Development and characterisation of a Y2Ti2O7-based glass-ceramic as a potential oxidation protective coating for titanium suboxide (TiOx)

A silica-based glass-ceramic, with Y₂Ti₂O₇ as the major crystalline phase, is designed, characterised and tested as an oxidation-protective coating for a titanium suboxide (TiO_x) thermoelectric material at temperatures of up to 600 °C. The optimised sinter-crystallisation treatment temperatures are found to be 1300 °C and 855 °C for a duration of 30 min, and this treatment leads to a glass-ceramic with cubic Y₂Ti₂O₇ and CaAl₂Si₂O₈ as crystalline phases. An increase of ~270 °C in the dilatometric softening temperature is observed after devitrification of the parent glass, thus further extending its working temperature range.Excellent adhesion of the glass-ceramic coating to the thermoelectric material is maintained after exposure to a temperature of 600 °C for 120 h under oxidising conditions, thus confirming the effectiveness of the T1 glass-ceramic in protecting the TiO_x material.     

Novel TiC-based composites with enhanced mechanical properties

Novel TiC-based composites were synthesized by reactive hot-pressing at 1800 °C for 1 h with ZrB₂ addition as a sintering aid for the first time. The effects of ZrB₂ contents on the phase composition, microstructure evolution, and mechanical properties were reported. Based on the reaction and solid solution coupling effects between ZrB₂ and TiC, the product ZrC may be partially or completely dissolved into the TiC matrix, and then phase separation within the miscibility gap is observed to form lamellar nanostructured ZrC-rich (Zr, Ti)C. The TiC-10 mol.% ZrB₂ (starting batch composition) exhibits good comprehensive mechanical properties of hardness 27.7 ± 1.3 GPa, flexural strength 659 ± 48 MPa, and fracture toughness of 6.5 ± 0.6 MPa m^1/2, respectively, which reach or exceed most TiC-based composites using ceramics as sintering aids in the previous reports.     

Enhanced mechanical properties of porous titanium implants via in-situ synthesized titanium carbide in lamellar pore walls

Directional lamellar porous titanium scaffolds are widely used as bone implant bearing materials because of their anisotropic pore structure. Their mechanical properties can be effectively improved by enhancing the strength of pore walls through the introduction of ceramics. In this work, porous titanium implants were prepared by freeze casting combined with TiH₂ decomposition. The graphene was introduced into the pore walls of porous titanium, which could transform into titanium carbide (TiC) in situ upon sintering. TiC was evenly distributed in the lamellar pore walls, and the interface was well bonded. The compression strength of the fabricated implants was up to 389.94 MPa when the graphene content was 3 wt%, which was 377.8% times as high as the porous titanium. The crack propagation was resisted by TiC because of the “pinning” effect on the pore wall. Some of TiC were pulled out from the matrix, and others were fractured. The strength of the fabricated implants was improved significantly by the large consumption of fracture energy. Also, fabricated porous titanium implants with TiC are suitable for bone implantation.     

Crystalline phase of TiO2 nanotube arrays on Ti–35Nb–4Zr alloy: Surface roughness,electrochemical behavior and cellular response

An investigation was made into the electrochemical, structural and biological properties of self-organized amorphous and anatase/rutile titanium dioxide (TiO₂) nanotubes deposited on Ti–35Nb–4Zr alloy through anodization-induced surface modification. The surface of as-anodized and heat-treated TiO₂ nanotubes was analyzed by field emission scanning electron microscopy (FE-SEM), revealing morphological parameters such as tube diameter, wall thickness and cross-sectional length. Glancing angle X-ray diffraction (GAXRD) was employed to identify the structural phases of titanium dioxide, while atomic force microscopy (AFM) was used to measure surface roughness associated with cell interaction properties. The electrochemical stability of TiO₂ was examined by electrochemical impedance spectroscopy (EIS) and the results obtained were correlated with the microstructural characterization. The in vitro bioactivity of as-anodized and crystallized TiO₂ nanotubes was also analyzed as a function of the presence of different TiO₂ polymorphic phases. The results indicated that anatase TiO₂ showed higher surface corrosion resistance and greater cell viability than amorphous TiO₂, confirming that TiO₂ nanotube crystallization plays an important role in the material's electrochemical behavior and biocompatibility.     

1D sub 10 nm nanofabrication of ultrahydrophobic Ag@TiO2 nanowires and their photocatalytic,UV shielding and antibacterial properties

Here we report the synthesis of 1D TiO₂ sub 10 nm nanowires through one pot hydrothermal method in an alkaline NaOH medium at 95 °C for 36 h. Further, these TiO₂ nanowires were embellished with silver (Ag) using polyvinylpyrrolidone (PVP) and ethylene glycol (EG) based solvothermal route at 160 °C for 4 h. With Ag decoration the photocatalytic activity was enhanced and the complete photooxidation of Methylene Blue (MB) was achieved in 35 min under optimized conditions. Super- and ultra-hydrophobic coating on cotton fabric exhibited a consistent antibacterial activity with enhanced UV-blocking property. Enhanced multifunctional properties observed were primarily attributed to the formation of Ag decorated 1D sub 10 nm TiO₂ nanowires heterojunctions achieved using facile chemical route. Hence, such multiple functionalities make the 1D sub 10 nm TiO₂ nanowires good candidate for industrial and domestic wastewater treatment.     

