喷雾转化法制备WC-Co复合粉末制备硬质合金的研究进展

综述了国内外以钨源、钴源或钨源、钴源、碳源通过喷雾转化法制备WC-Co复合粉末及硬质合金制备的研究进展。主要讨论制备WC-Co粉末及硬质合金的思路、方法、工艺参数和合金性能,为喷雾转化法制备WC-Co复合粉末制备硬质合金提供研究思路及方法。通过不断优化、改进制备工艺和方法可制备出工艺流程短、组元分布均匀、杂质含量低、粒度分布窄、晶粒度小、成本低的WC-Co复合粉末。     

粉末原料对SPS法制备WC-6Co硬质合金组织性能的影响

以不同形貌结构的WC-6Co复合粉和传统湿磨制备的WC-6Co混合粉为原料,通过放电等离子烧结制备出WC-6Co硬质合金,采用SEM、显微硬度计、密度仪、钴磁仪和矫顽磁力计等对硬质合金的微观组织、力学和物理性能进行了表征。分析结果表明:采用喷雾转化、低温煅烧、原位合成制备的球形复合粉为原料,经SPS法制备所得的WC-6Co硬质合金中残留有较多孔隙,合金密度仅为14.21g/cm~3,将球形复合粉湿磨48h后制备的合金密度略有提升,但硬度和韧性较低。分别采用喷雾转化、低温煅烧加短时球磨、原位合成制备的松散型WC-6Co复合粉和传统湿磨制备的WC-6Co混合粉为原料,经SPS法制备的合金微观组织均匀、合金孔隙减少,两组合金的密度分别增加至14.77、14.73g/cm~3;显微硬度分别增大至2 045、1 929kg/mm~2,韧性分别为8.76、9.29MPa/m~(1/2)。     

Preparation of Highly Dispersed and Ultrafine Pt Particles on Carbon Nanotubes used as an Effective Electrochemical Catalyst

研究了不同分散程度的双壁碳纳米管(DWCNTs)作为载体沉积Pt,得到了尺寸2.08 nm的Pt颗粒均匀分散于DWCNTs表面。这种尺寸与分散状态的Pt颗粒相比其样品显示了极高的电催化活性(电流密度为0.022 A·cm?2,电化学比表面积为86.38 m2 ·g-1)。进一步的分析表明,载体在溶液中的浓度对形成Pt颗粒的尺寸和分布具有重要影响,这种尺寸与分散状态的Pt颗粒可以实现高电催化活性和低成本的Pt催化剂制备     

直流溅射沉积CrAlN和CrN薄膜微观结构与摩擦性能分析研究（英文）

采用直流反应溅射在304不锈钢表面沉积CrAlN和CrN薄膜。利用X射线衍射仪(XRD),扫描电子显微镜(SEM),X射线光电子能谱仪(XPS),原子力显微镜(AFM)等表征Al元素的加入对CrN薄膜成分与组织结构的影响。采用摩擦磨损试验机和3 mm的Si_3N_4作为对偶球测试其在不同环境下的摩擦性能,并利用Nanomap 500LS三维轮廓仪表征磨痕轮廓。研究结果表明,CrN薄膜主要物相是CrN和Cr_2N相,CrAlN薄膜主要物相是CrAlN和Cr_2N相。CrN薄膜的(200)晶面的CrN相呈择优取向,而CrAlN薄膜的(200)晶面的CrAlN相也呈择优取向。在CrAlN沉积的过程中,部分的Cr原子被Al原子替代形成有利于细化晶粒和提高薄膜的综合性能。因此,在所有的实验环境中,CrAlN薄膜都比CrN薄膜具有更好的抗磨损性能和低的磨损率。     

