Electrodeposition of B,Ni co-doped diamond-like carbon films on AZ91D magnesium alloy: Corrosion and wear resistance

Diamond-like carbon (DLC) possesses brilliant and excellent properties, including excellent corrosion resistance as well as outstanding wear resistance. Ni and B co-doped DLC films were deposited on AZ91D magnesium alloy by electrodeposition under mild conditions (300 V and 25°C). Uniform and dense morphology of co-doped DLC films were observed, and Ni and B were uniformly incorporated into the carbon-based films. Among all the electrodeposits, the appearance of D and G peaks near 1330 and 1570 cm⁻¹ revealed that the as-deposited films were typical DLC films. As the addition of Ni was increased to 0.05 g, the highest microindentation hardness, the lowest friction coefficient, and wear loss were achieved to be 164.5 HV, 0.3, and 0.6 × 10⁻⁵ kg/m, respectively. The amorphous carbon films fabricated at 0.05 g Ni had the lowest corrosion current density and the most positive corrosion potential, which was mainly due to the small and dense granular structure effectively hindering the penetration of corrosion media.     

特种工程胎硫化外胎质量缺陷原因分析以及解决措施

我公司使用的硫化机采用氮气定型,二次水硫化的工艺。由于特种工程胎胎体偏厚且大,成型机都比较大,生产过程中的帘布筒、钢丝、胎侧等部件都比较重且大。成型胎面使用胎面缠绕机缠绕,所以整个生产过程难度较大。特种工程胎硫化外胎的主要质量问题有:胎面皮泡、胎侧缺胶、胎侧泡、胎肩侧皮泡、子口内侧露线、子口缺胶、胎肚内缺(窝气)、胎肚露线、胎肚皮泡、胎肚串泡、子口支边、胎冠支边、子口鼓包、外胎花缺等。通过对特种工程胎硫化外胎质量缺陷原因分析,找到相应的解决措施,从而减少硫化外胎质量缺陷。     

Wear and thermal behavior of basalt fiber reinforced rice husk/polyvinyl chloride composites

Plant fiber reinforced polymer composites (PFRPs) in practical application are often subjected to both complex friction and variable temperature environments. The present work explores the possibility of reinforcing rice husk/polyvinyl chloride (RH/PVC) composites with basalt fibers (BF) for developing a new wear resistant material with improved thermal stability. The results showed that the structural strength and wear resistance of the composites increased at first and then decreased with an increasing ratio of BF/RH, the highest value occurred at a BF/RH ratio of 8/42. The thermal stability of composites had a positive relationship with BF/RH ratio. The composites added with BF all possessed improved performance in comparison with unadded composites. Hence, the findings of this article proposed some new perspectives on improving the wear resistance and thermal stability of PFRPs that would broaden their practical application.     

Altered age-hardening behavior in the ultrafine-grained surface layer of Mg-Zn-Y-Ce-Zr alloy processed by sliding friction treatment

To gain insight into the ageing behavior of ultrafine grain(UFG)structure,the precipitation phenom-ena and microstructural evolutions of Mg-6Zn-1Y-0.4Ce-0.5 Zr(wt.％)alloy processed by sliding friction treatment(SFT)were systematically studied using hardness texting,transmission electron microscopy(TEM)equipped with high-angle annular dark-field scanning(HADDF-STEM),X-ray diffraction(XRD)and XRD line broadening analysis.The microhardness of the SFT-processed(SFTed)sample initially decreases from 109.6 HV to 104.8 HV at ageing for 8 h,and then increases to the peak-ageing point of 115.4 HV at 16 h.Subsequently,it enters the over-aged period.The un-SFTed sample,as the counterpart,follows a regular ageing behavior that increases from 89.9 HV to 99.6 HV when ageing for 12 h,and then drops.A multi-mechanistic model is established to describe the strengthening due to grain refinement,disloca-tion accumulation,precipitation etc.The analysis reveals that the temperature sensitive UFG structure has an obvious grain coarsening effect,which arouses the soft phenomenon in the early ageing stage.But precipitation hardening provides an excellent hardness enhancement for overcoming the negative influ-ence and helping to reach the peak-aged point.In our microstructural observations,a lot of equilibrium ultrafine MgZn2 precipitates precipitate along dislocations because defects can provide the favorable conditions for the migration and segregation of solute atoms.     

CrN和CrN/Ag涂层的真空高温摩擦磨损性能*

为改善涂层在真空、高温等苛刻条件下的摩擦学性能，利用中频直流磁控溅射技术在硅片和316L不锈钢上沉积了CrN和CrN/Ag涂层，利用扫描电镜、透射电镜和X射线衍射仪对涂层的成分及相结构进行了表征，通过划痕测试仪、纳米压痕仪和摩擦磨损试验机测试了涂层的力学及摩擦学性能。结果表明：添加Ag元素以后，CrN/Ag涂层硬度及承载能力有所减小，但结合强度增加；真空高温环境下CrN与CrN/Ag涂层摩擦因数随温度升高呈下降趋势，其中CrN涂层通过软化镀层减小剪切强度和阻力，从而减小摩擦因数，CrN/Ag涂层主要通过高温产生的热驱动力诱导表面Ag润滑膜的形成来减小摩擦因数；CrN涂层依靠自身剪切特性参与摩擦，而CrN/Ag涂层在真空高温下具有自润滑和持续润滑性能，作为自润滑零部件具有潜在的应用价值。     

