Corrosion behaviors of carbon steel induced by life activities of Phaeodactylum tricornutum in a marine environment

Microbiologically influenced corrosion induced by bacteria has been studied for many years. Corrosion is known to be sensitive to the presence of microalgae, such as Phaeodactylum tricornutum. However, the life activity of P. tricornutum that influences the general and localized corrosion of carbon steel is not fully understood. The current study uses a combination of immersion tests and electrochemical experiments with a detailed surface characterization to reveal the naturally formed corrosion products with/without the presence of P. tricornutum. The results show that samples suffer from pitting corrosion and the averaged pit depths are approximately 15 μm under a light–dark cycle condition or a 24-h constant light condition. Meanwhile, the corrosion products are mainly comprised of γ-FeOOH and Fe₃O₄ in a constant light condition. However, γ-FeOOH, Fe₃O₄, and FeCO₃ are found in a light–dark cycle. This study proposes the fundamental mechanisms of the effect of P. tricornutum life activities on the corrosion performance of Q235 carbon steel, to fulfill the knowledge gaps of the presence of microalgae inducing the general and pitting corrosion of carbon steel.     

Effect of microstructural features on the corrosion behavior of severely deformed Al–Mg–Si alloy

The aim of this study was to determine the influence of severe plastic deformation processing and the changes in microstructure resulting therefrom on the corrosion resistance of an Al–Mg–Si alloy. The alloy was processed using incremental equal channel angular pressing, which caused a reduction in grain size from 15 to 0.9 µm. The grain refinement was accompanied by an increase in the number of grain boundaries and dislocations, and by changes in grain orientation. However, there was no change in the size and number of intermetallic particles, which presumably resulted in a constant number of galvanic couplings. Electrochemical experiments revealed only slight differences between the samples before and after processing. Higher potential transients/oscillations upon immersion and increased corrosion currents in the vicinity of corrosion potential point to slightly higher reactivity of the most refined material. This indicates that intermetallic particles are the most crucial microstructural elements in terms of corrosion resistance. Their impact exceeds that of grain boundaries, in particular, at the stage of corrosion initiation. The development of corrosion attack is controlled more by the microstructure of the matrix as the grain refinement resulted in a less pronounced corrosion attack in comparison with the coarse-grained sample.     

杂化包覆玄武岩鳞片/环氧涂料制备与性能

本文在环氧涂料中添加玄武岩鳞片，提高其防腐蚀性能。针对玄武岩鳞片的团聚问题，通过机械力化学改性工艺，采用正硅酸四乙酯、HY-311型钛酸酯偶联剂、E-44型环氧树脂对玄武岩鳞片进行杂化包覆，结果表明，杂化包覆后玄武岩鳞片的沉降时间从2h提高至96 h。杂化包覆玄武岩鳞片添加量为20%涂层的性能最优，附着力为13.40 MPa，耐盐雾时间为2000 h，在3.5%NaCl溶液中浸泡2000 h后，0.01 Hz的阻抗模值仍然有5.15×109 Ω·cm2。     

Microstructure and electromagnetic properties of LiFe5O8 ferrite ceramics prepared from wet- and dry-milled powders

The effect of dry and wet ball milling of LiFe₅O₈ ferrite powder on the microstructure and electromagnetic properties of ferrite ceramics was studied using XRD analysis, scanning electron microscopy, dilatometry, thermogravimetry, calorimetry, and measurement of specific magnetization and electrical resistance. The sintering temperature was 1050 °C; the sintering time was 2 h. It was found that ferrite fabricated from dry-milled powder exhibits an ordered α-LiFe₅O₈ phase with bulk density of 91%. Its saturation magnetization and Curie temperature are 55 emu/g and 628°С, respectively. Specific electrical resistance is 4?10⁶ Ω cm. Wet milling in isopropyl alcohol causes formation of a disordered β-LiFe₅O₈ phase. Ceramics produced by this method shows higher bulk density (97%) and low porosity, and an order of magnitude lower resistivity. Its saturation magnetization and Curie temperature are 51 emu/g and 607°С, respectively.     

Mechanical properties and thermal shock in thin ZrO2–Y2O3–Al2O3 films obtained by the sol-gel method

Thin multilayer coatings of ZrO₂–Y₂O₃–Al₂O₃ were prepared using the sol-gel method and dip-coating technique in order to advance in the study of what influence the incorporation of Al₂O₃ has on films of Y₂O₃-doped ZrO₂, investigating its role in the synthesis of the solutions and in the characteristics and properties of the coatings. After the characterization of the solutions used in the process, the microstructure of the films was studied and their mechanical behaviour and resistance to thermal shock were determined so as to optimize the characteristics and functionality of these coatings. With increased alumina content, 3YSZ-Al₂O₃ (20 mol%), the cubic phase of the zirconia disappeared completely at the sintering temperature used (700 °C), resulting in the tetragonal phase with Al in solution. There was also a decrease in the coatings' hardness and Young's modulus, and an increase in toughness and resistance to thermal shock. These results allow guidelines to be established for the design of multilayer structures that are, tougher, more resistant, and have improved surface properties.     