Bimetallic platinum–ruthenium nanoparticles immobilized on reduced graphene oxide-TiO2 (RGO-TiO2) support for ethanol electro oxidation in acidic media

The present work addresses the potentialities of Pt–Ru nanoparticles deposited on a graphene oxide (RGO) and TiO₂ composite support towards electrochemical oxidation of ethanol in acidic media relevant for fuel cell applications. To immobilize platinum–ruthenium bimetallic nanoparticles on to an RGO-TiO₂ nanohybrid support a simple solution-phase chemical reduction method is utilized. An examination using electron microscopy and energy dispersive X-ray spectroscopy (EDS) indicated that Pt–Ru particles of 4–8 nm in diameter are dispersed on RGO-TiO₂ composite support. The corresponding Pt–Ru/RGO-TiO₂ nanocomposite electrocatalyst was studied for the electrochemical oxidation of ethanol in acidic media. Compared to the commercial Pt–Ru/C and Pt/C catalysts, Pt–Ru/RGO-TiO₂ nanocomposite yields higher mass-specific activity of about 1.4 and 3.2 times, respectively towards ethanol oxidation reaction (EOR). The synergistic boosting provided by RGO-TiO₂ composite support and Pt–Ru ensemble together contributed to the observed higher EOR activity and stability to Pt–Ru/RGO-TiO₂ nanocomposite compared with other in-house synthesized Pt–Ru/RGO, Pt/RGO and commercial Pt–Ru/C and Pt/C electrocatalysts. Further optimization of RGO-TiO₂ composite support provides opportunity to deposit many other types of metallic nanoparticles onto it for fuel cell electrocatalysis applications.     

B4C–TiB2 composites fabricated by hot pressing TiC–B mixtures: The effect of B excess

Previous research have reported that B₄C–TiB₂ composites could be prepared by the reactive sintering of TiC–B powder mixtures. However, due to spontaneous oxidation of raw powders, using TiC–B powder mixtures with a B/TiC molar ratio of 6: 1 introduced an intermediate phase of C during the sintering process, which deteriorated the hardness of the composites. In this report, the effects of B excess on the phase composition, microstructure, and mechanical properties of B₄C–TiB₂ composites fabricated by reactive hot pressing TiC–B powder mixtures were investigated. XRD and Raman spectra confirmed that lattice expansion occurred in B-rich boron carbide and B_xC–TiB₂ (x > 4) composites were obtained. The increasing B content improved the hardness and fracture toughness but decreased the flexural strength of B_xC–TiB₂ (x > 4) composites. When the molar ratio of B/TiC increased from 6.6:1 to 7.8:1, the Vickers hardness and the fracture toughness of the composites were enhanced from 26.7 GPa and 4.53 MPa m^1/2 to 30.4 GPa and 5.78 MPa m^1/2, respectively. The improved hardness was attributed to the microstructural improvement, while the toughening mechanism was crack deflection, crack bridging and crack branching.     

Performance of BaZrO3/Y2O3 dual-phase refractory applied to TiAl alloy melting

Vacuum induction melting is a potential process for the preparation of TiAl alloys with good homogeneity and low cost. But the crucial problem is a selection of high stability refractory. In this study, a BaZrO₃/Y₂O₃ dual-phase refractory was prepared and its performance for melting TiAl alloys was studied and compared with that of a Y₂O₃ refractory. The results showed the dual-phase refractory consisted of BaZr_1-xY_xO_3-δ and Y₂O₃(ZrO₂), exhibited a thinner interaction layer (30 μm) than the Y₂O₃ refractory (90 μm) after melting the TiAl alloy. Although the TiAl alloys melted in the dual-phase and Y₂O₃ refractory exhibited similar oxygen contamination (<0.1 wt%), the alloy melted in the dual-phase refractory had smaller Y₂O₃ inclusion content and size than that in the Y₂O₃ refractory, indicating that the dual-phase refractory exhibited a better melting performance than the Y₂O₃ refractory. This study provides insights into the process of designing highly stable refractory for melting TiAl alloys.     

Dye removal by polymer derived ceramic nanobeads

Emulsion processed polymer derived ceramic (PDC) nanobeads are used for Methylene Blue dye removal from aqueous solutions. The PDC nanobeads, produced at 600 °C and 1200 °C pyrolysis, are subsequently coated with titania (anatase). Titania-coated nanobeads show less than 35%, i.e., limited dye adsorption capability in dark. Instead, enhanced total removal efficiency (∼97%) is obtained when the initial adsorption is succeeded by photodegradation under UV. Direct reusability tests show that even after the third cycle, very high regeneration efficiencies being above 92% are observed for titania-coated nanobeads.     

A review study on titanium niobium oxide-based composite anodes for Li-ion batteries: Synthesis,structure, and performance

The growing demands for Li-ion batteries (LIBs) in the electrification revolution, require the development of advanced electrode materials. Recently, intercalating titanium niobium oxide (TNO) anode materials with the general formula of TiNb_xO_2+2.5x have received lots of attention as an alternative to graphite and Li₄Ti₅O₁₂ commercial anodes. The desirability of this family of compounds stems from their high theoretical capacities (377–402 mAh/g), high safety, high working voltage, excellent cycling stability, and significant pseudocapacitive behavior. However, the rate performance of TNO-based anodes is poor owing to their low electronic and ionic conductivities. TNO-based composites generally are prepared with two aims of enhancing the conductivity of TNO and achieving a synergic effect between the TNO and the other component of the composite. Compositing with carbon matrices, such as graphene and carbon nanotubes (CNTs) are the most studied strategy for improving the conductivity of TNO and optimizing its high-rate performance. Also, for obtaining anode materials with high capacity and high long-term stability, the composites of TNO with transition metal dichalcogenides (TMDs) materials were proposed in previous literature. In this work, a comprehensive review of the TNO-based composites as the anodes for LIBs is presented which summarizes in detail the main recent literature from their synthesis procedure, optimum synthesis parameters, and the obtained morphology/structure to their electrochemical performance as the LIBs anode. Finally, the research gaps and the future perspective are proposed.