Effect of microstructural features on the corrosion behavior of severely deformed Al–Mg–Si alloy

The aim of this study was to determine the influence of severe plastic deformation processing and the changes in microstructure resulting therefrom on the corrosion resistance of an Al–Mg–Si alloy. The alloy was processed using incremental equal channel angular pressing, which caused a reduction in grain size from 15 to 0.9 µm. The grain refinement was accompanied by an increase in the number of grain boundaries and dislocations, and by changes in grain orientation. However, there was no change in the size and number of intermetallic particles, which presumably resulted in a constant number of galvanic couplings. Electrochemical experiments revealed only slight differences between the samples before and after processing. Higher potential transients/oscillations upon immersion and increased corrosion currents in the vicinity of corrosion potential point to slightly higher reactivity of the most refined material. This indicates that intermetallic particles are the most crucial microstructural elements in terms of corrosion resistance. Their impact exceeds that of grain boundaries, in particular, at the stage of corrosion initiation. The development of corrosion attack is controlled more by the microstructure of the matrix as the grain refinement resulted in a less pronounced corrosion attack in comparison with the coarse-grained sample.     

Interface regulation effects on mechanical behavior of heterostructure Ti6Al4V/TiAl-based laminated composite sheets

Design of architectured composites with layered-ordered structure can solve the strength-toughness mismatch problem of structural materials. In the present study, heterostructure Ti6Al4V/TiAl laminated composite sheets with different thicknesses of interface layer and TiAl composite layer were successfully produced by hot-pressing technology. The effects of interface regulation and laminated structure on their mechanical properties, crack propagation, and fracture behavior were studied. The results indicated that compressive strength of the sheets increased with the decrease in interface thickness. Compressive strength of TiAl composite sheet with thicker composite layer reached 1481.55 MPa at the arrester orientation with sintering holding time of 40 min, which was 25.96% higher than that of the sheet obtained at 120 min. Analysis indicated that the interface area transferred stress through slip bands and through-interface cracks. Compressive strength at the divider orientation reached 1443.06 MPa, which was 45.78% higher than that of the sheet obtained at 120 min. In this case, the interface area transferred stress through slip bands and along-interface cracks. For TiAl composite sheets with thinner composite layer, compressive strength was further improved to 1631.01 MPa and 1594.66 MPa at the arrester and divider orientations with sintering holding time of 40 min, respectively. The ductile metal layer exerted a significant toughening effect. Both interface regulation and laminated structure transformation could enhance the hetero-deformation induced (HDI) strengthening and improve the comprehensive mechanical properties of the composite sheets.     

Auto-thermal reforming of acetic acid for hydrogen production by ZnxNiyCrOm±δ catalysts: Effect of Cr promoted Ni-Zn intermetallic compound

A series of Zn_xNi_yCrO_m±δ catalysts were synthesized via a typical co-precipitation method, in which Zn-Cr layered double hydroxides (LDHs) were found and Ni-Zn intermetallic compound (IMC) was formed after reduction in hydrogen. During auto-thermal reforming (ATR) of acetic acid (HAc), the Ni-Zn IMC was transformed into Ni/(amorphous-ZnO)-ZnCr₂O₄ species with uniformed distribution and appropriate interaction within these Ni-Zn-Cr-O species; besides, the adsorbed oxygen promoted the activation and transfer of oxygen species; therefore, deactivation by oxidation, sintering and coking was inhibited. And the optimized Zn_2.37Ni_0.63CrO_4.5±δ catalyst presented high activity and stability in a 45-h ATR test with HAc conversion near 100% and hydrogen yield at 2.7 mol-H₂/mol-HAc, showing potential for hydrogen production via ATR of HAc.     

316L不锈钢金属间相固溶过程中的微结构表征

利用扫描电镜、X射线衍射仪和电子背散射衍射仪等设备研究了热轧态316L不锈钢金属间相(σ相和χ相)在固溶过程中的微结构演变规律,同时,利用高温激光共聚焦显微镜对金属间相回溶的全过程进行了原位在线观察,确定了最佳固溶温度。结果表明,固溶过程中发生了γ+σ+χ→γ+σ+χ+α/FeCr→γ+α/FeCr的相变过程。金属间相的回溶从1033.1℃开始到1149.5℃结束,回溶时间为21s,消除金属间相的最佳固溶温度约为1150℃。固溶处理前,基体中分布的带状组织形态不规则,χ相和σ相的面积比分别为0.46%和0.94%;固溶处理后,带状组织形态一致,主要分布铁素体和FeCr相,而χ相和σ相不可见。     

Evaluation of Ca-doped BaZrO3 as the crucible refractory for melting TiAl alloys

In this study, a new Ca-doped BaZrO₃ refractory was designed by using thermodynamics approaches and tested for its applicability for vacuum induction melting (VIM) of TiAl alloys. The influence of CaO on the BaZrO₃ phase constitution and microstructure, as well as the key features of the TiAl melt interaction with the Ca-doped BaZrO₃ crucibles were investigated by X-ray diffraction (XRD), optical microscopy (OM) and scanning electron microscopy (SEM). Results revealed that the Ca-doped BaZrO₃ refractory consisted of Ba_1-xCa_xZrO₃ and CaO phases. An obvious interaction occurred during the melting of the TiAl alloy in the Ca-doped BaZrO₃ crucible along with the generation of BaAl₂O₄ as a reaction product, with formation of a reaction layer up to 5?µm thick. Dissolution of Ca-doped BaZrO₃ refractory in the TiAl melt was the main reason for the alloy-crucible reaction. Moreover, the Ca-doped BaZrO₃ crucible was found to substantially reduce the contamination of the TiAl alloy, with lower oxygen concentration as compared with other conventional oxide crucibles. Overall results confirmed that vacuum induction melting using the Ca-doped BaZrO₃ refractory can be considered as an appropriate method for the fabrication of TiAl alloys.     

Effect of intermetallics on susceptibility of Mg alloy welds to liquation cracking

ABSTRACT

The circular-patch welding test was used to study the liquation and liquation cracking of AZ-series Mg alloys. A heat treatment was carried out on the as-received AZ91 alloy to dissolve the γ(Mg₁₇Al₁₂) particles before welding. The circular-patch welding test was then conducted on the heat-treated, as-received AZ91 alloy using AZ61 and AZ91 filler wires. The results showed that the susceptibility of AZ91 alloy to liquation and liquation cracking was significantly reduced by the dissolution of massive γ(Mg₁₇Al₁₂) particles via a heat treatment before welding as the liquation mechanism was changed. Both constitutional liquation and incipient melting occurred in the partially melted zone of the as-received AZ91 welds, while only incipient melting occurred in the heat-treated AZ91 welds.