High dielectric constant of NiFe2O4–LaFeO3 nanocomposite: Interfacial conduction and dielectric loss

Materials exhibiting colossal dielectric constant are the most sought-after materials due to their variety of applications in various electronics industries. NiFe₂O₄ and LaFeO₃ belonging to the spinel and perovskite structures, respectively, were coupled into a nanocomposite by adapting a one-pot sol-gel synthesis. The ratio of NiFe₂O₄:LaFeO₃ was varied and the synthesized materials were studied for their dielectric behaviors. Interestingly, among the samples studied, the nanocomposite with the ratio of 1:2 of NiFe₂O₄–LaFeO₃ exhibited a high dielectric constant value of 10390 at a frequency of 1 kHz with a several-fold increase in conductivity. The high conductivity resulted in a high dielectric loss. The origin of such a high dielectric constant and loss have been attributed to the Maxwell-Wagner type space charge polarization arising from the microstructure that consists of large and continuous grain boundaries, and the conducting phase at the interface, respectively.     

Toughness and R-curve behaviour of laminated Si3N4/SiCw ceramics

Laminated Si₃N₄/SiC_w ceramics were successfully prepared by tape casting and hot-pressing. Its mechanical properties were measured and the impact resistance was discussed. The toughness of the laminated Si₃N₄/SiC_w ceramics was 13.5 MPa m^1/2, which was almost 1.6 times that of Si₃N₄/SiC_w composite ceramics, namely 8.5 MPa m^1/2. Moreover, the indentation strength of laminated Si₃N₄/SiC_w ceramics was not sensitive to increasing indentation loads and exhibited a rising R-curve behaviour, indicating that the laminated Si₃N₄/SiC_w ceramics had excellent impact resistance. The improved toughness and impact resistance of laminated Si₃N₄/SiC_w ceramics was attributed to the residual stress caused by a thermal expansion coefficient mismatch between the different layers, resulting in crack deflection and bridging of SiC whiskers in the interface layer, thus consuming a large amount of fracture work.     

Effects of Cu on the corrosion behavior and microstructure of Mg–Zn–Ca bulk metallic glass

For the purpose of developing biodegradable magnesium alloys with suitable properties for biomedical applications, Mg–Zn–Ca–Cu metallic glasses were prepared by copper mold injection methods. In the present work, the effect of Cu doping on mechanical properties, corrosion behavior, and glass-forming ability of Mg₆₆Zn₃₀Ca₄ alloy was studied. The experimental findings demonstrated that the incorporation of Cu decreases the corrosion resistance of alloys, but increases the microhardness and degradation rate slightly. However, the addition of a trace amount of Cu can make the samples have antibacterial properties. Therefore, Mg–Zn–Ca–Cu has great advantages in clinical implantation and is the potential implant material.     

Electrodeposition of B,Ni co-doped diamond-like carbon films on AZ91D magnesium alloy: Corrosion and wear resistance

Diamond-like carbon (DLC) possesses brilliant and excellent properties, including excellent corrosion resistance as well as outstanding wear resistance. Ni and B co-doped DLC films were deposited on AZ91D magnesium alloy by electrodeposition under mild conditions (300 V and 25°C). Uniform and dense morphology of co-doped DLC films were observed, and Ni and B were uniformly incorporated into the carbon-based films. Among all the electrodeposits, the appearance of D and G peaks near 1330 and 1570 cm⁻¹ revealed that the as-deposited films were typical DLC films. As the addition of Ni was increased to 0.05 g, the highest microindentation hardness, the lowest friction coefficient, and wear loss were achieved to be 164.5 HV, 0.3, and 0.6 × 10⁻⁵ kg/m, respectively. The amorphous carbon films fabricated at 0.05 g Ni had the lowest corrosion current density and the most positive corrosion potential, which was mainly due to the small and dense granular structure effectively hindering the penetration of corrosion media.     

Phase and microstructure evolution of Sc2O3–CeO2 –ZrO2ceramics in Na2SO4 + V2O5 molten salts

In this study, the destabilization resistance of Sc₂O₃ and CeO₂ co-stabilized ZrO₂ (SCZ) ceramics was tested in Na₂SO₄ + V₂O₅ molten salts at 750°C–1100 °C. The phase structure and microstructure evolution of the samples during the hot corrosion testing were analyzed with X-ray diffraction (XRD), Raman spectra, scanning electron microscopy (SEM), energy dispersive X-ray spectrum (EDS), and X-ray photoelectron spectroscopy (XPS). Results showed that the destabilization of SCZ ceramics at 750 °C was the result of the chemical reaction with V₂O₅ to produce m-ZrO₂ and CeVO₄, and little ScVO₄ was detected in the Sc₂O₃-rich SCZ ceramics. The primary corrosion products at 900 °C and 1100 °C were CeO₂ and m-ZrO₂ due to the mineralization effect. The Sc₂O₃-rich SCZ ceramics exhibited excellent degradation resistance and phase stability owing to the enhanced bond strength and the decreased size misfit between Zr⁴⁺ and Sc³⁺. The destabilization mechanism of SCZ ceramic under hot corrosion was also discussed.