All-printed and highly stable organic resistive switching device based on graphene quantum dots and polyvinylpyrrolidone composite

We propose all printed and highly stable organic resistive switching device (ORSD) based on graphene quantum dots (G-QDs) and polyvinylpyrrolidone (PVP) composite for non-volatile memory applications. It is fabricated by sandwiching G-QDs/PVP composite between top and bottom silver (Ag) electrodes on a flexible substrate polyethylene terephthalate (PET) at ambient conditions through a cost effective and eco-friendly electro-hydrodynamic (EHD) technique. Thickness of the active layer is measured around 97 nm. The proposed ORSD is fabricated in a 3 × 3 crossbar array. It operates switching between high resistance state (HRS) and low resistance state (LRS) with OFF/ON ratio ∼14 for more than 500 endurance cycles, and retention time for more than 30 days. The switching voltage for set/reset of the devices is ±1.8 V and the bendability down to 8 mm diameter for 1000 cycles are tested. The elemental composition and surface morphology are characterized by XPS, FE-SEM, and microscope.     

Effect of stoichiometry and Cu-substitution on the phase structure and hydrogen storage properties of Ml-Mg-Ni-based alloys

To improve the electrochemical properties of rare-earth–Mg–Ni-based hydrogen storage alloys, the effects of stoichiometry and Cu-substitution on the phase structure and thermodynamic properties of the ...     

Effect of oxygenation on electrocatalysis of La0.6Ca0.4CoO3−x in bifunctional air electrode

A vacuum-annealed La_0.6Ca_0.4CoO_3−x was consecutively oxygenated in air at temperatures decreasing from 800 to 100 °C, and its electrocatalytic activities for oxygen reduction and evolution were then measured as a function of the oxygenation temperature. The valence of Co cation, changing between +2 and +3, was found susceptible to annealing either in vacuum or air. The catalytic activities initially decrease monotonically as the oxygenation temperature was decreased from 800 to 300 °C, as a result of increasing oxygen content, and then rise abruptly with the oxygen reduction activity reaching a maximum at 200 °C and the oxidation activity at 150 °C. X-ray photoelectron spectroscopy analysis indicated that the enhancements by the low-temperature oxygenation involved increased OH coverage and less charged cations at surface. The results clearly reveal the importance of the post-calcination annealing process for optimizing the performance of La_0.6Ca_0.4CoO_3−x in air electrode applications.     

Effect of Stoichiometry on Properties of Rare-Earth-Based Hydrogen Storage Alloy for Nickel-Metal Hydride Secondary Battery

Effect of stoichiometry on microstructures, electrochemical properties and PCT characteristics of the alloys MI(Ni0.71Co0.15-Al0.06Mn0.08)x (MI=Lanthanum-rich Michmetal, x=4.6~5.2) have been investigated. The lattice constants a, c, and cellvolumes of non-stoichiometric alloys are bigger than those of the stoichiometric alloy. With the increasing stoichiometry x,the value of a decreases, and the value of c and cell volume increases except for those of the stoichiometric alloy; the plateaupressure of PCT curve, discharge capacity and cycling stability all increase. The alloy with x=5.2 shows the highest dischargecapacity and the best cycling stability among the studied alloys.     

Ca掺杂钨镁酸铅陶瓷材料的制备及其介电性能

研究了Ca掺杂钨镁酸铅(PMW)陶瓷材料的合成、结构、烧结以及介电性能。结果发现：在Ca^2 摩尔分数小于15％时，能形成单相的PCMW钙铁矿相，结构由原来的斜方相向立方相转变。用二步合成法制备的样品容易致密烧结，气孔率比一步法制备的样品小。Ca的加入降低了材料的介电损耗，在频率为1MHz时，介质损耗达到了10^-4。当Ca^2 摩尔分数大于10％时，材料的Curie峰宽化显著，介电常数温度系数降低。     

菱镁矿固硫特性的理论分析

对菱镁矿在固体燃料燃烧过程中的固硫特性进行了理论研究，所得结论对进一步将菱镁矿作为固体燃料燃烧过程中的固硫剂具有非常重要的意义。     

L－B膜修饰电极循环伏安行为模拟──（Ⅰ）电荷转移速度常数对循环伏安性能的影响

本文用计算机数字模拟方法研究了电活性分子多层Ｚ型Ｌ－Ｂ膜修饰电极的循环伏安行为。计算了电极与修饰Ｌ－Ｂ膜分子第一层之间的电荷转移速度常数Ｋ_ｏ，Ｌ－Ｂ膜分子层间的电荷转移速度常数ｋ_ｉ；对峰电位差△Ｅ_ｐ及阳极峰面积Ｑ的影响，以及在不同条件下各层分子的氧化态分数随扫描时间的变化。为研究和设计电活性分子修饰电极的实际体系提供了大量数据和信息。     

用硫酸铁铵容量法测定钛精矿中二氧化钛含量

样品在过氧化钠熔融、水浸取及盐酸酸化后，在盐酸和硫酸介质中，隔绝空气，用金属铝将钛(Ⅳ)还原至钛(Ⅲ)，以硫氰酸盐为指示剂，用硫酸铁铵标准溶液滴定。