O/W乳状液。当水相含1.0%JN-A和0.5%催化剂时,两种稠油水热裂解后的反应混合物为O/W乳状液,黏度仅为319和309 mPa.s,静置除水后的稠油降黏率增加到86.5%和87.3%,其中的轻组分含量进一步增加。该井下乳化/催化水热裂解复合降黏法成功地用于孤东两口蒸汽吞吐井,稠油井作业后初期采出的原油黏度由~9 Pa.s降低到1 Pa.s左右,随采油时间延长而逐渐升高,约50天后超过4Pa.s。图2表6参5。     

Effect of oxygenation on electrocatalysis of La0.6Ca0.4CoO3−x in bifunctional air electrode

A vacuum-annealed La_0.6Ca_0.4CoO_3−x was consecutively oxygenated in air at temperatures decreasing from 800 to 100 °C, and its electrocatalytic activities for oxygen reduction and evolution were then measured as a function of the oxygenation temperature. The valence of Co cation, changing between +2 and +3, was found susceptible to annealing either in vacuum or air. The catalytic activities initially decrease monotonically as the oxygenation temperature was decreased from 800 to 300 °C, as a result of increasing oxygen content, and then rise abruptly with the oxygen reduction activity reaching a maximum at 200 °C and the oxidation activity at 150 °C. X-ray photoelectron spectroscopy analysis indicated that the enhancements by the low-temperature oxygenation involved increased OH coverage and less charged cations at surface. The results clearly reveal the importance of the post-calcination annealing process for optimizing the performance of La_0.6Ca_0.4CoO_3−x in air electrode applications.     

大块非晶合金的性能、制备及应用

综述了大块非晶合金的性能、制备方法及应用，对比了吸铸法制备的棒状Zr41.2Ti13.8Cu12.5Ni10Be22.5,Zr57Cu20Al10Ni8Ti5,Zr52.5Ti5Cu17.9Ni14.6Al10(原子分数)大块非晶样品的过冷温度区间宽度(△Tx)，给出了3种大块非晶合金系列的热稳定性参数Tg、Tx及△Tx，提出了大块非晶合金领域存在的问题及发展方向．     

一种制氢预转化催化剂还原的新方法

对上海高桥分公司2×10~4m~3/h(标准状态)制氢装置原设计的预转化催化剂还原流程进行了改进。先跳开预转化反应器,利用转化炉制取氢气,再用自产的高纯氢气代替重整氢,对预转化催化剂进行单独升温还原,避免了催化剂在还原初期因发生甲烷化反应而超温失活的问题,使催化剂具有更好的活性和稳定性。     

Cd-ZSM-5沸石催化剂的制备、表征和芳构化催化性能

采用离子交换、浸渍和混合三种方法制备镉改性ZSM-5沸石催化剂,考察了改性方法和镉含量对催化剂的表面酸性和Cd状态以及芳构化性能的影响。结果表明,加入镉降低了B酸性,Cd~(2+)与沸石结合形成了L_(1612)酸中心,其生成量取决于改性方法和Cd含量,并与芳构化活性提高有直接关系。     

聚合物载体－稀土金属络合物的研究 ⅩⅢ．聚［苯乙烯－甲基丙烯酸β（甲基亚硫酰基）乙酯］的结构与其稀土金属络合物催化丁二烯聚合的活性

从测得的竞聚率计算了单体链节在聚［苯乙烯－甲基丙烯酸β（甲基亚硫酰基）乙酯］（ＰＳＭ）中的序列分布。苯乙烯（Ｓ）或甲基丙烯酸β（甲基亚硫酰基）乙酯（Ｍ）的长序列的概率随着ＰＳＭ中相应单体含量的增加而增加。对于Ｓ和Ｍ摩尔分数大致相等的ＰＳＭ，单体链节的长序列分布函数值相接近。用与此结构相近的ＰＳＭ合成的稀土金属络合物，其催化活性不佳。在Ｍ短序列分布和Ｓ长序列分布较高的情况下，络合物的催化活性最好。所得聚丁二烯的微观结构与ＰＳＭ中单体单元的分布无关。