Gelling behavior of MgAl2O4 slurries with a common dispersant

MgAl₂O₄ transparent ceramics were shaped by a commonly used polyacrylic acid (PAA), which acted as both dispersant and gelling agent. The spinel slurries were prepared by ball-milling MgAl₂O₄ powder, PAA, and water in an attrition mill. The gelling of slurries happened at room temperature in air atmosphere without any other organic additive. The gelling mechanism was the formation of chelates between Mg²⁺ and carboxyl groups (-COO⁻) of PAA. The frequency-based testing method was applied to investigate the gelling process of the as-prepared slurry. In addition, a novel in situ characterization method based on a modified indentation testing was invented to better understand the strengthening of the wet green body with time and to guide when demolding could be carried out. After sintering, transparent MgAl₂O₄ ceramics with high in-line transmittance were resulted.     

Eco-friendly tape casting of borosilicate glass/Al2O3 sheets for LTCC applications

This work reports the innovative development of a borosilicate glass/Al₂O₃ tape for LTCC applications using an eco-friendly aqueous tape casting slurry. Polyvinylpyrrolidone (PVP) and polyacrylic acid (PAA) were the respective dispersants, while carboxymethyl cellulose (CMC) and styrene acrylic emulsion (SA) were the respective binders. The results showed that PVP was more suitable than PAA as the dispersant for the aqueous casting slurry, and that 1.5 wt% PVP would achieve well dispersion of CABS glass/Al₂O₃ powder in the aqueous slurry. Moreover, a small amount of 2.0 wt% CMC binder could yield smooth CABS glass/Al₂O₃ tapes crack free. A high-quality CABS glass/Al₂O₃ tape with a smooth surface was made from an aqueous slurry containing 1.5 wt% PVP dispersant, 2.0 wt% CMC binder, and 2.0 wt% PEG-400 plasticizer. The density, tensile strength, and surface roughness of the green tape were 2.05 g/cm³, 0.87 MPa, and 148 nm, respectively. The resulting CABS glass/Al₂O₃ composites sintered at 875 °C exhibited a bulk density of 3.14 g/cm³, a dielectric constant of 8.09, a dielectric loss of 1.0 × 10^?3, a flexural strength of 213 MPa, a thermal expansion coefficient of 5.30 ppm/^°C, and a thermal conductivity of 3.2 W m^?1 K^?1, thus demonstrating its broad prospects in LTCC applications.     

基于平均飞行航迹的CCO减噪效用研究

近年来，通过优化飞行程序降低机场飞机噪声影响成为机场环境保护的重要研究方向。文章首先建立了基于飞机“噪声-功率-距离”数据的噪声计算模型，介绍了平均飞行航迹以及连续爬升运行(Continuous Climb Opera-tion, CCO)离场程序的相关理论，最后以大型国际机场为实例，使用飞机平均飞行航迹进行噪声预测，运用综合噪声模型计算出噪声影响面积并绘制噪声影响等值线图，比较了CCO离场相对常规的标准仪表离场(Standard Instru-ment Departure, SID)的降噪效果。结果表明，CCO离场程序可有效降低机场噪声影响，在高噪声级影响区域的降噪效果更佳。     

Thermodynamic calculation and microstructure characterization of spinel formation in MgO–Al2O3–C refractories

In this paper, by simulating the gas phase conditions inside the MgO–Al₂O₃–C refractories during continuous casting process and combining with thermodynamic analysis, as well as SEM analysis, the gas-gas and gas-solid formation of MA spinel were clarified in carbon containing refractories. Thermodynamic calculations showed that gas partial pressure of CO, O₂ and Mg could meet the formation and stable existence conditions of MA spinel in MgO–Al₂O₃–C refractories under service environment, and nitrogen could not affect the formation of MA spinel at 1550 °C in the thermodynamic condition. The formation processes of MA spinel were analyzed experimentally under embedding carbon atmosphere. The carbon-coated alumina powders in MgO–Al₂O₃–C refractories prevented the direct contact between magnesia and alumina. Mg gas was formed by carbon thermal reaction, then reacted with alumina (gas-solid) and gas containing aluminum (gas-gas) to generate MA spinel. Through gas-gas or gas-solid reaction, the formation of MA spinel was effectively controlled. By means of SEM analysis, a two-layer structure with dense outer spinel layer and loose inner layer was formed in MgO–Al₂O₃–C refractories.     

