Effect of sodium doping on graded Cu(In1−xGax)Se2 thin films prepared by chemical spray pyrolysis

In the present work we have studied the effect of Na on the properties of graded Cu(In_1−xGa_x)Se₂ (CIGS) layer. Graded CIGS structures were prepared by chemical spray pyrolysis at a substrate temperature of 350 °C on soda lime glass. Sodium chloride is used as a dopant along with metal (Cu/In/Ga) chlorides and n, n-dimethyl selenourea precursors. The addition of Na exhibited better crystallinity with chalcopyrite phase and an improvement in preferential orientation along the (112) plane. Energy dispersive analysis of X-rays (line/point mapping) revealed a graded nature of the film and percentage incorporation of Na (0.86 at%). Raman studies showed that the film without sodium doping consists of mixed phase of chalcopyrite and CuAu ordering. Influence of sodium showed a remarkable decrease in electrical resistivity (0.49–0.087 Ω cm) as well as an increase in carrier concentration (3.0×10¹⁸–2.5×10¹⁹ cm⁻³) compared to the un-doped films. As carrier concentration increased after sodium doping, the band gap shifted from 1.32 eV to 1.20 eV. Activation energies for un-doped and Na doped films from modified Arrhenius plot were calculated to be 0.49 eV and 0.20 eV, respectively. Extremely short carrier lifetimes in the CIGS thin films were measured by a novel, non-destructive, noncontact method (transmission modulated photoconductive decay). Minority carrier lifetimes of graded CIGS layers without and with external Na doping are found to be 3.0 and 5.6 ns, respectively.     

Abrasive waterjet micro-machining of channels in metals: Comparison between machining in air and submerged in water

Abrasive water jet technology can be used for micro-milling using recently developed miniaturized nozzles. Abrasive water jet (AWJ) machining is often used with both the nozzle tip and workpiece submerged in water to reduce noise and contain debris. This paper compares the performance of submerged and unsubmerged abrasive water jet micro-milling of channels in 316L stainless steel and 6061-T6 aluminum at various nozzle angles and standoff distances. The effect of submergence on the diameter and effective footprint of AWJ erosion footprints was measured and compared. It was found that the centerline erosion rate decreased with channel depth due to the spreading of the jet as the effective standoff distance increased, and because of the growing effect of stagnation as the channel became deeper. The erosive jet spread over a larger effective footprint in air than in water, since particles on the jet periphery were slowed much more quickly in water due to increased drag. As a result, the width of a channel machined in air was wider than that in water. Moreover, it was observed that the instantaneous erosion rate decreased with channel depth, and that this decrease was a function only of the channel cross-sectional geometry, being independent of the type of metal, the jet angle, the standoff distance, and regardless of whether the jet was submerged or in air, in either the forward or backward directions. It is shown that submerged AWJM results in narrower features than those produced while machining in air, without a decrease in centerline etch rate.     

Al-10Mg型固溶合金自然时效稳定性研究

测定了ZL30 5合金自然时效 33年的力学性能变化 ,观察了晶界的析出相 ,研究了组织和性能的关系 ,从而确定了ZL30 5合金具有长期自然时效稳定性。     

Mechanical behavior of 30–50 nm thick aluminum films under uniaxial tension

We present uniaxial tensile test results for 30–50 nm thick freestanding aluminum films. Young’s modulus and ductility were found to decrease monotonically with grain size. Reverse Hall–Petch behavior was observed with no appreciable room temperature creep. Non-linear elasticity with small irreversible deformation was observed for 50 nm thick specimens.     

硼酸铝晶须增强环氧树脂和双马来酰亚胺树脂体系的研究

本文以硼酸铝晶须为增强剂，以4，5-环氧环己烷-1，2-二甲酸二缩水甘油酯(TDE-85)，甲基纳狄克酸酐(MNA)、N，N’-二胺基二苯甲烷型双马来酰亚胺(BMI)/O，O′-二烯丙基双酚A(BA)体系分别作为基体制备晶须增强复合材料。研究了晶须对树脂的尺寸、表面处理方法、含量对树脂体系力学性能和热性能的影响；通过扫描电子显微镜(SEM)分析了浇注体的弯曲、冲击断口，研究晶须的增强机理。     

Influence of inhibitor addition on the corrosion protection performance of sol–gel coatings on AA2024

Sol–gel films are actively investigated during the last decade as possible candidates for environmentally friendly pre-treatments. However, the important drawback in this case is the lack of active corrosion protection and self-healing ability.     

Transmittance and cathodoluminescence of AlN ceramics sintered with Ca3Al2O6 as sintering additive

Aluminum nitride ceramics were prepared by sintering with 0–4.8 mass% of Ca₃Al₂O₆ (C₃A) as a sintering additive. The transmittance in the range of 260–550 nm increased with increasing amount of C₃A. The cathodoluminescence intensity attributed to oxygen-induced defects decreased with increasing amount of C₃A. From the results, the increase of the transmittance in the range of 260–550 nm was considered to be related to the decrease of the oxygen-induced defect density.     

单轴-平面W型复合锶铁氧体的制备及其吸波特性研究

用草酸盐共沉淀和微量掺杂法研制六角晶系W型Ni,Zn,Co,Al多元复合锶铁氧体，通过调节Ni2W同Co2W的摩尔比例，可使该种铁氧体易磁化方向从C单轴型向垂于C轴的平面型转化，控制置换锶铁氧体中部分Fe3 的微量掺杂Al3 ，可以调整4πMs值，提高磁晶各向异性场，测试分析了5种不同含Co量的W型复合锶铁氧体粉料涂层的吸波特性，发现其自然共振吸收峰随Co含量增加向低频方向偏移，最高吸收峰可达32．8dB，是适用于电子隐形技术的高品位的微波吸收剂。     

ZnO陶瓷材料的负阻特性

介绍了ＺｎＯ陶瓷的负阻特性，主要研究了ＭｎＯ２掺杂和Ｎｉ２Ｏ３掺杂对ＺｎＯ陶瓷负阻特性的影响。