原位合成WC-6Co复合粉末制备超细YG6硬质合金

将原位合成WC-6Co复合粉末采用干袋式冷等静压压制成型(压制压力1×10~8 Pa、保压时间15 s),将压制好的坯料采用低压烧结炉烧结(烧结温度1360℃、烧结时间40 min、加压5 MPa、保温保压时间20 min),烧结制备超细YG6硬质合金,对合金的形貌、金相组织及物理力学性能进行分析。结果表明:原位合成WC-6Co复合粉末制备的超细YG6硬质合金,晶粒异常长大,WC平均晶粒尺寸为0.8μm,硬度HV_(30)为(21500±100) MPa,较传统超细YG6X硬度高。再将WC-6Co复合粉末采用滚动湿磨、压力式喷雾干燥、掺成型剂、挤压成型、低压烧结等工序制备超细YG6硬质合金,研究不同晶粒长大抑制剂配比、球磨时间、挤压压力、烧结温度对合金性能的影响。结果表明:添加0.3%VC、0.8%Cr_3C_2(质量分数),湿磨48 h,挤压压力24 MPa,烧结温度1340℃,制备的超细YG6硬质合金WC晶粒均匀,无异常长大的WC晶粒,WC平均晶粒度尺寸0.4μm,呈多边形,外形较圆。强度、硬度最高,抗弯强度TRS为(2250±20) MPa、硬度HV30为(22600±100) MPa。断口形貌为沿晶断裂,沿WC与WC晶界断裂或WC与Co晶界断裂。     

硬质合金的发展趋势及特殊粉末的制备技术

在简要介绍硬质合金特点的基础上,阐述了切削刀具、矿用工具这两大类硬质合金的发展趋势,并重点对高性能硬质合金及特殊原料粉末的制备技术进行了比较和分析.     

Processing and properties of 2D SiC/SiC composites by precursor infiltration and pyrolysis

Two-dimensional plain-weave silicon carbide fiber fabric reinforced silicon carbide (2D-SiC/SiC) composites were molded by stacking method and densified through precursor infiltration and pyrolysis (PIP) process. SiC coating was deposited as the fiber/matrix interphase layer by chemical vapor deposition (CVD) technique. Fiber/matrix debonding and relatively long fiber pullouts were observed on the fracture surfaces. Additionally, the flexural strength and elastic modulus of the composites with and without fiber/matrix interphase layer were investigated using three-point bending test and single-edge notched beam test. The results show that the fiber fraction and the porosity of 2D-SiC/SiC composites with and without coating are 27.2% (volume fraction) and 11.1%, and 40.7% (volume fraction) and 7.5%, respectively. And the flexural strength and elastic modulus of 2D-SiC/SiC composites with and without coating are 363.3 MPa and 127.8 GPa, and 180.2 MPa and 97.2 GPa, respectively. With a proper thickness, the coating can effectively adjust the fiber/matrix interface, thus causing a dramatic increase in the mechanical properties of the composites. Foundation item: Project(NCET-07-0228) support by the New Century Excellent Talents in University     

超高温雾化制备球形铸造碳化钨粉末形貌控制及性能研究

传统的热喷涂用碳化钨粉末通常采用铸造方法生产,粉末呈多角状,流动性差且硬度低,难以满足高性能硬面材料的要求。以钨粉、炭黑、碳化钨粉前躯体或多角状碳化钨为原料,采用自行设计的超高温熔炼及超高温雾化装备制备出球形碳化钨粉末,利用扫描电镜、X射线衍射仪、金相显微镜、显微硬度计分析测试了粉末的相、组织、成分及性能。结果表明:碳化钨粉末外观呈球状、内部为细针状共晶组织、显微硬度3 200 HV、霍尔流速6.5 s/50 g、具有流动性好、耐磨性佳等优良的综合性能。     

喷雾转换法制备纳米WC-Co复合粉末的研究现状

介绍了纳米WC-Co复合粉末喷雾转化制备方法,该方法具有流程短、组元分布均匀、制造成本低等优点,被广泛、深入地研究,从而衍生出多种纳米WC-Co复合粉末制备法。     

新型YWR_2稀土硬质合金的使用性能与显微结构

YWR_2是在YW_2基础上通过添加微量稀土添加剂所获得的硬质合金新牌号,本文利用正交试验的方法获得了最佳稀土添加形态、添加量、添加方式,该稀土合金具有优良的物理机械性能和使用性能,同条件下,在硬度不变甚至略有提高的情况下,抗弯强度和抗冲击韧性值比YW_2都提高10％以上,十多家用户使用结果表明,YWR_2的平均耐用度为YW_2的1倍以上。 采用电子探针、扫描电镜、金相仪等手段研究了稀土在YWR_2合金中的存在形式和分布状态以及对粘结相,硬质相、相界面等的影响。从YWR_2和YW_2合金的显微结构比较,阐述了稀土改善YW_2合金性能的作用机理。