Effect of microstructural features on the corrosion behavior of severely deformed Al–Mg–Si alloy

The aim of this study was to determine the influence of severe plastic deformation processing and the changes in microstructure resulting therefrom on the corrosion resistance of an Al–Mg–Si alloy. The alloy was processed using incremental equal channel angular pressing, which caused a reduction in grain size from 15 to 0.9 µm. The grain refinement was accompanied by an increase in the number of grain boundaries and dislocations, and by changes in grain orientation. However, there was no change in the size and number of intermetallic particles, which presumably resulted in a constant number of galvanic couplings. Electrochemical experiments revealed only slight differences between the samples before and after processing. Higher potential transients/oscillations upon immersion and increased corrosion currents in the vicinity of corrosion potential point to slightly higher reactivity of the most refined material. This indicates that intermetallic particles are the most crucial microstructural elements in terms of corrosion resistance. Their impact exceeds that of grain boundaries, in particular, at the stage of corrosion initiation. The development of corrosion attack is controlled more by the microstructure of the matrix as the grain refinement resulted in a less pronounced corrosion attack in comparison with the coarse-grained sample.     

Synthesis and slurry spray coating of barium strontium alumino silicate on SiC substrate

Barium strontium alumino silicate (BSAS); (Ba_0.6Sr_0.4Al₂Si₂O₈) was synthesized through solid state reaction between BaCO₃, SrCO₃, Al₂O₃ and SiO₂ subjected to wet milling in isopropanol for about 24 h. The sequence of the solid state reaction was studied by subjecting to DG/DTG from room temperature to 1550 °C. The crystallographic phase evolution was confirmed by X-ray diffraction of the powders calcined in the range 1000 to 1300 °C for 2 h. The monoclinic celsian phase obtained at 1300 °C, pelletized through uniaxial pressing was sinterable to 67 to 78% density in the temperature range of 1300 to 1500 °C. The density improved to 75 to 94% after ball milling for 76 h, while ZrO₂ addition further improved the density by 2%. The celcian phase of BSAS was dispersed in isopropyl alcohol, milled for about 24 h and spray coated on to plain SiC and mullite precoated SiC substrates. Sintering of coated samples and characterization for weight gain/loss, microstructure, scratch test prove that mullite + BSAS coating is more effective than single layer coating of BSAS on SiC substrates.     

杂化包覆玄武岩鳞片/环氧涂料制备与性能

本文在环氧涂料中添加玄武岩鳞片，提高其防腐蚀性能。针对玄武岩鳞片的团聚问题，通过机械力化学改性工艺，采用正硅酸四乙酯、HY-311型钛酸酯偶联剂、E-44型环氧树脂对玄武岩鳞片进行杂化包覆，结果表明，杂化包覆后玄武岩鳞片的沉降时间从2h提高至96 h。杂化包覆玄武岩鳞片添加量为20%涂层的性能最优，附着力为13.40 MPa，耐盐雾时间为2000 h，在3.5%NaCl溶液中浸泡2000 h后，0.01 Hz的阻抗模值仍然有5.15×109 Ω·cm2。     

Thermal depolarization and electromechanical hardening in Zn2+-doped Na1/2Bi1/2TiO3-BaTiO3

Na_1/2Bi_1/2TiO₃-based materials have been earmarked for one of the first large-volume applications of lead-free piezoceramics in high-power ultrasonics. Zn²⁺-doping is demonstrated as a viable route to enhance the thermal depolarization temperature and electromechanically harden (1-y)Na_1/2Bi_1/2TiO₃-yBaTiO₃ (NBT100yBT) with a maximum achievable operating temperature of 150 °C and mechanical quality factor of 627 for 1 mole % Zn²⁺-doped NBT6BT. Although quenching from sintering temperatures has been recently touted to enhance T_F-R, with quenching the doped compositions featuring an additional increase in T_F-R by 17 °C, it exhibits negligible effect on the electromechanical properties. The effect is rationalized considering the missing influence on conductivity and therefore, negligible changes in the defect chemistry upon quenching. High-resolution diffraction indicates that Zn²⁺-doped samples favor the tetragonal phase with enhanced lattice distortion, further corroborated by ²³Na Nuclear Magnetic Resonance investigations.     

Water vapor volatilization and oxidation induced surface cracking of environmental barrier coating systems: A numerical approach

A numerical model is developed for surface crack propagation in brittle ceramic coatings, aiming at the intrinsic failure of rare-earth silicate environmental barrier coating systems (EBCs) under combustion conditions in advanced gas turbines. The main features of progressive degradation of EBCs in such conditions are captured, including selective silica vaporization in the top coat due to exposure to water vapor, diffusion path-dependent bond coat oxidation, as well as crack propagation during cyclic thermal loading. In light of these features, user-defined subroutines are implemented in finite element analysis, where surface crack growth is simulated by node separation. Numerical results are validated by existing experimental data, in terms of monosilicate layer thickening, thermal oxide growth, and fracture behaviors. The experimentally observed quasi-linear oxidation in the early stage is also elucidated. Furthermore, it is suggested that surface crack undergoes rapid propagation in the late stage of extended thermal cycling in water vapor and leads to catastrophic failure, driven by both thermal mismatch and oxide growth stresses. The latter is identified as the dominant mechanism of penetration. Based on detailed analyses of failure mechanisms, the optimization strategy of EBCs composition is proposed, balancing the trade-off between mechanical compliance and erosion resistance.     