往复活塞式压缩机活塞杆温度高故障分析及改造

针对2台2D40型空气压缩机在实际试机过程中,活塞杆温度过高,导致连锁报警,压缩机不能正常工作的问题进行了详细的故障原因分析;对压缩机技术性能参数进行介绍;对压缩机的损伤情况进行说明并找到改造方案,解决机组运行中活塞杆温度过高的问题,从而提高机组的运行效率,使机组运行安全、稳定。     

Mechanical properties,corrosion resistance,and rubber pad forming of cold differential speed-rolled pure titanium for bipolar plates of proton-exchange membrane fuel cells

Due to problems such as pores on surface-treated coatings, the corrosion resistance of pure titanium bipolar plates for proton-exchange membrane fuel cells can be further improved by increasing the corrosion resistance of pure titanium by using differential speed-rolling (DSR); however, these materials have not yet reached the standard requirements of bipolar plates (corrosion current density i_corr＜10³ nA·cm^?2). In this work, the corrosion resistance of pure titanium was improved by optimizing the DSR process while the strength was maintained. The best corrosion resistance of the DSR pure titanium was achieved when the roller speed ratio was 2, while i_corr was 429 nA·cm^?2 in a solution of 0.5 M H₂SO₄ and 2 mg/L HF at room temperature. The formability of the DSR pure titanium for bipolar plates was verified. The optimal holding pressure range was 6.8–7.0 kN.     

基于滚动摩擦作用下玉米颗粒在模拟筒仓卸料中的力链分析（网络首发、推荐阅读）

针对颗粒滚动摩擦作用对筒仓中玉米颗粒的力链空间分布进行研究，通过EDEM离散元软件建立筒仓模型与仿真玉米颗粒模型进行卸粮仿真模拟，并与筒仓卸料实验作流态对比，验证模型与仿真结果的准确性。通过对模拟仓进行切片观察和数据处理，对比分析了不同摩擦情况下力链的细观参数随时间演化规律。模拟结果表明：颗粒间摩擦系数越大，卸粮完成的最终时间越长；颗粒间滚动摩擦系数越小，颗粒由整体流转变为管状流的时间越早。对于有漏斗的筒仓来说，减小颗粒间摩擦会改变整体流和管状流之间的极限，从而增加产生管状流的面积。标准滚动摩擦系数下玉米颗粒在卸料过程中会出现起拱-塌陷效应；减小滚动摩擦，玉米颗粒卸料较稳定，未出现起拱的应力突增、以及拱塌陷的应力衰减；增大颗粒间滚动摩擦不但会增加拱效应，且出现成拱高度距离漏斗口更高。     

Non-keyhole Friction Stir Welding for 6061-T6 Aluminum Alloy

A novel non-keyhole friction stir welding technique was proposed to weld the butt joint of 6061-T6 aluminum alloy with the thickness of 6 mm. A sound joint was obtained by this technique, simultaneously eliminating the flash, shoulder mark and keyhole defects. The sleeve directly affected zone (SDAZ) and the sleeve indirectly affected zone (SIAZ) were divided into the joint according to the plunging position of the hollow sleeve. The lack of root penetration defect was avoided when the plunging depth of the hollow sleeve was only 4.2 mm, because the hollow part inside the sleeve improved the material flow below the sleeve. An S-shaped line was left at the SIAZ, and the height of it had the minimum value of 1.47 mm at 20 mm/min. Whether the failure location of the joint was in SIAZ/SDAZ or the heat-affected zone (HAZ) depended on the height and bonding strength of the S-shaped line. The joint fracture location changed from the SIAZ/SDAZ at 35 mm/min to the HAZ at 20 and 30 mm/min. The maximum tensile strength of 224.3 MPa was obtained at 30 mm/min which was 73.7% of that of the base material. The fracture surface morphology exhibited the typical ductile fracture.     

Passivity‐based adaptive control of a 2‐DOF serial robot manipulator with temperature dependent joint frictions

Mechanical systems are always suffering from the effects of temperature dependent friction forces where the system is operated in a wide range of temperature. Temperature and its variation play an important role in friction force in mechanical systems. If it is not compensated, it will tend to unwanted consequences, including steady‐state errors, limit cycling, and hunting. Therefore, it is necessary to take the temperature effects into account. This has been a strong motivation for the researchers to work on temperature effects on joint friction. In this paper, an adaptive compensation (control) scheme is proposed and applied to a 2‐degree‐of‐freedom serial robot manipulator by taking the temperature effects into account on the joints friction. In the proposed control scheme, the temperature is not required to be sensed. In this paper, joint friction is described by LuGre dynamic model with temperature dependent parameters. These parameters are described by some functions with unknown temperature dependent terms. According to the mathematical and practical concepts, the temperature dependent friction is decomposed into a viscous term and a disturbance term. An adaptive controller is designed to compensate the friction effect and it is shown that the proposed controller relaxes the condition for a priori knowledge about the environment characteristics, including the upper and lower bounds of the environment temperature and the parameters of the functions, describing the temperature dependent joint frictions. The stability and convergence of the joint position and velocity are proved in the sense of Lyapunov and then the proposed method is confirmed by the simulations.