Achieving fabrication of highly transparent Y2O3 ceramics via air pre-sintering by deionization treatment of suspension

An easy albeit quite effective deionization suspension treatment was adopted to alleviate the detrimental effects related to the hydrolysis of Y₂O₃ in an aqueous medium. Fabrication of highly transparent Y₂O₃ ceramics with a fine grain size via air pre-sintering and post–hot isostatic pressing (HIP) treatment without using any sintering additive was achieved using the treated suspensions. The hydrolysis issue of Y₂O₃ powder in an aqueous medium was effectively alleviated by using deionization treatment, and a well-dispersed suspension with a low concentration of dissolved Y³⁺ species was obtained. The dispersed suspensions were consolidated by the centrifugal casting method, and the green bodies derived from the suspension of 35.0 vol% solid loading showed an improved homogeneity with a relative density of 52.1%. Fully dense Y₂O₃ transparent ceramic with high transparency was obtained by pre-sintering consolidated green compacts at a low temperature of 1400°C for 16 h in air followed by a post-HIP treatment at 1550°C for 2 h under 200 MPa pressure. The sample had a fine average grain size of 690 nm. The in-line transmittance of the sample reached 83.3% and 81.8% at 1100 nm and 800 nm, respectively, very close to the theoretical values of Y₂O₃.     

Tuning of shear thickening behavior and elastic strength of polyvinylidene fluoride via doping of ZnO-graphene

ZnO rice like nonarchitects are grafted on the graphene carbon core via a rapid microwave synthesis route. The prepared grafted systems are characterized via XRD, SEM, RAMAN, and XPS to examined the structural and morphological parameters. Zinc oxide grafted graphene sheets (ZnO-G) are further doped in β-phase of polyvinylidene fluoride (PVDF) to prepare the polymer nanocomposites (PNCs) via mixed solvent approach (THF/DMF). β-phase confirmation of PVDF PNCs is done by FTIR studies. It is observed that ZnO-G filler enhances the β-phase content in the PNCs. Non-doped PVDF and PNCs are further studied for rheological behavior under the shear rate of 1–100 s⁻¹. Doping of ZnO-G dopant to the PVDF matrix changes its discontinuous shear thickening (DST) behavior to continues shear thickening behavior (CST). Hydrocluster formation and their interaction with the dopant could be the reason for this striking DST to CST behavioral change. Strain amplitude sweep (10⁻³% -10%) oscillatory test reveals that the PNCs shows extended linear viscoelastic region with high elastic modulus and lower viscous modulus. Effective shear thickening behavior and strong elastic strength of these PNCs present their candidature for various fields including mechanical and soft body armor applications.     

Anisotropic strength and fracture resistance of epoxy-ceramic composite materials produced by ultrasound freeze-casting

The anisotropic mechanical properties of ultrasound freeze cast epoxy-ceramic composite materials were studied by measuring flexural strength and fracture resistance curves (R-curves) using both unnotched and notched three-point beam bending experiments, respectively, cut in three different orientations relative to the directional freezing axis. Three ultrasound frequencies of 0.699, 1.39 and 2.097 MHz were used in order to introduce different length scales into the microstructure, with 0 MHz used as the control samples. For all cases, the composites showed higher strength and fracture resistance when the crack plane cut across the direction of ice growth (denoted as the YX orientation). The anisotropic properties were more evident for the material produced without ultrasound (0 MHz) where the flexural strength was approximately 160% higher for the YX orientation compared to two orthogonal orientations. Most of the fracture resistance increase was found to occur within a crack extension, Δa, of ～0.5 mm. Comparing the fracture resistance at Δa = 0.5 mm for the highly anisotropic 0 MHz samples showed that the YX orientation was approximately 86% tougher than the two orthogonal orientations. When the ultrasound operation frequencies of 0.699, 1.39 and 2.097 MHz were applied, the amount of anisotropy in the strength and fracture resistance gradually decreased as the operating frequency increased. The high strength and fracture resistance for the YX orientation was attributed to the alignment of the ceramic particles along the freeze front direction creating a barrier for crack propagation. Ultrasound modifies the material microstructure, introducing relatively dense ceramic layers perpendicular to the freezing front direction that act as an additional, orthogonal barrier to crack propagation. The addition of the denser layers acts to improve the mechanical properties in the weaker orientations and reduce the overall anisotropy.     

