Wear resistance and hardness properties of TiB2– Fe coating developed on AISI 1020 steel by tungsten inert gas (TIG) cladding

The present work is attempted to improve the microhardness and wear properties of AISI 1020 steel by depositing TiB₂–Fe composite coating using tungsten inert gas (TIG) cladding. In this study, different compositions of TiB₂–Fe paste form were preplaced on the substrate plates and then TIG heat input was applied to deposit hard composite coating layer. The main objective of the present work was to explore the influence of TIG input current as well as iron content on the microstructure and surface properties of deposited coatings. Microhardness, microstructural and phase characterization of the coating have been done by the Vickers microhardness tester, scanning electron microscope (SEM), Energy dispersive spectroscopy (EDS) and X-ray diffractrometer (XRD). The results showed that the microhardness of the TiB₂–Fe coating was strongly influenced by the composition of the coating materials as well as the TIG processing current. The microhardness increases with decreasing Fe contents in the coating materials with constant processing current (90 A) as well as it also increases with decreasing processing current with the fixed composition of coating materials (80TiB₂–20Fe). The maximum average microhardness found was 3082 HV_0.1 for the coating of 100TiB₂–0Fe composition ratio and 90 A processing current which was about 18 times higher than that of the substrate average microhardness value (163 HV_0.1). Average wear rate evaluated by considering weight loss of the TIG cladded samples using pin on disc tribometer by the sliding distance of 864 m and 20 N normal loads. The wear results also showed that the coating contains 100 wt% of TiB₂ (0 wt% of Fe) exhibited lower rate of wear 6.74 × 10^?8 g/Nm which is about 24 times lower as compared to AISI 1020 mild steel wear rate (166.31 × 10^?8 g/Nm).     

Peracetic acid as a single endodontic irrigant: effects on microhardness,roughness and erosion of root canal dentin

The aim was to assess the effects of 1% peracetic acid (PAA) as a single endodontic irrigant on microhardness, roughness, and erosion of root canal dentin, compared with 2.5% sodium hypochlorite (NaOCl) and with 2.5% NaOCl combined with 17% EDTA. Forty human, single‐rooted tooth hemisections were submitted to Knoop microhardness test, before and after the following irrigation protocols: PAA = 1% PAA; NaOCl = 2.5% NaOCl; NaOCl‐EDTA‐NaOCl = 2.5% NaOCl +17% EDTA +2.5% NaOCl; and SS = saline. Another 40 roots were instrumented, irrigated with the same protocols, and sectioned longitudinally. The roughness analysis was performed on the mesial section using a confocal laser scanning microscope, whereas erosion was analyzed on each third of the distal section, using a scanning electron microscope. The data were analyzed using ANOVA and Tukey post‐tests, and Kruskal‐Wallis and Dunn post‐tests (α = .05). The PAA and NaOCl‐EDTA‐NaOCl groups showed no significant differences (p > .05); both promoted reduction in microhardness and increase in roughness, compared with the NaOCl and SS groups (p < .05). NaOCl‐EDTA‐NaOCl promoted higher erosion in the cervical and middle thirds than the other groups (p < .05); there was no difference among PAA, NaOCl, and SS (p > .05). There was also no difference among the groups regarding the apical third (p > .05). PAA used as a single endodontic irrigant caused reduction in root canal dentin microhardness and increase in roughness in a similar way to NaOCl‐EDTA‐NaOCl; however, PAA caused less erosion than NaOCl‐EDTA‐NaOCl.     

Microstructure and properties of WC-12Co composite coatings prepared by laser cladding

A comprehensive study of the phase composition, microstructure evolution, microhardness and wear performance of WC-12Co composite coatings fabricated by laser cladding using coaxial powder-feed mode was presented. It was shown that a combination of high scan speed and high laser energy density made WC on the edge of WC-12Co composite powders partially melt in liquid Co and 304 stainless steel matrix, and then new carbides consisting of lamellar WC and herringbone M₃W₃C (M=Fe, Co) were formed. Meanwhile, WC-12Co composite coatings with no porosity, cracks and drawbacks like decarburization were obtained, showing high densification and good metallurgical bonding with the substrate. Furthermore, a considerably high microhardness of HV_0.3 1500-1600, low coefficient of friction of 0.55 and wear rate of (2.15±0.31)×10^-7 mm³/(N·m) were achieved owing to the synergistic effect of excellent metallurgical bonding and fine microstructures of composite coating under laser power of 1500 W.     

