Ultimate bearing capacity of strip footing resting on clay soil mixed with tire-derived aggregates

This study investigated the use of recycled tire-derived aggregate (TDA) mixed with kaolin as a method of increasing the ultimate bearing capacity ( UBC) of a strip footing. Thirteen 1g physical modeling tests were prepared in a rigid box of 0.6 m × 0.9 m in plan and 0.6 m in height. During sample preparation, 0%, 20%, 40%, or 60% (by weight) of powdery, shredded, small-sized granular (G 1–4 mm) or large-sized granular (G 5–8 mm) TDA was mixed with the kaolin. A strip footing was then placed on the stabilized kaolin and was caused to fail under stress-controlled conditions to determine the UBC. A rigorous 3D finite element analysis was developed in Optum G-3 to determine the UBC values based on the experimental test results. The experimental results showed that, except for the 20% powdery TDA, the TDA showed an increase in the UBC of the strip footing. When kaolin mixed with 20% G (5–8 mm), the UBC showed a threefold increase over that for the unreinforced case. The test with 20% G (1–4 mm) recorded the highest subgrade modulus. It was observed that the UBC calculated using finite element modeling overestimated the experimental UBC by an average of 9%.     

超声波辅助插层-剥离法制备煤系高岭土微粉的研究

我国煤系高岭土储量丰富,为满足造纸、纺织等行业个性化的需求,通常要对其进行深加工。以山西朔州煤系高岭土为原料,分别在恒温磁力搅拌和超声波作用下探究了煤系高岭土/二甲基亚砜(DMSO)插层复合物制备的最佳条件,在插层复合物的基础上对煤系高岭土进行超声辅助剥离,制备得到高岭土微粉,并利用XRD、SEM、BET、TG-DSC等方法分析表征样品。正交实验结果表明在磁力搅拌条件下DMSO用量、插层时间以及插层温度均对插层率具有一定的影响,引入超声波有利于高岭土插层率的提升。插层复合物经超声辅助剥离后晶粒厚度明显减小,高岭土片层状结构大体上呈现碎片化,仅保留少部分大的片状结构,其边缘碎化,整体上也出现碎裂的趋势。剥离样品的比表面积和孔径均大幅度增加,为硬质高岭土的剥离和超微细粉体的制备提供了新的思路。     

低硅铝比X分子筛合成研究进展

综述了低硅铝比X分子筛合成的研究进展,分别从常规化学药品原料、非常规原料高岭土和其他原料进行了评述,并分析了各种原料和合成方法的优缺点,详细介绍了常规原料合成低硅铝比X分子筛的几种方法,重点讨论了在钾钠体系下低温老化高温晶化两步法合成低硅铝比X分子筛的研究进展,指出了高岭土和常规原料合成低硅铝比X分子筛存在物料不纯、活性不足、预处理工序复杂问题和不足。     

聚丙烯酰胺-聚硅酸锌复合絮凝剂的制备和絮凝性能

利用物理复合的方法制备聚丙烯酰胺（PAM）-聚硅酸锌（PSZ）复合絮凝剂。结果表明,聚丙烯酰胺-聚硅酸锌絮凝剂在复配比例为V （PAM）： V （PSZ）=1.0、投加量为0.10 mL、模拟水样pH为8左右时,对高岭土模拟废水絮凝效果最好,脱色率达91.2%,均高于聚丙烯酰胺和聚硅酸锌单独使用的效果（最高脱色率分别达87.66%和89.78%）;而且,在中性和碱性范围内,这种复合絮凝剂受pH影响较小。三种絮凝剂应用于四种工业废水的脱色处理结果表明,聚丙烯酰胺-聚硅酸锌复合絮凝剂的脱色率也均比单一絮凝剂要高。     

