Sol-Gel Preparation and Luminescence Properties of BaMgAl10O17∶Eu2+ Phosphors

The synthesis of BaMgAl10O17∶ Eu2 (BAM) phosphors using the sol-gel method and their luminescence properties were reported. The blue-light emitting BAM was synthesized using citric acid and ethylene glycol as chelating materials. Emission of blue-light was obtained from these phosphors. The luminescent intensity increases as the temperature of heat treatment is increased. This study investigated the effects of the molar ratio of ethylene glycol to citric acid (Φ value), with respect to the phase formation and luminescence properties of BAM. The variation of the Φ value resulted in the change of the sol-gel reaction mechanism and the microstructures of the resultant powders. An increase in Φ value leads to an increase in the rate of BAM phase formation. The photoluminescent intensity of the prepared phosphors increases with heating temperatures because of enhanced crystallization.     

BaFe12O19/SiO2-B2O3微晶玻璃陶瓷的制备和微波性能

采用柠檬酸sol-gel工艺合成了BaFe12O19/SiO2-B2O3微晶玻璃陶瓷，研究了SiO2-B2O3玻璃的含量，Ba/Fe原子比和热处理温度对体系析出晶相的影响，以及介电常数和磁异率在1MHz-6GHz频率范围的变化规律，结果表明，休系中SiO2-B2O3玻璃的含量和Ba/Fe比越高，BaF312O19相的析出越困难，前驱体合适的热处理温度为1000℃，介电常数和磁导率基本上随测试频率的增而加下降；介电损耗的最大值为0．43，磁损耗较小。     

Sol-Gel Preparation of LaNiO3 and Its Physical and Chemical Properties

LaNiO3 was synthesized by sol-gel method in which lanthanum nitrate and nickel nitrate were used as start materials and citric acid was used as complex for gel formation.The precursor was dried and subsequently heated at elevated temperature to form the desired product.XRD analysis shows that pure LaNiO3 was synthesized.Electrical conductivity and electrochemical performance of the material were tested.The electrical conductivity decreases from 34.5that there are current peaks in the curve, which is the evidence of the electrochemical activity of LaNiO3.     

Selective hydrogenation of oleic acid to 9-octadecen-1-ol: Catalyst preparation and optimum reaction conditions

A new catalyst, ruthenium-tin-alumina is found to selectively hydrogenate oleic acid to 9-octadecen-1-ol (oleyl + elaidyl alcohol) at low pressure with high yield. Catalyst preparation methods, catalyst raw materials and activation conditions have a significant effect on the activity of the catalyst. The optimum atomic ratio of ruthenium to tin is about 1:2. Catalyst prepared by an improved sol-gel method shows higher activity and selectivity than catalysts prepared by impregnation and coprecipitation methods. Chloride is found to have a negative effect on catalytic activity. The best catalyst is prepared from chloride-free ruthenium and tin raw materials. Under the optimum reaction conditions of 250°C and 5.6 MPa, the selectivities for 9-octadecen-1-ol and total alcohol (9-octadecen-1-ol + stearyl alcohol) formation are 80.9% and 97%, respectively, at a conversion of 81.3%.     

Nonepitaxial Orientation in Sol–Gel Bismuth Titanate Films

Control over crystallographic orientation in ceramic thin films is important for highly anisotropic structures. Layered perovskites, like Bi₄Ti₃O₁₂, have interesting properties associated with their ferroelectric nature, which may be fully exploited only when films are highly textured. Textured films of this titanate were fabricated via a sol–gel technique without using epitaxial growth. Orientation in the film is confirmed by XRD and SEM, and supported by refractive index and dielectric measurements. In an attempt to explain the orienting effect, light scattering experiments were conducted to yield information about the molecular size, shape, and conformation of macromolecules as the sol–gel solution ages and condensation reactions proceed. These experiments clearly show an increase in the size of molecular clusters with time. We believe that it is the organization of these large clusters during spin coating, and the relationship of the backbone chemistry to the crystal structure of Bi₄Ti₃O₁₂, that are responsible for the observed orientation.     

YAG：Ce Phosphors for WLED via Nano-Pesudoboehmite Sol-Gel Route

The sub-micron sized YAG ： Ce phosphors were synthesized via a modified sol-gel method by peptizing nano-pesudoboehmite particulate. It is found that YAG phase from the dried gel powders appears at 1000 ℃ then the pure YAG phase exists at a relatively lower sintering temperature of 1400 ℃. The smaller sizes of phosphors in the ranges of 1 - 3 μm are obtained due to the contribution of seeding effects of nano-sized alumina particles to strengthen each step of the processes. Both the excitation and emission spectra of photoluminescence of the phosphor obtained at 1400 ℃ meet well with the spectroscopic requirements of the WLED phosphors.     

溶胶–凝胶法制备ATO-SiO_2抗静电复合薄膜的特性研究

采用两步溶胶–凝胶法制备出 ATO(掺锑氧化锡)-SiO_2复合抗静电薄膜。通过 DTA-TG、XRD、SEM 对 薄膜的结构和形貌进行了表征,结果表明:抗静电复合薄膜表面均匀致密。薄膜中 SiO_2为无定形结构,ATO 的衍射峰 与 SnO_2一致。研究了 SnO_2的含量对薄膜导电性能、结合强度和透过率的影响,发现随 SnO_2含量增加 ?(SnO_2/ SiO_2)从 5 至 12.5,薄膜的表面电阻降低(从 1010ù/□降低到 108ù/□),薄膜的结合强度下降,薄膜的透过率降低(从 89.0%降至 84.2%),结合三方面性能,得出最佳 SnO_2的配比为:?(SnO_2/ SiO_2)=10。     

TiO2纳米薄膜的微结构控制

通过有机酸修饰的水基so1-gel法，分别制备了由层状、针形和球形纳米粒子构成的纳米二氧化钛薄膜，采用SEM、XRD、红外光谱进行了表征.研究发现，调节水解过程中钛酸四丁酯：醋酸的摩尔比，可以控制薄膜的微结构，并对其机理进行了分析.该方法可以应用于sol-gel法制备其他纳米薄膜过程中的材料微结构控制.     

溶胶-凝胶法制备纳米氧化锡及其性能表征

以SnCl4·5H2O为原料,采用溶胶-凝胶法制备了纳米SnO2粒子,研究了焙烧温度、碱的种类及反应物浓度对纳米SnO2粒子大小和分散状态的影响。采用XRD、TEM、ED等技术对SnO2纳米粒子的性能进行了表征。实验结果表明:用氨水和尿素作为沉淀剂,控制反应结束时pH值为7,在600℃焙烧,制备得到粒子尺寸约为15nm、分散性良好的纳米SnO2粒子。     

溶胶-凝胶法制备磷钨酸-硅胶催化合成苹果酯

采用溶胶-凝胶法制备了一系列磷钨酸-硅胶催化剂(PW/SG),考察了该催化剂催化乙酰乙酸乙酯与乙二醇液相缩合制备苹果酯的反应性能。实验结果表明,PW质量分数为40%时的PW/SG催化剂表现出最佳的催化活性;40%PW/SG催化剂制备苹果酯的最佳工艺条件为:n(乙酰乙酸乙酯)∶n(乙二醇)=1∶1.2,催化剂用量占反应物质量的0.36%,带水剂环己烷用量占反应物体积的30%,反应温度383K,反应时间90min;在此条件下,乙酰乙酸乙酯的转化率可达95.5%,苹果酯的选择性大于97%;催化剂稳定性实验表明,经5次重复使用,40%PW/SG催化剂的活性基本保持不变,乙酰乙酸乙酯转化率稳定在95.0%左右。