20MnCr5圆棒锯切困难原因分析

某厂在锯切20MnCr5圆棒过程中锯条容易断裂，采用光学显微镜(OM)和扫描电子显微镜(SEM)等观察分析手段，对锯条容易断裂的原因进行分析。分析结果表明：锯条断裂的原因为加工20MnCr5过程中粘刀崩齿。针对此类加工缺陷，提出了相应的改进措施。     

Water vapor volatilization and oxidation induced surface cracking of environmental barrier coating systems: A numerical approach

A numerical model is developed for surface crack propagation in brittle ceramic coatings, aiming at the intrinsic failure of rare-earth silicate environmental barrier coating systems (EBCs) under combustion conditions in advanced gas turbines. The main features of progressive degradation of EBCs in such conditions are captured, including selective silica vaporization in the top coat due to exposure to water vapor, diffusion path-dependent bond coat oxidation, as well as crack propagation during cyclic thermal loading. In light of these features, user-defined subroutines are implemented in finite element analysis, where surface crack growth is simulated by node separation. Numerical results are validated by existing experimental data, in terms of monosilicate layer thickening, thermal oxide growth, and fracture behaviors. The experimentally observed quasi-linear oxidation in the early stage is also elucidated. Furthermore, it is suggested that surface crack undergoes rapid propagation in the late stage of extended thermal cycling in water vapor and leads to catastrophic failure, driven by both thermal mismatch and oxide growth stresses. The latter is identified as the dominant mechanism of penetration. Based on detailed analyses of failure mechanisms, the optimization strategy of EBCs composition is proposed, balancing the trade-off between mechanical compliance and erosion resistance.     

A novel ceramic matrix composite based on YNbO4–TiO2 for microwave applications

This work presents the dielectric properties of YNbO₄ (YNO)–TiO₂ composites in the microwave range. X-ray diffraction analysis demonstrates that the addition of TiO₂ to YNO results in the formation of a Y(Nb_0.5Ti_0.5)₂O₆ phase. In the microwave range, the values of permittivity and dielectric loss did not present major changes with the increment of TiO₂. Moreover, the addition of TiO₂ results in an improvement in the thermal stability of YNO, with YNO63 demonstrating a resonant frequency of ?8.96 ppm.°C^?1. We utilised numerical simulations to evaluate the behaviour of these materials as dielectric resonator antennae and it is found that they exhibit a reflection coefficient below ?10 dB at the resonant frequency, with a realised gain of 4.94 – 5.76 dBi, a bandwidth of 665–1050 MHz and a radiation efficiency above 84%. Our results indicate that YNO–TiO₂ composites are interesting candidates for microwave operating devices.     

Turbulent boundary layer control with a spanwise array of DBD plasma actuators

The turbulent boundary layer control on NACA 0012 airfoil with Mach number ranging from 0.3 to 0.5 by a spanwise array of dielectric barrier discharge(DBD)plasma actuators by hot-film sensor technology is investigated.Due to temperature change mainly caused through heat produced along with plasma will lead to measurement error of shear stress measured by hot-film sensor,the correction method that takes account of the change measured by another sensor is used and works well.In order to achieve the value of shear stress change,we combine computational fluid dynamics computation with experiment to calibrate the hot-film sensor.To test the stability of the hot-film sensor,seven repeated measurements of shear stress at Ma = 0.3 are conducted and show that confidence interval of hot-film sensor measurement is from-0.18 to 0.18 Pa and the root mean square is 0.11 Pa giving a relative error 0.5％over all Mach numbers in this experiment.The research on the turbulent boundary layer control with DBD plasma actuators demonstrates that the control makes shear stress increase by about 6％over the three Mach numbers,which is thought to be reliable through comparing it with the relative error 0.5％,and the value is hardly affected by burst frequency and excitation voltage.     

机井自动化供水方案改进

针对民乐县农村人饮机井水位自动供水系统控制中存在的可靠性低、成本高等问题,文章结合深井泵提取地下水进行供水的实际情况,提出了软启动控制柜+浮球开关+微电脑时间控制器改进的思路和方法,运用效果良好。     

工艺参数对动态流量控制法挤压弯管应力的影响

采用有限元模拟和实验研究了挤压钛合金弯曲管件。通过实验验证了工件的形状和尺寸精度,并通过有限元模拟分析了工艺参数对挤出过程中变形体的平均压应力分布情况和挤出弯管件的曲率半径的影响规律。结果表明:有限元模拟中,弯管件的曲率半径误差为6.03%,弯管直径误差为3.82%;在靠近定径带处,平均压应力呈非均匀分布;在焊合腔内,靠近细分流孔区域的平均压应力小于靠近粗分流孔区域的平均压应力,平均压应力的大小顺序在通过粗、细分流孔前后相反;在模具结构固定不变时,弯管件的曲率半径随挤压速度的减小而增大,不随挤压温度的变化而变化。     

采用温控和碘吸收池技术的发射激光稳频技术

多普勒测风激光雷达通过分析系统回波信号的多普勒频移反演出风速，为提高风场探测精度，从稳频技术方面展开研究。在稳频过程中，分别采取措施消除激光频率的长期漂移和短期抖动。针对激光频率的长期漂移，设计并研制了种子激光器温控箱，通过水浴的控温方式大大减小了激光频率的长期漂移，将激光频率稳定在±50 MHz以内；针对激光频率的短期抖动，采用以碘分子吸收池为核心器件的稳频系统，通过半导体控温方式对碘分子吸收池精确控温，控温精度达0.03 ℃，提高了稳频精度，将激光频率进一步稳定在±8 MHz以内，满足±10 MHz以内的设计精度要求。通过搭建多普勒测风激光雷达系统，对发射激光稳频装置进行系统验证，连续4组风场观测结果表明:系统探测高度为17 km，绝大部分方差在4 m/s以下，满足测风激光雷达测量指标的要求。     

Effect of atmosphere control on magnetic properties of CaO-Al2O3-SiO2-Fe3O4 glass ceramics

The influences of atmosphere during processes of melting and heat treatment, heat treatment temperature, Fe₃O₄ content and basicity on the magnetic properties of magnetite-based glass ceramics were investigated. For sample containing 20 % Fe₃O₄ melted in different atmospheres, the highest saturation magnetisation was realized in 20vol% air + 80 vol% Ar, due to the fact that ratio of Fe³⁺ to Fe²⁺ in melt obtained in this atmosphere was close to 2. However, it was found that the coercivity of glass ceramics was not affected by the melting atmosphere. A high sintering temperature led to the decrease of saturation magnetisation and the increase of coercivity. As increasing Fe₃O₄ content, the main crystal phase transformed from CaSiO₃ to CaFe_0.6Al_1.3Si_1.08O₆ and finally to magnetite phase, accompanied by the increase of saturation magnetisation and coercivity. In addition, the increase of basicity caused the decrease of saturation magnetisation and the increase of coercivity.     

稀土灼烧过程温湿度场仿真分析

影响稀土灼烧工艺的因素十分复杂,关系产品质量稳定及能耗,现行工艺存在优化空间。通过剖析灼烧窑中温度和湿度分布状况,运用κ-ε双方程湍流模型、流体传热、多孔介质传热等理论,按特定组分运输模式,建立灼烧过程质量、动量和能量耦合传递数学模型。设置不同边界导入Fluent环境对数学模型进行仿真试验,完成数据处理实现工艺参数优化。结果表明所建模型能准确反映灼烧窑中温湿度场分布及变化,且最终仿真结果与实际灼烧后的产品湿度含量相符合。