Influence of SiC microstructure on its corrosion behavior in molten FLiNaK salt

The influence of the microstructure on the corrosion rate of three monolithic SiC samples in FLiNaK salt at 900 °C for 250 h was studied. The SiC samples, labeled as SiC-1, SiC-2, and SiC-3, had corrosion rates of 0.137, 0.020, and 0.043 mg/cm²h, respectively. Compared with grain size and the presence of special grain boundaries (i.e., Σ3), the content of high-angle grain boundaries (HAGBs) appeared to have the strongest influence on the corrosion rate of SiC in FLiNaK salt, since the corrosion rate increased six times as the concentration of high-angle grain boundaries increased from 19 to 32% for SiC-2 and SiC-1, respectively. These results stress the importance of controlling the content of HAGBs during the production process of SiC.     

Distinct Pharmacological Properties of Gaseous CO and CO-Releasing Molecule in Human Platelets

Carbon monoxide (CO)—gaseous or released by CO-RMs—both possess antiplatelet properties; however, it remains uncertain whether the mechanisms involved are the same. Here, we characterise the involvement of soluble guanylate cyclase (sGC) in the effects of CO—delivered by gaseous CO–saturated buffer (CO_G) and generated by CORM-A1—on platelet aggregation and energy metabolism, as well as on vasodilatation in aorta, using light transmission aggregometry, Seahorse XFe technique, and wire myography, respectively. ODQ completely prevented the inhibitory effect of CO_G on platelet aggregation, but did not modify antiplatelet effect of CORM-A1. In turn, CO_G did not affect, whereas CORM-A1 substantially inhibited energy metabolism in platelets. Even though activation of sGC by BAY 41-2272 or BAY 58-2667 inhibited significantly platelet aggregation, their effects on energy metabolism in platelets were absent or weak and could not contribute to antiplatelet effects of sGC activation. In contrast, vasodilatation of murine aortic rings, induced either by CO_G or CORM-A1, was dependent on sGC. We conclude that the source (CO_G vs. CORM-A1) and kinetics (rapid vs. slow) of CO delivery represent key determinants of the mechanism of antiplatelet action of CO, involving either impairment of energy metabolism or activation of sGG.     

Computational Investigation Identified Potential Chemical Scaffolds for Heparanase as Anticancer Therapeutics

Heparanase (Hpse) is an endo-β-D-glucuronidase capable of cleaving heparan sulfate side chains. Its upregulated expression is implicated in tumor growth, metastasis and angiogenesis, thus making it an attractive target in cancer therapeutics. Currently, a few small molecule inhibitors have been reported to inhibit Hpse, with promising oral administration and pharmacokinetic (PK) properties. In the present study, a ligand-based pharmacophore model was generated from a dataset of well-known active small molecule Hpse inhibitors which were observed to display favorable PK properties. The compounds from the InterBioScreen database of natural (69,034) and synthetic (195,469) molecules were first filtered for their drug-likeness and the pharmacophore model was used to screen the drug-like database. The compounds acquired from screening were subjected to molecular docking with Heparanase, where two molecules used in pharmacophore generation were used as reference. From the docking analysis, 33 compounds displayed higher docking scores than the reference and favorable interactions with the catalytic residues. Complex interactions were further evaluated by molecular dynamics simulations to assess their stability over a period of 50 ns. Furthermore, the binding free energies of the 33 compounds revealed 2 natural and 2 synthetic compounds, with better binding affinities than reference molecules, and were, therefore, deemed as hits. The hit compounds presented from this in silico investigation could act as potent Heparanase inhibitors and further serve as lead scaffolds to develop compounds targeting Heparanase upregulation in cancer.     

高稳高效海上风电安装平台关键制造技术研究

海上风电作为可再生清洁能源之一,受到世界各国的高度重视与大力发展。我国将海上风电提升至解决能源危机、减缓气候变化、调整能源结构的国家战略高度,到2030年我国单位国内生产总值二氧化碳排放将比2005年下降65%以上,非化石能源占一次能源消费比重将达到25%左右。安装平台不足将是我国海上风电场无法如期建成投产的主要障碍。对自升自航式海上风电安装平台系列高端装备及其设计制造的三大技术难题——腿站立作业易“失稳”、大平台大跨距大倾覆力矩自升易“失控”、高空吊装巨型叶片逾百螺栓精准定位易“失准”,以及焊缝缺陷修复和局部裂纹损伤的激光锻造修复再制造进行了介绍,研制的具有不同规格的系列装备在中国、英国、丹麦、德国等国家的著名海上风电场建设应用情况良好。     

Highly oriented α-Al2O3 transparent ceramics shaped by shear force

Alumina platelets were arranged horizontally in submicron alumina particles by shear force in the flow of slurries during casting. The obtained alumina green bodies with platelets were pressureless-sintered in vacuum, producing ceramics with thoroughly oriented grains and high transmittance. The effects of sintering parameters on the densification, microstructure evolution, and orientation degree of alumina ceramics were investigated and discussed. The results showed that the densification, grain size, orientation degree, and in-line transmittance were increased with increasing sintering temperature. The enhancement of orientation degree was mainly coherent with grain growth. The grain-oriented samples exhibited a much higher in-line transmittance (at 600 nm) of 61 % than that of the grain random sample (29 %). Moreover, the transmission remained a high level in the ultraviolet range (<300 nm).     

