Effect of microstructural features on the corrosion behavior of severely deformed Al–Mg–Si alloy

The aim of this study was to determine the influence of severe plastic deformation processing and the changes in microstructure resulting therefrom on the corrosion resistance of an Al–Mg–Si alloy. The alloy was processed using incremental equal channel angular pressing, which caused a reduction in grain size from 15 to 0.9 µm. The grain refinement was accompanied by an increase in the number of grain boundaries and dislocations, and by changes in grain orientation. However, there was no change in the size and number of intermetallic particles, which presumably resulted in a constant number of galvanic couplings. Electrochemical experiments revealed only slight differences between the samples before and after processing. Higher potential transients/oscillations upon immersion and increased corrosion currents in the vicinity of corrosion potential point to slightly higher reactivity of the most refined material. This indicates that intermetallic particles are the most crucial microstructural elements in terms of corrosion resistance. Their impact exceeds that of grain boundaries, in particular, at the stage of corrosion initiation. The development of corrosion attack is controlled more by the microstructure of the matrix as the grain refinement resulted in a less pronounced corrosion attack in comparison with the coarse-grained sample.     

退火温度对HA/Ti-24Nb-4Zr复合材料组织与性能的影响

利用放电等离子烧结(SPS)技术制备了HA/Ti-24Nb-4Zr生物复合材料,研究了不同退火温度对复合材料显微组织和力学性能(抗压强度、屈服强度、屈强比、压缩弹性模量)的影响。结果表明,烧结态复合材料主要由β-Ti相、少量初生α-Ti相及HA相组成;随着退火温度的升高,复合材料基体中β-Ti相含量增多且晶粒逐渐长大,针状次生α-Ti相在晶界处和晶内不断析出,HA相结构和含量变化不大;与烧结态相比,不同退火温度处理后的复合材料强度和弹性模量先略微上升后下降,而塑韧性呈不断提高趋势;复合材料在850 ℃退火处理后,抗压强度、屈服强度、屈强比和压缩弹性模量值分别为1507 MPa、1270 MPa、0.84和42 GPa,塑韧性得到明显改善,作为生物医用植入材料具有潜在的应用前景。     

Characterisation of the microplasma spraying of biocompatible coating of titanium

This paper presents new results of studying the influence of parameters of microplasma spraying (MPS) of Ti wire on the structure and properties of Ti coatings. Based on the design of the experiment and the results of the SEM study, certain spraying modes were chosen to form the desired composition and structure of the Ti coating.  The dense sublayer (up to 300 µm thick) provides good adhesion to the substrate, and a porous top layer can accelerate the coated implant ingrowth with the bone.  This technology is developed for the manufacture of coated endoprosthesis implants.     

Microstructure−fracture toughness relationships and toughening mechanism of TC21 titanium alloy with lamellar microstructure

The independent influence of microstructural features on fracture toughness of TC21 alloy with lamellar microstructure was investigated. Triple heat treatments were designed to obtain lamellar microstructures with different parameters, which were characterized by OM and SEM. The size and content of α plates were mainly determined by cooling rate from single β phase field and solution temperature in two-phase field; while the precipitation behavior of secondary α platelets was dominantly controlled by aging temperature in two-phase field. The content and thickness of α plates and the thickness of secondary α platelets were important microstructural features influencing the fracture toughness. Both increasing the content of α plates and thickening α plates (or secondary α platelets) could enhance the fracture toughness of TC21 alloy. Based on energy consumption by the plastic zone of crack tip in α plates, a toughening mechanism for titanium alloys was proposed.     

Ti改性催化裂化汽油选择加氢催化剂的研究

以氢氧化铝干胶和偏钛酸为主要原料制备了Al2O3-TiO2载体，采用等体积浸渍法制备出一系列不同TiO2含量及不同配体改性的CoMo/Al2O3-TiO2催化剂；采用BET，XRD，TPR，HRTEM等方法对所制备的催化剂进行了表征，在10 mL固定床评价装置上对所制备的两个系列催化剂进行了FCC汽油选择加氢脱硫活性评价。结果表明，载体中TiO2的质量分数为10%、浸渍液中添加乙二醇和磷酸改性的催化剂具有较高的加氢脱硫活性和选择性。     

不同方法发酵的酸豆角品质对比分析

本文将研究不同方法发酵的酸豆角品质对比分析。选取质地嫩脆、条形均匀、无病虫害的新鲜豆角为泡制原料。采用自然干法发酵、自然湿法发酵与纯种湿法发酵的发酵方法制作酸豆角。检测发酵过程中，pH值、还原糖含量、总酸含量、总糖含量、亚硝酸盐含量以及氨基酸态氮含量，分析纯种湿法发酵与自然湿法发酵对酸豆角品质的影响。结果表明：纯种湿法发酵25 d后，其pH值和还原糖含量分别为3.92、0.03%，均高于自然湿法发酵；总酸、总糖、亚硝酸盐含量、氨基酸态氮含量分别为0.25%、0.04%、0.01 mg/kg和0.01%，均低于自然湿法发酵。另外，纯种湿法发酵酸豆角的甲氧基乙酸含量为0.37%，乙酸乙酯为0.51%，含水量为81.15%，感官评分为45.52，均高于自然干法发酵。纯种湿法发酵对酸豆角品质的效果最好，亚硝酸盐的含量在发酵后期显著降低，感官评分较高，对豆角工业化生产提供了较好的参考价值。     

应用M-MIVM预测含钛渣系组元活度

 在钢铁冶炼过程中,随着护炉钛材料和含钛铁矿石的应用,大量的含钛炉渣被生产出来。由于缺少多元含钛渣系的热力学数据,限制了钛资源综合利用技术的深入发展。因此,应用改进的分子相互作用体积模型(M-MIVM(FII)),预测了基础渣系Al₂O₃-CaO-SiO₂、FeO-MnO-SiO₂和含钛渣系FeO-MnO-TiO₂、FeO-SiO₂-TiO₂、MnO-SiO₂-TiO₂、Al₂O₃-CaO-FeO-TiO₂中各组元活度,并与试验值比较。结果表明,M-MIVM(FII)的预测值与试验值符合较好,6个体系总的平均相对误差为11%,该精度处于Turkdogan提出的30%以内的试验误差范围; M-MIVM(FII)在参数拟合与活度预测能力方面均优于MIVM,该模型对多元含钛熔渣体系组元活度具有更好的预测效果。在此基础上,应用M-MIVM(FII)预测Al₂O₃-CaO-SiO₂-TiO₂熔体中TiO₂活度,并分析其影响因素。结果表明,TiO₂活度预测值与试验值吻合良好,且随炉渣碱度、Al₂O₃含量的增加而降低,该规律与试验规律相一致。M-MIVM(FII)仅通过拟合子二元系活度或者直接由无限稀活度系数就能够预测多元熔体的热力学性质。     

细粒尾矿综合利用技术研究

姑山矿业公司为提高细粒尾矿的综合利用率，研究分析了细粒尾矿的性质，系统研究了尾矿含量、煅烧工艺制度对不同成分体系尾矿陶粒堆积密度、表观密度、空隙率、吸水率、筒压强度及软化系数的影响。研究得出了全尾矿陶粒、细粒尾矿+污泥陶粒、细粒尾矿+污泥+粉煤灰陶粒3种成分体系的尾矿陶粒较优的尾矿含量及煅烧工艺制度，且3种尾矿陶粒均可代替石头用作粗集料。