LD钢超塑性压缩变形参数与金相组织

通过对ＬＤ（７Ｃｒ７Ｍｏ３Ｖ２Ｓｉ）模具钢起塑性压缩变形后的金相组织观察研究，分析了变形参数、原始组织对变形后金相组织的影响。     

A simple mathematical analysis on the effect of sand in Cr(VI) reduction using zero valent iron

A simple mathematical model was proposed to analyze the enhancement of Cr(VI) reduction when sand materials are added to the zero valent iron (ZVI). Natural decay of Cr(VI) in a control experiment was analyzed by using a zero-order decay reaction. Adsorption kinetics of Cr(VI) to sand was modeled as a first-order reversible process, and the reduction rate by ZVI was treated as a first-order reaction. Natural decay of Cr(VI) was also included in other experiments, i.e., the adsorption to sand, the reduction by ZVI, and both adsorption and reduction when sand and ZVI are present together. The model parameters were estimated by fitting the solution of each model to the corresponding experimental data. To observe the effect of sand addition to ZVI, both adsorption and reduction rate models were considered simultaneously including the natural decay. The solution of the combined model was fitted to the experimental data to determine the first-order adsorption and reduction rate constants when sand as well as ZVI is present. The first-order reduction rate constant in the presence of sand was about 35 times higher than that with ZVI only.     

高速钢W6Mo5Cr4V2的脱磷试验

在３０ｋｇ感应炉上用ＣａＯ－Ｎａ２ＣＯ３－ＣａＦ２－ＦｅｘＯ（ＭｏＯ３）渣、ＭｏＣｌ６粉剂和Ａｌ－Ｃａ合金作脱磷剂对高速钢Ｗ６Ｍｏ５Ｃｒ４Ｖ２进行脱磷试验。结果表明，ＣａＯ－Ｎａ２ＣＯ３－ＣａＦ２－ＦｅｘＯ渣的脱磷效果最好，一般脱磷率可达２６％￣５６％。     

Probing the early stages of polymerization of ethylene on a model chromium/silica catalyst by Fourier transform infrared spectroscopy

The nature of the interaction of monomer, and the early stages of growth of oligomers of ethylene on a rather more uniform surface of Cr/SiO₂ catalyst than hitherto studied has been investigated by differenceFTIR spectroscopy using C₂D₄ and C₂H₄ as reactants both with and without subsequent treatment of the catalyst with CO andTHF. The active catalyst was prepared by reaction of vapour phase CrO₂Cl₂ with the vicinal hydroxyls of the silica surface. Three distinct kinds of methylene groups were detected. Arguments are given for assigning the peaks at 2935 and 2860 cm^–1 to CH₂ groups directly bound to the active site and those at 2920 and 2850 to CH₂s in the growing chain well removed from the Cr. The peaks at 2160 and 2165 cm^–1 are attributed to CD₂ groups hydrogen bonded to surface hydroxyls.     

常减压蒸馏装置阻垢剂进料管腐蚀与防护

通过对常减压蒸馏装置阻垢剂进料管的材质、性能、工作条件及腐蚀形貌、腐蚀产物的全面分析,找出了使进料管发生大面积腐蚀的腐蚀介质为环烷酸.并提出了减缓阻垢剂进料管环烷酸腐蚀的措施,主要包括选用更耐蚀的316或316 L材质以及改进三通结构等.     

修正步冷温度曲线试验研究

按修正步冷温度曲线对经步冷脆化的 2 .2 5Cr 1Mo和在加氢反应器内运行 5a的 2 2 5Cr 1Mo试块进行了修正步冷试验 ,评定了材料的回火脆性。结果表明 ,按修正步冷曲线进行修正步冷试验能使已经脆化的材料进一步脆化 ,为加氢反应器材料损伤的研究提供了一条途径。     

改进渣浆泵过流件铸造工艺及硬度的措施

介绍了渣浆泵过流件材质的化学成分及其正交试验的优选过程，以及重新制定的铸造工艺。     

A new precipitate phase in Al-4wt. % Cu thin-film interconnects

We report here the identification of a new precipitate phase in thin-film Al-4wt.%Cu metallization used for interconnects on integrated circuits. The phase is based on a trigonal distortion of a face centered cubic lattice. Computer simulation of electron diffraction intensities suggests that the basis structure is isomorphous with Al₂Ca but with a large and ordered population of vacancies on Cu sites. The reason for the formation of the new phase and its implications for electromigration reliability are discussed.     

High energy Urbach characteristic observed for gallium nitride amorphous surface oxide

We have observed an “above band-gap” Urbach like characteristic for gallium nitride films (at the high energy side of the band-edge). A combination of X-ray diffraction, secondary ion mass spectroscopy and optical transmission measurements were taken for gallium nitride samples of different thickness. From this data we demonstrate that the high energy Urbach like characteristic is related to the presence of an amorphous surface oxide. It is shown to dominate the absorption spectra of thin gallium nitride samples, for which the influence of surface oxidation is strongest.     

Cr12MoV钢冷挤压成形模强化工艺的研究

针对Crl2MoV钢冷挤压成形模热处理存在的质量问题，对加热温度和方式进行了大量的试验研究，在此基础上，提出了改进的快速加热工艺。结果表明，经该工艺处理后，模具使用寿命得到显提高。