Methods and mechanisms for uniformly refining deformed mixed and coarse grains inside a solution-treated Ni-based superalloy by two-stage heat treatment

The uniform refinement mechanisms and methods of deformed mixed and coarse grains inside a solution-treatment Ni-based superalloy during two-stage annealing treatment have been investigated.The two-stage heat treatment experiments include an aging annealing treatment(AT)and a subsequent recrystallization annealing treatment(RT).The object of AT is to precipitate some δ phases and consume part of storage energy to inhibit the grain growth during RT,while the RT is to refine mixed and coarse grains by recrystallization.It can be found that the recrystallization grains will quickly grow up to a large size when the AT time is too low or the RT temperature is too high,while the deformed coarse grains cannot be eliminated when the AT time is too long or the RT temperature is too low.In addition,the mixed microstructure composed of some abnormal coarse recrystallization grains(ACRGs)and a large number of fine grains can be observed in the annealed specimen when the AT time is 3 h and RT tem-perature is 980℃.The phenomenon attributes to the uneven distribution of δ phase resulted from the heterogeneous deformation energy when the AT time is too short.In the regions with a large number of δ phases,the recrystallization nucleation rate is promoted and the growth of grains is limited,which results in fine grains.However,in the regions with few δ phases,the recrystallization grains around grain boundaries can easily grow up,and the new recrystallization nucleus is difficult to form inside grain,which leads to ACRGs.Thus,in order to obtain uniform and fine annealed microstructure,it is a prereq-uisite to precipitate even-distributed δ phase by choosing a suitable AT time,such as 12 h.Moreover,a relative high RT temperature is also needed to promote the recrystallization nucleation around δ phase.The optimal annealing parameters range for uniformly refining mixed crystal can be summarized as:900℃×12 h+990℃×(40-60 min)and 900℃×12 h+1000℃×(10-15 min).     

Sol-gel auto-combustion synthesis of Ba–Sr hexaferrite ceramic powders

We report the mechanism involved in sol-gel auto-combustion synthesis of Ba–Sr-hexaferrite (Ba_1-xSr_xFe₁₂O₁₉; x = 0, 0.25, 0.5, 0.75 and 1, BSFO) ceramic powders through the analysis of the phases evolved during annealing of the as-synthesized powders, along with their structure and morphological studies. The XRD patterns of the as-synthesized samples indicate the formation of barium/strontium monoferrite ((Ba/Sr)Fe₂O₄) and maghemite (γ-Fe₂O₃) phases along with a minute amount of hematite (α-Fe₂O₃) phase. Annealing of these samples facilitates formation of BSFO phase through the solid state reaction between BaFe₂O₄ and γ-Fe₂O₃ phase. Interestingly, after annealing the samples with x = 0, 0.5 and 1, at 1000 °C for 2 h, we observed that phase pure Ba–Sr hexaferrite structure forms, but for samples with x = 0.25 and 0.75, high amount of hematite (α-Fe₂O₃) phase is observed, especially for x = 0.75. The reason associated with this could be the large difference between the ionic radii of Ba²⁺ and Sr²⁺ ions occupying the oxygen site. Furthermore, our study on annealing dependent phase evolution confirms that, this difference in ionic radii forbids the formation of a single phase Ba–Sr hexaferrite. The growth of clear hexagonal-shaped plate-like particles with varied particle sizes was observed for all the samples. The particle size variation may be due to the influence of the ionic radii difference on the sinterability of the samples. Our study provides a better understanding of synthesis mechanism of Ba–Sr hexaferrite samples.     

Ca2+ doping effects on the structural and electrical properties of Na0.5Bi4.5Ti4O15 piezoceramics

Bismuth layer structured Na_0.5Bi_4.5Ti₄O₁₅ (NBT) ferroelectric is one of the most promising materials for potential applications at high temperature. However, it is challenged to achieve a balance between high Curie temperature piezoelectric coefficient and excellent thermal stability for NBT piezoceramics. Here, through chemical modification at the A site of NBT with Ca²⁺, novel (Na_0.5Bi_0.5)_1-xCa_xBi₄Ti₄O₁₅ piezoceramics with excellent properties fabricated by solid state reaction were studied. After doping of Ca²⁺, the Curie temperature T_C increased from 648 °C to 662 °C while the piezoelectric coefficient d₃₃ increased from 14 pC/N to 22 pC/N which can be attributed to the intrinsic contribution of TiO₆ octahedral lattice distortion (tilting and rotation) and the extrinsic contribution of the increased density of domain walls. The composition of (Na_0.5Bi_0.5)_0.95Ca_0.05Bi₄Ti₄O₁₅ ceramics with x = 0.05 has the optimal performance with high T_C of 655 °C, large d₃₃ of 22 pC/N, high electrical resistivity ρ close to 10⁷ Ω cm at 500 °C and especially excellent thermal stability of d₃₃ only about 5% reduction after being annealed at 625 °C. The work effectively reveals the great potential of CNBT-5 ceramics for high-temperature piezoelectric applications.     

