Synthesis of polyanilines with pendant fluorescent units

Functionalized polyanilines containing biphenyl, terphenyl, carbazole, anthracene, and 4-n-hexylphenyl moieties were synthesized though the reaction of polyaniline in emeraldine base form with sodium salt of corresponding vinylketoaromatics with quantitative yields. Polymers were characterized with Fourier transform infrared spectroscopy, proton nuclear magnetic resonance spectroscopy, and thermogravimetry. The emission characteristics of these polymers in N-methyl-2-pyrrolidone solution were examined. The functionalized polyanilines exhibited an intense green emission.     

High‐Performance,Monolithic Polyaniline Electrochemical Actuators

New polyaniline (PANI) asymmetric membranes were fabricated using a phase‐inversion technique with hexane as the coagulation bath. These membranes exhibit a dense structure with macrovoids distributed asymmetrically throughout the cross‐section. A stress–strain study demonstrated that the Young's modulus (1.421 GPa) and strain at break (7.6 %) of the new PANI asymmetric membranes prepared from hexane are approximately 12 and 4 times higher, respectively, than the values reported previously for the PANI integrally skinned asymmetric membranes (ISAMs) (123 MPa Young's modulus and 1.8 % strain at break). Furthermore, monolithic electrochemical actuators based on a single PANI asymmetric membrane were constructed, and a bending movement of up to 20 Hz was experimentally recorded in a hydrochloric acid aqueous solution. A lifetime of over 329 500 cycles was determined for these actuators at a ± 2° angular displacement (5 Hz). The lifetime is limited by a bending fatigue that creates a transversal crack on the PANI membrane at the air–water interface. Control over the actuator movement is also manifested by the linear dependences of the bending angle on the charge and of the angular velocity on the current. These relationships are independent of both the kind of applied electric signal and the frequency used.     

Preparation and properties of PAn/ATTP/PE conductive composites

Polyaniline/Attapugite/PE（PAn-ATTP/PE）composites containing particles with core-shell structure were obtained via the two-step blending processs. The experimental condition is as follows： Organo-attapulgite and PAn was obtained by modifying attapulgite with laury benzenesulfonic acid sodium salt and, then added to PE. The electrical conductivity, structure and properties of the composites were studied. Under the function of shear stress, core-shell structure particles with ATTP as the core and PAn as the shell were formed in the composites. The structure of PAn-ATTP/PE composites were characterized by FTIR,XRD,SEM, etc, respectively. The effects of concentration of doping agent on the conductivity and mechanical property of the composites were investigated. The mechanical properties and impact fracture surface of the ternary composites were studied by means of the tensile tester, SEM, etc. The results show that polyaniline encapsulated ATTP enhances the strength of the PE. And the conductivity of PAn-ATTP/PE composites of is improved effectively when polyaniline encapsulated ATTP is added. The composite have good conductivity when 10% polyaniline encapsulated ATTP is added.     

丙烯酸酯三元共聚物酸掺杂改性聚苯胺的研究

选择丙烯酸 (AA)、丙烯酸丁酯 (BA)和甲基丙烯酸甲酯 (MMA)三元共聚物对聚苯胺 (PAn)进行改性 ,研究了BA的用量和引发剂浓度对PAn导电率的影响 ,对样品进行DSC、FTIR和SEM测试。结果表明 ,丙烯酸酯三元共聚物酸对PAn有良好的掺杂改性作用 ,当共聚单体 (AA -BA -MMA)组成为 10∶45∶45 (质量比 ) ,引发剂浓度为0 0 5 48mol·L-1时 ,可制得电导率达 1 42 1S·cm-1的导电PAn。     

聚苯胺盐的合成及导电性能研究

用对甲苯磺酸作为掺杂剂对聚苯胺(PANI)进行掺杂，合成了导电聚苯胺盐(ES)。研究了掺杂剂用量、模压压力、模压温度、氧化剂用量对聚苯胺盐电导率的影响。结果表明：随着掺杂剂用量的增加，PANI的电导率也在不断的增大；当ES所受压力较高时，电导率提高；高温使PANI电导率上升；氧化剂与苯胺的最佳配比为1：1。     

Solid-state NMR study of N labelled polyaniline upon reaction with DPPH

The quantitative investigation of the radical scavenging properties of polyaniline (PANI) upon reaction with excess of the stable DPPH radical (a 4:1 ratio of DPPH to aniline units in the polymer) was carried out using ¹⁵N and ¹³C solid state NMR spectroscopy. During the process the polyaniline was oxidised so that the imine content increased from 45 to 65%. The extent of oxidation measured by NMR was confirmed by N1s XPS analysis. However, within a 30 min reaction time, about 85% of the DPPH radicals were scavenged as monitored by the decay in its EPR signal. This is about 20 times greater than the fraction of DPPH required to oxidize PANI from an imine content of 45-65%. An identification of further redox processes is required to explain the high degree of radical scavenging. At the same time, there was no evidence of significant chemical binding or trapping of DPPH in the PANI structure.     

Electrochemical capacitance of well-coated single-walled carbon nanotube with polyaniline composites

Well-coated single-walled carbon nanotube (SWNT) with polyaniline (PANI) composite electrodes with good uniformity for electrochemical capacitors are prepared by the polymerization of aniline containing well-dissolved SWNTs. The capacitance properties are investigated with cyclic voltammetry, charge-discharge tests and ac impedance spectroscopy. The composite electrode shows much higher specific capacitance, better power characteristics and is more promising for application in capacitor than pure PANI electrode. The effect and role of SWNT in the composite electrode are also discussed in detail.