Thermal shock performance and failure behavior of Zr6Ta2O17-8YSZ double-ceramic-layer thermal barrier coatings prepared by atmospheric plasma spraying

Zr₆Ta₂O₁₇ has higher fracture toughness, better phase stability, thermal insulation performance and calcium-magnesium-alumino-silicates (CMAS) attack resistance than yttria-stabilized zirconia (8 YSZ, 7–8 wt%) at temperatures above 1200 °C. However, the thermal expansion coefficients between Zr₆Ta₂O₁₇ coating and bond coating do not match well. A double-ceramic-layer design is applied to alleviate the thermal stress mismatch. The Zr₆Ta₂O₁₇/8 YSZ double-ceramic-layer thermal barrier coatings (TBCs) are prepared by atmospheric plasma spraying (APS). During the thermal shock test, Zr₆Ta₂O₁₇/8 YSZ double-ceramic-layer TBCs exhibit a better thermal shock resistance than 8 YSZ and Zr₆Ta₂O₁₇ single-layer TBCs. The thermal shock performance and failure mechanism of TBCs in the thermal shock test are investigated and discussed in detail.     

Novel thermal barrier coatings based on La2(Zr0.7Ce0.3)2O7/8YSZ double-ceramic-layer systems deposited by electron beam physical vapor deposition

Double-ceramic-layer (DCL) thermal barrier coatings (TBCs) of La₂(Zr_0.7Ce_0.3)₂O₇ (LZ7C3) and yttria stabilized zirconia (YSZ) were deposited by electron beam-physical vapor deposition (EB-PVD). The thermal cycling test at 1373 K in an air furnace indicates the DCL coating has a much longer lifetime than the single layer LZ7C3 coating, and even longer than that of the single layer YSZ coating. The superior sintering-resistance of LZ7C3 coating, the similar thermal expansion behaviors of YSZ interlayer with LZ7C3 coating and thermally grown oxide (TGO) layer, and the unique growth modes of columns within DCL coating are all very helpful to the prolongation of thermal cycling life of DCL coating. The failure of DCL coating is mainly a result of the reduction-oxidation of cerium oxide, the crack initiation, propagation and extension, the abnormal oxidation of bond coat, the degradation of t′-phase in YSZ coating and the outward diffusion of Cr alloying element into LZ7C3 coating.     

La2Ce2O7/YSZ热障涂层抗热震性能的陶瓷层厚度影响研究

采用实验和数值方法研究了陶瓷层厚度比对La2Ce2O7/YSZ(LC/YSZ)热障涂层热震性能的影响。实验结果表明,随着LC与YSZ厚度比的降低,涂层热震寿命显著提高,涂层失效区域逐渐向试样中心转移,剥离位置逐渐从两陶瓷层界面附近转移到LC内靠近上表面处。数值结果表明,界面边缘处较大的轴向应力与剪切应力易导致较大厚度比涂层边缘处剥落;LC表面中心区域较大的径向拉应力会导致垂直裂纹萌生,并伴随界面偏折,这是较小厚度比涂层自LC内部剥离的原因。     

Thermal cycling behavior of plasma-sprayed yttria-stabilized zirconia thermal barrier coating with La0.8Ba0.2TiO3−δ top layer

In this study, a La_0.8Ba_0.2TiO_3?δ (LBT) upper layer was deposited on an yttria-stabilized zirconia (YSZ) thermal barrier coating (TBC) through atmospheric plasma spraying. The thermal cycling behaviors of the YSZ single-ceramic-layer and LBT–YSZ double-ceramic-layer coatings at 1000 °C were investigated through a water quenching method. Moreover, phases, microstructural evolution, and elemental distributions were studied through by X-ray diffraction and scanning electron microscopy–energy-dispersive X-ray spectroscopy. The results showed that the thermal cycling lifetime of the LBT–YSZ coating was 27% higher than that of conventional YSZ coating. The conventional YSZ coating failed after 251 cycles because of the joining of the continuous horizontal and vertical cracks caused by the formation of thermal growth oxides and the bending effect of the single-ceramic-layer structure. The thermal cycling behavior of the LBT–YSZ coating was different from that of the YSZ coating at the edge and center. Although the former was similar to the failure behavior of the YSZ coating, the cracks in the vertical direction were deflected as a result of the bending effect of the double-ceramic-layer structure during quenching. This deflection led to the formation of slope cracks with longer propagation paths and slope spallation zones. The latter showed small-debris spallation on top of the LBT upper layer due to the lower fracture toughness of the LBT, which protected the central coating from the structural damage of the ceramic coating. These two behaviors would either release the thermal stress or increase the crack-propagation energy requirement in the ceramic coating, consequently improving the thermal cycling lifetime of the LBT–YSZ coating. In summary, depositing an LBT upper layer could potentially improve the thermal cycling lifetimes of TBCs.