Anisotropic thermal expansion and ionic conductivity of a crystal-oriented,Mg2+-conducting NASICON-type solid electrolyte

Multivalent ion-conducting ceramics are required for the manufacture of high-safety, high-capacity rechargeable batteries. However, the low ionic conductivity of solid electrolytes and discrepancies in the thermal expansion between the battery components limit their widespread application. Furthermore, anisotropic thermal expansion in crystals during battery manufacturing and the charge-discharge cycles causes the formation of microcracks, which degrade the battery performance. The physical properties of ceramic materials with anisotropic crystal structures can be modified by varying the crystallographic orientation of their grains. In this study, a co-precipitation approach was used to synthesize an Mg²⁺-conducting (Mg_0.1Hf_0.9)_4/3.8Nb(PO₄)₃ solid electrolyte, and the grain orientation in the bulk sample was controlled using strong magnetic fields during the slip casting process. The results showed that inducing an orientation along the c-axis enhanced the apparent ionic conductivity of the bulk sample. It was also observed that (Mg_0.1Hf_0.9)_4/3.8Nb(PO₄)₃ crystal has a negative volumetric thermal expansion despite a positive linear thermal expansion along its c-axis. By adjusting the c-axis orientation of the grains, (Mg_0.1Hf_0.9)_4/3.8Nb(PO₄)₃ electrolytes with negative or positive linear thermal expansion coefficient have been produced. The findings of this study suggest that solid-electrolytes with negative, positive, or zero linear thermal expansion can be produced to create more compatible and higher-performance solid-state devices.     

面向连续查询的敏感语义位置隐私保护方案

针对连续查询位置服务中构造匿名区域未考虑语义位置信息导致敏感隐私泄露问题，通过设计[(K,θ)]-隐私模型，提出一种路网环境下面向连续查询的敏感语义位置隐私保护方案。该方案利用Voronoi图将城市路网预先划分为独立的Voronoi单元，依据用户的移动路径和移动速度，选择具有相似特性的其他[K-1]个用户，构建匿名用户集；利用匿名用户集用户设定的敏感语义位置类型和语义安全阈值，以及用户所处语义位置的Voronoi单元，构建满足[(K,θ)]-隐私模型的语义安全匿名区域，可以同时防止连续查询追踪攻击和语义推断攻击。实验结果表明，与SCPA算法相比，该方案在隐私保护程度上提升约15%，系统开销上降低约20%。     

Up-pulling force analysis for ESC hollow cylindrical casting

Electroslag casting(ESC)is an important method to produce high quality castings.In this study,the ESC up-pulling inner mold method(EUPIM)was used to produce hollow cylindrical castings with the multiple consumable electrodes.The radial deformation,the axial and radial internal stress of the inner mold,and the axial internal stress of the slag shell were analyzed using the finite element method(FEM)with the aid of ANSYS software.The ProCAST software was used to calculate the specific heat,heat conductivity and density curve of Cu.Simulation results show that the radial deformation,the axial and radial internal stress of the inner mold,and the axial internal stress of the slag shell near the slag-metal interface of hollow cylndrical casting gradually increase from 0 s to 360 s after the ESC starting(slagging)process but before applying the up-pulling force.The suitable initial up-pulling moment of the inner mold is at around 180-198 s after the starting process.