考虑区域协调性的城际列车开行方案优化

针对城际列车开行方案没有有效匹配城市轨道交通运能的问题，提出一种考虑区域协调性的城际列车开行方案优化方法。首先，以旅客出行费用最小和铁路运输效益最大为优化目标，考虑城际列车载客能力、出发地目的地（Original Destination，OD）客流需求和通过能力等约束；然后，在此基础上增加运能匹配度的限制，构建了考虑区域协调性的城际列车开行方案多目标非线性规划模型，并设计改进的模拟退火算法求解模型；最后，以广深城际铁路为例并进行两组对比分析。实验结果表明:考虑区域协调性的列车开行方案可以使旅客出行总广义费用降低约4.06%，铁路部门的效益提高约9.58%，旅客和铁路的系统总成本降低约23.27%；与遗传算法相比，改进的模拟退火算法在求解质量与收敛速度上均有较大提高。所提模型和算法可充分兼顾旅客和铁路双方利益，能够为城际列车开行方案优化问题提供有效解决方法。     

罩式退火温度对高强IF钢组织及性能的影响

为研究不同退火温度下高强IF钢的组织性能及织构的变化规律,采用温箱式电阻炉加热模拟罩式退火工艺,研究了不同退火温度下高强IF钢210P1冷轧板力学性能;对不同退火温度钢板的r90进行了统计并对其进行显微组织观察;采用X射线衍射仪及热场发射扫描电镜对不同退火温度的罩式退火成品板进行了织构分析。结果表明,在高强IF钢210P1冷轧板的罩式退火过程中,提高退火温度将使晶粒明显长大。随着退火温度的升高,屈服强度及抗拉强度下降,伸长率升高,n值略有上升,板材横向r值增加较明显,有利织构{111}取向密度增加,不利织构{100}取向密度降低。     

高伸长率冷轧双相钢DP980显微组织及性能

摘要：为了进一步提高冷轧双相钢DP980的强塑性，采用低C-Si-Mn-Nb-Cr成分，通过调整连续退火工艺参数，系统研究了工艺组织性能的关系，利用OM、SEM、EBSD分析了不同退火温度条件下各相的比例、尺寸、形貌、分布，同时利用力学拉伸试验手段研究了连退两相区退火温度对强塑性的影响。结果表明，通过优化调整连续退火工艺，不仅可以在冷轧铁素体和马氏体双相钢的组织上获得少量的残余奥氏体，也能细化再结晶晶粒，最终获得ReL/Rm≤0.5、高伸长率A50≥15%的冷轧DP980，提高强塑性的同时改善了成型性能。     

轧制与退火对T9S钛合金板材组织与性能的影响

研究了轧制变形量及退火温度对T9S钛合金板材显微组织和室温力学性能的影响。结果表明:增加成品轧制变形量,板材组织破碎更充分,退火后形成等轴α相、拉长α相和晶间β相组织形貌,变形流线比较明显,板材室温强度和硬度升高,伸长率降低,弹性模量增加。随着退火温度升高,板材室温强度和硬度逐渐降低,伸长率逐渐提高,横向弹性模量逐渐减小,纵向弹性模量先增加后减小。经(750~790) ℃×45 min空冷退火处理后的板材可以获得较好的强度和塑性的匹配。     

PEDOT:PSS对PEDOT:PSS/Si杂化太阳电池性能影响的研究

聚合物poly(3,4-ethylenedioxythiophene):polystyrene sulfonate(PEDOT:PSS)是一种具有高电导率和良好透过性的p型半导体材料。PEDOT:PSS/Si杂化太阳电池由于具有较低的工艺温度,且工艺简单而具有一定的前景。在这种杂化太阳电池结构中,PEDOT:PSS的光学、电学性质对器件性能有重要影响。分别从PEDOT:PSS退火工艺、溶液二次掺杂(二甲基亚砜)的含量以及PEDOT:PSS薄膜厚度3个方面对薄膜的光、电特性以及器件性能的影响进行研究,并优化相关工艺。根据这些优化的参数,最终得到6.63%的太阳电池转化效率(太阳电池面积为2.25 cm^2)。     

退火温度对新型锆合金薄板带材析出相和织构的影响

采用扫描电镜和超高分辨透射电镜,对具有良好冲制性能的新型锆合金薄板成品带材进行含晶粒、第二相粒子等在内的显微组织研究,并探索真空退火处理条件下温度对带材显微组织的影响。结果显示:新型锆合金薄板成品带材晶粒平均尺寸2.17 μm,存在{0001}<1010>和{0001}<1120>两种织构,大部分晶粒<1120>平行带材RD方向,较少晶粒<1010>平行带材RD方向;第二相粒子分布在晶粒内部及晶界,平均尺寸114 nm,尺寸较大的为不规则椭圆形的Zr-Nb-Fe相,尺寸较小的为圆形的β-Nb相;热处理退火温度降低,带材晶粒尺寸减小,第二相粒子细小弥散分布;新型锆合金薄板成品带材良好冲制性能主要源于轧制积累应变诱发再结晶过程进行充分,导致晶粒细小及孪晶发生破碎;相对轧制变形,退火对带材冲制性能影响不显著。     

等温退火对8030铝合金导线组织性能的影响

研究了不同等温退火工艺对8030铝合金导线组织及性能的影响。结果表明:等温退火前后合金均由α-Al基体和Al₆Fe相组成。在同一等温温度下,随着等温时间的延长组织逐渐趋于均匀化;同一等温时间下,随着等温温度的升高,组织趋于均匀化的时间缩短。经过等温退火处理后铝合金导线的导电率均有所提高,在470 ℃均匀化退火24 h后再经240 ℃等温4 h,合金导电率达到最高值57.21%IACS,比未经热处理试样的导电率提高了2.4%IACS。经过等温退火处理后铝合金导线的硬度及抗拉强度均有所降低,塑性大幅度提高。在470 ℃均匀化退火24 h后再经260 ℃等温8 h,合金的伸长率最高可达23.64%。热处理前后合金均为塑性断裂。