Effects of Cu on the corrosion behavior and microstructure of Mg–Zn–Ca bulk metallic glass

For the purpose of developing biodegradable magnesium alloys with suitable properties for biomedical applications, Mg–Zn–Ca–Cu metallic glasses were prepared by copper mold injection methods. In the present work, the effect of Cu doping on mechanical properties, corrosion behavior, and glass-forming ability of Mg₆₆Zn₃₀Ca₄ alloy was studied. The experimental findings demonstrated that the incorporation of Cu decreases the corrosion resistance of alloys, but increases the microhardness and degradation rate slightly. However, the addition of a trace amount of Cu can make the samples have antibacterial properties. Therefore, Mg–Zn–Ca–Cu has great advantages in clinical implantation and is the potential implant material.     

Inhibited intracrystalline cracks and enhanced electrochemical properties of NCM811 cathode materials coated by EPS

The formation of micro-cracks in Ni-rich LiNi_0.8Co_0.1Mn_0.1O₂ (NCM811) cathode particles is an extremely important factor affecting the electrochemical characteristics after long-term cycling. Generally, cracks can be divided into intergranular crack and intracrystalline crack according to their positions. Coating has been confirmed as a highly effective strategy to relieve intergranular cracks. However, the intracrystalline cracks of primary-like particles have rarely been studied. In this work, ethoxy functional polysiloxane (EPS) was directly coated on the surface of original NCM811 by tetraethyl orthosilicate (TEOS) hydrolytic polycondensation method without any additives. Then, the microstructure, micromorphology, surface state and electrochemical properties were investigated in detail by XRD, SEM, TEM, CV and EIS. The results displayed that the micro-cracks of primary-like particles were effectively suppressed under appropriate EPS coating. Accordingly, excellent capacity retention of 95.6% (100 cycles, 1C) and rate performance (144.6 mA h/g, 5C) were obtained. These improved mechanical and electrochemical properties are considered to be related to the EPS stress buffer layer, suppressed oxygen vacancies, inhibited phase transition and reduced volume change.     

Self-healing capacity of Mullite-Yb2SiO5 environmental barrier coating material with embedded Ti2AlC MAX phase particles

Repetitive heating and cooling cycles inevitably cause crack damage of hot gas components of gas turbine engines, such as blades and vanes. In this study the self-healing capacity is investigated of mullite + ytterbium monosilicate (Yb₂SiO₅) as EBC material with Ti₂AlC MAX phase particles embedded as a crack-healing agent. The effect of Ti₂AlC in the EBC was compared with the self-healing ability of the mullite + Yb₂SiO₅ material. After introducing cracks by Vickers indentation on the surface of each sample, crack healing was realized by controlling the temperature and time during the post-heat-treatment process. For the mullite + Yb₂SiO₅ composite with Ti₂AlC particles, crack healing occurred at 1000 °C, while in the case of the mullite + Yb₂SiO₅ composite without Ti₂AlC, a sustained temperature of 1300 °C or higher was required. Compared with the healing of the mullite + Yb₂SiO₅ composite by the formation of a eutectic phase, the addition of Ti₂AlC promoted healing via the oxidation of Ti and Al. Notably, the surface formation of a ternary oxide of Ti–Yb–O was confirmed, which completely covered the damage area. Consequently, the addition of a Ti₂AlC MAX phase to the EBC composite resulted in a complete strength recovery, while the mullite + Yb₂SiO₅ composite without Ti₂AlC showed a strength recovery of about 80%. Furthermore, by analyzing the indentation load–displacement curve to indicate the role of Ti₂AlC, the addition of Ti₂AlC improved both the hardness and stiffness of the composite.     

Development and characterisation of a Y2Ti2O7-based glass-ceramic as a potential oxidation protective coating for titanium suboxide (TiOx)

A silica-based glass-ceramic, with Y₂Ti₂O₇ as the major crystalline phase, is designed, characterised and tested as an oxidation-protective coating for a titanium suboxide (TiO_x) thermoelectric material at temperatures of up to 600 °C. The optimised sinter-crystallisation treatment temperatures are found to be 1300 °C and 855 °C for a duration of 30 min, and this treatment leads to a glass-ceramic with cubic Y₂Ti₂O₇ and CaAl₂Si₂O₈ as crystalline phases. An increase of ~270 °C in the dilatometric softening temperature is observed after devitrification of the parent glass, thus further extending its working temperature range.Excellent adhesion of the glass-ceramic coating to the thermoelectric material is maintained after exposure to a temperature of 600 °C for 120 h under oxidising conditions, thus confirming the effectiveness of the T1 glass-ceramic in protecting the TiO_x material.     

尿素14C胶囊中55Fe分析方法研究

为确保药品质量的可控性与安全性，需对尿素¹⁴C胶囊中的杂质核素⁵⁵Fe进行分析。本工作建立了尿素¹⁴C胶囊中⁵⁵Fe分析测量方法，样品经过AGMP-1阴离子交换树脂2次分离纯化后，用液体闪烁计数器（LSC）测量⁵⁵Fe的活度，同时计算了尿素¹⁴C胶囊样品中放射性杂质核素⁵⁵Fe的检测限，并对方法的专属性、耐用性和检测限进行了验证。结果表明，放射性杂质核素⁵⁵Fe的活度限值为小于等于¹⁴C活度的0.1%、干扰核素¹⁴C的去污因子大于10⁵、铁的化学回收率在57%～67%之间、测量1 h的检测限为0.4 Bq。