工艺参数对超声辅助脉冲电沉积镍-氮化钛复合镀层的影响

在45钢表面以超声波辅助脉冲电沉积制备Ni-TiN复合镀层。研究了平均阴极电流密度、脉冲占空比、超声功率和TiN粒子(平均直径20~30 nm)添加量对复合镀层的TiN粒子含量和显微硬度的影响。得到较优的工艺参数为:NiSO4ꞏ6H2O 300 g/L,NiCl2ꞏ6H2O 30 g/L,H3BO330 g/L,十二烷基硫酸钠0.3 g/L,TiN 25 g/L,pH 4.1~4.3,温度40°C,平均阴极电流密度4 A/dm2,脉冲占空比40%,脉冲频率1000 Hz,超声功率300 W,机械搅拌速率200 r/min,时间60 min。该条件下所得Ni-TiN复合镀层的TiN质量分数为8.35%,显微硬度为819 HV,表面平整、致密,晶粒尺寸均匀。     

TiC含量对TC4合金激光熔覆层组织和性能的影响

采用激光熔覆工艺在TC4钛合金基体表面制备了添加不同质量分数(0%、2%、4%、6%)TiC的Ni60A复合熔覆层,通过光学显微镜、显微硬度计、X射线衍射仪、摩擦磨损机分析了不同TiC含量对熔覆层组织及性能的影响。结果表明:未添加TiC的熔覆层组织以树枝晶为主,添加TiC后出现了花瓣状物相;XRD分析发现熔覆层中出现了AlCCr₂、Al_0.24B_0.01Ni_0.75等硬质增强相,这些能够显著提高熔覆层的硬度。显微硬度及摩擦磨损试验结果表明,添加TiC的熔覆层平均硬度均较基体硬度有大幅提高,摩擦因数显著降低,且随TiC含量的增加,熔覆层硬度先增加后降低,摩擦因数先降低后增加,4%TiC熔覆层的硬度最大,相比基体提高了213.3%,摩擦因数最小,为0.309 774。     

Fabrication of composites from different carbon content ferrous powders adopting thermomechanical processes

In this research, deep consolidation technique is utilized for processing of low and high carbon content ferrous powders to manufacture composite material. High carbon content ferrous powders were used as reinforcing material. The powder particles were allowed to mix with low carbon content ferrous powders in 50:50 weight percent for fabrication of composites. The composites were heat treated at three different temperatures (i.e., 800°C, 900°C, and 1000°C). The changes in microstructure, microhardness, the grain size, and bonding among powder particles were studied. Refinement of grains was observed and this led to improved hardness enabling the processed material to be used as a suitable composite. Abrasive wear tests were carried out using a laboratory tribometer in dry reciprocating sliding contact against Sic abrasive paper. The outcomes demonstrate that the abrasive wear resistance was notably affected by the treatment temperature and hardness of the composites.     

高频微振辅助工艺对激光焊接接头组织性能的影响

基于自主搭建的高频微振平台，进行316L不锈钢振动辅助激光焊接试验，探究高频微振激光焊接工艺对接头组织性能的影响. 结果表明，施加振动后，焊缝表面无飞溅，成形良好. 截面未出现塌陷、堆高，背部熔宽均匀. 振动的施加，能够明显细化焊缝区的晶粒，在共振频率1 467.5 Hz的高频微振激光焊条件下，晶粒尺寸最小. 点状颗粒物分布在奥氏体晶粒间，趋于弥散，新相及大颗粒物减少. 随着振动频率增加，焊缝区显微硬度值跟着增加，在较高共振频率显微硬度值增加显著，在共振频率1 467.5 Hz、加速度160 m/s2条件下，焊缝区平均硬度206 HV，与无振动相比，硬度值增加5.6%.     

电压对电刷镀三价铬镀层性能的影响

在45钢表面电刷镀得到三价铬镀层,镀液组成和工艺条件为:Cr2(SO4)36H2O 0.4 mol/L,甲酸铵0.5 mol/L,氨基乙酸0.5 mol/L,H3BO30.6 mol/L,NaH2PO2 H2O 0.3 mol/L,pH=1.5,温度50°C,镀笔移动速率15 cm/s。研究了电压对镀铬层显微结构、表面粗糙度、厚度、显微硬度和耐磨性的影响。随电压增大,镀层厚度增大,显微硬度和耐磨性均先提高后降低。电压为14 V时,镀层的表面平整,粗糙度为2.387μm,显微硬度为602 HV,耐磨性最好。     

脉冲电沉积镍-铜合金

采用脉冲电沉积技术在304不锈钢表面制备Ni-Cu合金镀层,镀液组成和工艺条件为:NiSO4ꞏ6H2O 200g/L,CuSO4ꞏ5H2O 10 g/L,十二烷基硫酸钠0.2 g/L,柠檬酸钠80 g/L,糖精0.2 g/L,pH 4.0,温度25°C,搅拌速率30 r/min,平均电流密度40~120 mA/cm2,脉冲频率0~100 Hz,占空比20%~90%,时间30 min。研究了平均电流密度、脉冲频率和占空比对Ni-Cu合金镀层的元素组成、表面形貌和显微硬度的影响,得到较优的工艺参数为:平均电流密度40 mA/cm2,脉冲频率50 Hz,占空比60%。该条件下所得Ni-Cu合金镀层由质量分数分别为56.53%和43.47%的Ni和Cu组成,呈“菜花”状形貌,结晶细致、均匀,显微硬度为614.4 HV。