Achieving excellent energy storage density of Pb0.97La0.02(ZrxSn0.05Ti0.95-x)O3 ceramics by the B-site modification

The applications of antiferroelectric (AFE) materials in miniaturized and integrated electronic devices are limited by their low energy density. To address the above issue, the antiferroelectricity of the reinforced material was designed to improve its AFE-ferroelectric (FE) phase transition under electric fields. In this present study, the composition of Zr⁴⁺ (0.72 Å) and Ti⁴⁺ (0.605 Å) at B-site of Pb_0.97La_0.02(Zr_xSn_0.05Ti_0.95-x)O₃ ceramics with orthogonal reflections are synthesized via the tape-casting method. These ceramics are modified to enhance their antiferroelectricity by reducing their tolerance factor. A recoverable energy storage density W_rec 12.1 J/cm³ was obtained for x = 0.93 under 376 kV/cm, which is superior value than reported until now in lead-based energy storage systems. Moreover, the discharge energy density can reach 10.23 J/cm³, and 90 % of which can be released within 5.66 μs. This work provides a new window and potential materials for further industrialization of pulse power capacitors.     

Bi-templated grain growth maximizing the effects of texture on piezoelectricity

Templated grain growth is beneficial for piezoelectric materials, the properties of which become the best in their single crystalline form. Nevertheless, a textured ceramic prepared by a templated grain growth technique often fails in exhibiting as good properties as expected in single crystals even with a high degree of orientation factor. Here, we propose a new strategy for maximizing texturing effect by suppressing the growth of untextured matrix grains. The textured ceramics made by our method, so-called bi-templated grain growth, are featured by ultrahigh piezoelectric properties (d₃₃ = ～1,031 pC/N, d?g = ～59,000, k_p = ～0.76). A special emphasis is on the achieved electric-field-induced strain of 0.13 % at 1 kV/mm, which is as high as that of single crystals. This work demonstrates that not only the degree of texture but also the coarsening of untextured matrix grains should be well-controlled to best exploit the templated grain growth technique.     

Structural dependence of microwave dielectric properties in ilmenite-type Mg(Ti1-xNbx)O3 solid solutions by Rietveld refinement and Raman spectra

Mg(Ti_1-xNb_x)O₃ (x = 0–0.09) ceramics were prepared by the conventional solid-state reaction method. The phase composition, sintering characteristics, microstructure and dielectric properties of Ti⁴⁺ replacement by Nb⁵⁺ in the formed solid solution Mg(Ti_1-xNb_x)O₃ (x = 0–0.09) ceramics were systematically studied. The structural variations and influence of Nb⁵⁺ doping in Mg(Ti_1-xNb_x)O₃ were also systematically investigated by X-ray diffraction and Raman spectroscopy, respectively. X-ray diffraction and its Rietveld refinement results confirmed that Mg(Ti_1-xNb_x)O₃ (x = 0–0.09) ceramics crystallised into an ilmenite-type with R-3 (148) space group. The replacement of the low valence Ti⁴⁺ by the high valence Nb⁵⁺ can improve the dielectric properties of Mg(Ti_1-xNb_x)O₃ (x = 0–0.09). This paper also studied the different sintering temperatures for Mg(Ti_1-xNb_x)O₃ (x = 0–0.09) ceramics. The obtained results proved that 1350 °C is the best sintering temperature. The permittivity and Q × f initially increased and then decreased mainly due to the effects of porosity caused by the sintering temperature and the doping amount of Nb₂O₅, respectively. Furthermore, the increased Q × f is correlated to the increase in Ti–O bond strength as confirmed by Raman spectroscopy, and the electrons generated by the oxygen vacancies will be compensated by Nb⁵⁺ to a certain extent to suppress Ti⁴⁺ to Ti³⁺, which was confirmed by XPS. The increase in τ_f from ?47 ppm/°C to ?40.1 ppm/°C is due to the increment in cell polarisability. Another reason for the increased τ_f is the reduction in the distortion degree of the [TiO₆] octahedral, which was also confirmed by Raman spectroscopy. Mg(Ti_0.95Nb_0.05)O₃ ceramics sintered at 1350 °C for 2 h possessed excellent microwave dielectric properties of ε_r = 18.12, Q × f = 163618 GHz and τ_f = ?40.1 ppm/°C.     

Turbulent boundary layer control with a spanwise array of DBD plasma actuators

The turbulent boundary layer control on NACA 0012 airfoil with Mach number ranging from 0.3 to 0.5 by a spanwise array of dielectric barrier discharge(DBD)plasma actuators by hot-film sensor technology is investigated.Due to temperature change mainly caused through heat produced along with plasma will lead to measurement error of shear stress measured by hot-film sensor,the correction method that takes account of the change measured by another sensor is used and works well.In order to achieve the value of shear stress change,we combine computational fluid dynamics computation with experiment to calibrate the hot-film sensor.To test the stability of the hot-film sensor,seven repeated measurements of shear stress at Ma = 0.3 are conducted and show that confidence interval of hot-film sensor measurement is from-0.18 to 0.18 Pa and the root mean square is 0.11 Pa giving a relative error 0.5％over all Mach numbers in this experiment.The research on the turbulent boundary layer control with DBD plasma actuators demonstrates that the control makes shear stress increase by about 6％over the three Mach numbers,which is thought to be reliable through comparing it with the relative error 0.5％,and the value is hardly affected by burst frequency and excitation voltage.