高岭土合成Y型分子筛研究进展

综述高岭土合成Y型分子筛研究进展,分别从原位合成、纳米分子筛、高硅分子筛和其他合成方法进行评述,并分析各种合成方法的优缺点。原位合成Y型分子筛是合成性质优良Y型分子筛的重要方法,相关研究不断深化成熟,以此方法合成特殊性能的Y型分子筛成功应用于催化裂化催化剂。合成具有特殊形态和结构组成的分子筛如小晶粒Y型分子筛、高硅Y型分子筛是近年来的研究热点。分别从优化合成条件、加入分散剂和使用微波加热法介绍小晶粒Y型分子筛合成研究进展。高硅Y型分子筛的合成主要分为直接合成和二次改性方法,直接合成法反应条件苛刻,存在原料浪费等问题;二次改性方法工艺流程长,易导致合成成本增加。重点讨论具有特种性能的特种Y型分子筛合成研究进展,对离子液体合成Y型分子筛、干胶转化合成Y型分子筛和高岭土合成复合分子筛等新方法进行综述,并结合其他先进的分子筛合成方法,指出Y型分子筛合成的研究方向和前景。     

光稳定剂对水工闸门用PE-HD/高岭土复合材料性能的影响

采用共混造粒制备含有不同光稳定剂的水工闸门用高密度聚乙烯(PE-HD)/高岭土复合材料,讨论和研究光老化前后复合材料的力学性能变化规律。通过偏光显微镜观察复合材料试样表面形貌、采用傅里叶变换红外光谱和核磁共振氢谱对表面析出物进行分析,讨论比较不同受阻胺光稳定剂的析出原因及抗光老化作用差异。结果表明,添加光稳定剂2020、光稳定剂944、光稳定剂123、光稳定剂770和光稳定剂292的复合材料光老化后力学性能保留率平均值分别为87.1%,81.7%,79.1%,78.2%和75.6%,抗光老化性能依次变弱;分子量大的光稳定剂2020和光稳定剂944更容易与复合材料体系相容,不容易析出,具有更好的抗光老化作用,同时带有较稠密的受阻胺结构的光稳定剂2020具有出色的抗光老化作用,这可为PE-HD/高岭土复合材料光稳定剂选配和抗光老化性失效分析提供参考。     

Reaction behavior of kaolinite with ferric oxide during reduction roasting

The pre-separation of silica and alumina in aluminosilicates is of great significance for efficiently treating alumina-/silica-bearing minerals for alumina production. In this work, the reaction behavior of kaolinite with ferric oxide during reduction roasting was investigated. The results of thermodynamic analyses and reduction roasting experiments show that ferrous oxide obtained from ferric oxide reduction preferentially reacts with alumina in kaolinite to form hercynite, meanwhile the silica in kaolinite is transformed into quartz solid solution and/or cristobalite solid solution. With increasing roasting temperature, fayalite formed by reaction of surplus ferrous oxide with silica at low temperature is reduced to silica and metallic iron in the presence of sufficient carbon dosage. However, increasing roasting temperature and decreasing Fe₂O₃/Al₂O₃ molar ratio favor mullite formation. The complete conversion of kaolinte into free silica and hercynite can be obtained by roasting raw meal of kaolin, ferric oxide and coal powder with Fe₂O₃/Al₂O₃/C molar ratio of 1.2:2.0:1.2 at 1373 K for 60 min. This work may facilitate the development of a technique for comprehensively utilizing silica and alumina in aluminosilicates.     

在X-射线衍射中与白云母特征峰重合的高岭土矿物组分测算

针对高岭土矿物在X-射线衍射分析过程中,组成矿物之间存在特征峰重合无法定量各组分含量的情形。该测算通过X-射线物相定量分析、化学成分分析、氧化物在矿物中所占比例等参数进行换算,计算出了高岭土各组成矿物的含量。     

Dynamic modeling of a multiple hearth furnace for kaolin calcination

A dynamic model of a multiple hearth kaolin calciner has been developed and is presented in this article. This model describes the physical‐chemical phenomena taking place in the six furnace parts: the solid phase, gas phase, walls, cooling air, rabble arms, and the central shaft. The solid phase movement, in particular, is described by a novel mixing model. The mixing model divides the solid bed in a hearth into volumes and the distribution of their contents, after one full central shaft rotation, is identified by the pilot experiments. First, the model is validated by the industrial data, and then the dynamics of the multiple hearth furnace is studied by introducing step changes to the three manipulated variables: the feed rate, and the gas, and air flows supplied. The responses of the gas phase temperature and solid bed component profiles are analysed and the results are discussed. © 2015 American Institute of Chemical Engineers AIChE J, 61: 3683–3698, 2015